In order to explore the possible diffusion distance of carbon during proeutectoid ferrite transformation, a slow cooling test of low carbon steel was carried out under vacuum of the thermal simulator. The microstructu...In order to explore the possible diffusion distance of carbon during proeutectoid ferrite transformation, a slow cooling test of low carbon steel was carried out under vacuum of the thermal simulator. The microstructure and thermal expansion curve were discussed and the carbon concentration inside the sample was measured. The ferrite layer of about 450 μm thickness was obtained without pearlite on the surface of the sample in the microstructure. The thermal expansion curve shows that the ferrite layer without pearlite is formed during the local phase transformation, which is followed by the global transformation. The carbon concentration in the core of the sample (0.061%) is significantly higher than that of the bulk material (0.054%). All results show that carbon has long-range diffusion from the outer layer to the inner layer of the sample. The transformation is predominantly interface-controlled mode during local transformation, and the interface migration rate is about 2.25 μm/s.展开更多
Based on the diffusion channel,the influence of Si content on the microstructure evolution of iron-based hot-dip Al-χSi coating was analyzed(χ=0,1.5 wt%,3.0 wt% and 7.0 wt%).The results show that the introduction of...Based on the diffusion channel,the influence of Si content on the microstructure evolution of iron-based hot-dip Al-χSi coating was analyzed(χ=0,1.5 wt%,3.0 wt% and 7.0 wt%).The results show that the introduction of Si makes the reaction interface change from the lingual-tooth interface of hot-dip Al to the flat interface of hot-dip Al-Si.It also reduces the thickness of the alloy layer in the coating,especially the Fe_(2)Al_(5) layer.When the Si content is 1.5 wt%or 3.0 wt%,the diffusion channel crosses the conjugate line of the two-phase region(FeAl_(3)+liquid phase)into the FeAl_(3) single-phase region,and then moves to the region with higher Si content.Next,the diffusion channel cuts off the conjugate line of FeAl_(3)phase,τ_(1)/τ_(9) phase,and Fe_(2)Al_(5)phase,which promotes the form ofτ_(1)/τ_(9) phase.The formedτ_(1)/τ_(9) phase inhibits the diffusion between Fe and Al atoms.When the Si content is 7.0 wt%,the diffusion channel passes through the two-phase region(liquid phase+τ_(5))and enters theτ_(5) single-phase region.The form ofτ_(5) single-phase region has a strong inhibitory effect on the interatomic diffusion of Fe and Al,thereby reducing the thickness of the coating,especially the Fe_(2)Al_(5)layer.展开更多
A new insight into the constant current-constant voltage （CC-CV） charge protocol based on the spherical diffusion model was presented. From the model, the CV-charge process compensates, to a large extent, the capaci...A new insight into the constant current-constant voltage （CC-CV） charge protocol based on the spherical diffusion model was presented. From the model, the CV-charge process compensates, to a large extent, the capacity loss in the CC process, and the capacity loss increases with increasing the charging rate and decreases with increasing the lithium-ion diffusion coefficient and using a smaller r value （smaller particle-size and larger diffusion coefficient） and a lower charge rate will be helpful to decreasing the capacity loss. The results show that the CC and the CV charging processes, in some way, are complementary and the capacity loss during the CC charging process due to the large electrochemical polarization can be effectively compensated from the CV charging process.展开更多
Biodiesel is a kind of clean and renewable energy. The effect of ethanol addition on the flame characteristics of waste oil biodiesel is studied by using OH-PLIF technique from the perspective of OH radical evolution....Biodiesel is a kind of clean and renewable energy. The effect of ethanol addition on the flame characteristics of waste oil biodiesel is studied by using OH-PLIF technique from the perspective of OH radical evolution. Ethanol addition leads to the appearance of diffusion flame reaction interface ahead of schedule and shortens the diffusion flame height. The experimental results show a linear correlation between the flame height and the fuel flow rate for a given fuel and oxidant. The same conclusion is drawn from the theoretical analysis of the approximate model. In addition. ethanol addition makes the average OH signal intensity of flame at different fuel flow rate tend to be consistent and the fuel flow rate enlarge where the flame field shows the strongest oxidation performance. Average OH signal intensity begins to weaken at larger fuel flow rate, which indicates that fuel flow rate of fuels blended with ethanol can change in larger range and does not significantly affect the uniformity of combustion.展开更多
基金Project(16PJ1430200)supported by Shanghai Pujiang Program,China
文摘In order to explore the possible diffusion distance of carbon during proeutectoid ferrite transformation, a slow cooling test of low carbon steel was carried out under vacuum of the thermal simulator. The microstructure and thermal expansion curve were discussed and the carbon concentration inside the sample was measured. The ferrite layer of about 450 μm thickness was obtained without pearlite on the surface of the sample in the microstructure. The thermal expansion curve shows that the ferrite layer without pearlite is formed during the local phase transformation, which is followed by the global transformation. The carbon concentration in the core of the sample (0.061%) is significantly higher than that of the bulk material (0.054%). All results show that carbon has long-range diffusion from the outer layer to the inner layer of the sample. The transformation is predominantly interface-controlled mode during local transformation, and the interface migration rate is about 2.25 μm/s.
基金Projects(51971039,51671037)supported by the National Natural Science Foundation of ChinaProject(19KJA530001)supported by the Natural Science Research Project of Higher Education of Jiangsu,ChinaProject(KYCX21_2868)supported by the Postgraduate Research&Practice Innovation Program of Jiangsu Province,China。
文摘Based on the diffusion channel,the influence of Si content on the microstructure evolution of iron-based hot-dip Al-χSi coating was analyzed(χ=0,1.5 wt%,3.0 wt% and 7.0 wt%).The results show that the introduction of Si makes the reaction interface change from the lingual-tooth interface of hot-dip Al to the flat interface of hot-dip Al-Si.It also reduces the thickness of the alloy layer in the coating,especially the Fe_(2)Al_(5) layer.When the Si content is 1.5 wt%or 3.0 wt%,the diffusion channel crosses the conjugate line of the two-phase region(FeAl_(3)+liquid phase)into the FeAl_(3) single-phase region,and then moves to the region with higher Si content.Next,the diffusion channel cuts off the conjugate line of FeAl_(3)phase,τ_(1)/τ_(9) phase,and Fe_(2)Al_(5)phase,which promotes the form ofτ_(1)/τ_(9) phase.The formedτ_(1)/τ_(9) phase inhibits the diffusion between Fe and Al atoms.When the Si content is 7.0 wt%,the diffusion channel passes through the two-phase region(liquid phase+τ_(5))and enters theτ_(5) single-phase region.The form ofτ_(5) single-phase region has a strong inhibitory effect on the interatomic diffusion of Fe and Al,thereby reducing the thickness of the coating,especially the Fe_(2)Al_(5)layer.
基金Projects(20676152, 20876178) supported by the National Natural Science Foundation of China
文摘A new insight into the constant current-constant voltage （CC-CV） charge protocol based on the spherical diffusion model was presented. From the model, the CV-charge process compensates, to a large extent, the capacity loss in the CC process, and the capacity loss increases with increasing the charging rate and decreases with increasing the lithium-ion diffusion coefficient and using a smaller r value （smaller particle-size and larger diffusion coefficient） and a lower charge rate will be helpful to decreasing the capacity loss. The results show that the CC and the CV charging processes, in some way, are complementary and the capacity loss during the CC charging process due to the large electrochemical polarization can be effectively compensated from the CV charging process.
基金Project(51766007)supported by the National Natural Science Foundation of ChinaProject(U1602272)supported by the NSFC-Yunnan Joint Fund Project+1 种基金Project(2015FB128)supported by the Natural Science Fund Project in Yunnan Province,ChinaProject(CNMRCUTS1704)supported by the Research Fund from State Key Laboratory of Complex Nonferrous Metal Resources Clean Utilization,China
文摘Biodiesel is a kind of clean and renewable energy. The effect of ethanol addition on the flame characteristics of waste oil biodiesel is studied by using OH-PLIF technique from the perspective of OH radical evolution. Ethanol addition leads to the appearance of diffusion flame reaction interface ahead of schedule and shortens the diffusion flame height. The experimental results show a linear correlation between the flame height and the fuel flow rate for a given fuel and oxidant. The same conclusion is drawn from the theoretical analysis of the approximate model. In addition. ethanol addition makes the average OH signal intensity of flame at different fuel flow rate tend to be consistent and the fuel flow rate enlarge where the flame field shows the strongest oxidation performance. Average OH signal intensity begins to weaken at larger fuel flow rate, which indicates that fuel flow rate of fuels blended with ethanol can change in larger range and does not significantly affect the uniformity of combustion.