The La-Ni complex oxide catalyst was prepared by solid state reactions under microwave.The structure and reducibility of the catalyst were characterized by using TG-DTA,XRD,TEM and TPR methods.At the same time the cat...The La-Ni complex oxide catalyst was prepared by solid state reactions under microwave.The structure and reducibility of the catalyst were characterized by using TG-DTA,XRD,TEM and TPR methods.At the same time the catalytic activity of oxidative dehydrogenation of ethylbenzene to styrene with carbon dioxide over the complex oxide nanoparticle was investigated.The results show that the product is K2NiF4 nanoparticles,and the size is 13 nm.The complex oxide sample had high activity for the oxidative dehydrogenation of ethylbenzene to styrene.展开更多
以纳米碳纤维(CNFs)为基体材料,采用化学镀法在CNFs表面沉积了Ni-Co-P催化剂。研究了催化剂用量,硼氢化钠、氢氧化钠浓度,温度等对碱性硼氢化钠溶液水解释氢的影响。电感耦合等离子体原子发射光谱法(ICP-AES)测试得出负载型Ni-Co-P催化...以纳米碳纤维(CNFs)为基体材料,采用化学镀法在CNFs表面沉积了Ni-Co-P催化剂。研究了催化剂用量,硼氢化钠、氢氧化钠浓度,温度等对碱性硼氢化钠溶液水解释氢的影响。电感耦合等离子体原子发射光谱法(ICP-AES)测试得出负载型Ni-Co-P催化剂含镍13.30%(质量分数,下同)、钴82.25%、磷4.45%。硼氢化钠水解释氢实验结果表明,产氢速率与催化剂用量呈线性关系。当温度为45℃、催化剂浓度为7.5 g/L、氢氧化钠浓度为5%、硼氢化钠浓度为2.5%时,氢气释放速率达到最大值18.044 L/(g·min)。通过对负载型催化剂Ni-Co-P/CNFs催化碱性硼氢化钠溶液释放氢气动力学研究表明,该催化剂的活化能Ea为51.57 k J/mol。展开更多
文摘The La-Ni complex oxide catalyst was prepared by solid state reactions under microwave.The structure and reducibility of the catalyst were characterized by using TG-DTA,XRD,TEM and TPR methods.At the same time the catalytic activity of oxidative dehydrogenation of ethylbenzene to styrene with carbon dioxide over the complex oxide nanoparticle was investigated.The results show that the product is K2NiF4 nanoparticles,and the size is 13 nm.The complex oxide sample had high activity for the oxidative dehydrogenation of ethylbenzene to styrene.
文摘以纳米碳纤维(CNFs)为基体材料,采用化学镀法在CNFs表面沉积了Ni-Co-P催化剂。研究了催化剂用量,硼氢化钠、氢氧化钠浓度,温度等对碱性硼氢化钠溶液水解释氢的影响。电感耦合等离子体原子发射光谱法(ICP-AES)测试得出负载型Ni-Co-P催化剂含镍13.30%(质量分数,下同)、钴82.25%、磷4.45%。硼氢化钠水解释氢实验结果表明,产氢速率与催化剂用量呈线性关系。当温度为45℃、催化剂浓度为7.5 g/L、氢氧化钠浓度为5%、硼氢化钠浓度为2.5%时,氢气释放速率达到最大值18.044 L/(g·min)。通过对负载型催化剂Ni-Co-P/CNFs催化碱性硼氢化钠溶液释放氢气动力学研究表明,该催化剂的活化能Ea为51.57 k J/mol。