Low-cost catalysts with high activity are in immediate demand for energy storage and conversion devices.In this study,polyvinyl pyrrolidone was used as a complexing agent to synthesize La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)...Low-cost catalysts with high activity are in immediate demand for energy storage and conversion devices.In this study,polyvinyl pyrrolidone was used as a complexing agent to synthesize La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_(3)(LSCF)perovskite oxide.The obtained porous layered LSCF has a large specific surface area of 23.74 m^(2)/g,four times higher than that prepared by the traditional sol-gel method(5.08 m^(2)/g).The oxygen reduction reaction activity of the oxide in 0.1 mol/L KOH solution was studied using a rotating ring-disk electrode.In the tests,the initial potential of 0.88 V(vs.reversible hydrogen electrode)and the limiting diffusion current density of 5.02 mA/cm^(2)were obtained at 1600 r/min.Therefore,higher catalytic activity and stability were demonstrated,compared with the preparation of LSCF perovskite oxide by the traditional method.展开更多
基金Project(20192BAB216015)supported by the Science and Technology Program of Jiangxi Province,ChinaProjects(GJJ180464,GJJ171499)supported by the Science and Technology Program of Education Department of Jiangxi Province,China+2 种基金Project(jxxjbs17057)supported by the Scientific Research Foundation of Jiangxi University of Science and Technology,ChinaProject([2018]50)supported by the Key R&D Programs of Science and Technology Project of Ganzhou City,ChinaProject([2017]179)supported by the Science and Technology Project of Ganzhou City,China。
文摘Low-cost catalysts with high activity are in immediate demand for energy storage and conversion devices.In this study,polyvinyl pyrrolidone was used as a complexing agent to synthesize La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_(3)(LSCF)perovskite oxide.The obtained porous layered LSCF has a large specific surface area of 23.74 m^(2)/g,four times higher than that prepared by the traditional sol-gel method(5.08 m^(2)/g).The oxygen reduction reaction activity of the oxide in 0.1 mol/L KOH solution was studied using a rotating ring-disk electrode.In the tests,the initial potential of 0.88 V(vs.reversible hydrogen electrode)and the limiting diffusion current density of 5.02 mA/cm^(2)were obtained at 1600 r/min.Therefore,higher catalytic activity and stability were demonstrated,compared with the preparation of LSCF perovskite oxide by the traditional method.