By sol-gel method and dip-coating technique,TiO2 particles were loaded to the surfaces of molecular sieve particles and porous Al2O3 beads,respectively.The XRD results indicated that TiO2 appeared on both supp...By sol-gel method and dip-coating technique,TiO2 particles were loaded to the surfaces of molecular sieve particles and porous Al2O3 beads,respectively.The XRD results indicated that TiO2 appeared on both supporting materials in anatase as nano-grade particle.Catalytic activities of the supported TiO2 photocatalysts were confirmed by degrading Rhodamine B in water.展开更多
The transition metal ion doped TiO 2 nanoparticles were prepared with hydrothermal method, and the effects of doping different metal ions on the ability of TiO 2 in photocatalyzing degradation of rhodamine B(RB) were ...The transition metal ion doped TiO 2 nanoparticles were prepared with hydrothermal method, and the effects of doping different metal ions on the ability of TiO 2 in photocatalyzing degradation of rhodamine B(RB) were studied. The results showed that the doping of Fe 3+ , Co 2+ , Ni 2+ and Cr 3+ in TiO 2 nanoparticles made the photocatalytic efficiency of the TiO 2 particles reduce and the higher the initial content of Fe 3+ , the lower the ability of TiO 2 in photocatalyzing the degradation of RB. But the doping of Zn 2+ and Cd 2+ , especially Zn 2+ , made the photocatalytic efficiency of the TiO 2 particles enhance, showing a great increase of the rate constant( k ) and the initial reaction rate( r ini ).展开更多
TiO2-SnO2-SiO2 nanocomposite photocatalysts were prepared with Na2SiO3·9H2O, SnCl4·5H2O and TiCl4 as precursors by chemistry coating processes and supercritical fluid drying (SCFD) method. Characterizations ...TiO2-SnO2-SiO2 nanocomposite photocatalysts were prepared with Na2SiO3·9H2O, SnCl4·5H2O and TiCl4 as precursors by chemistry coating processes and supercritical fluid drying (SCFD) method. Characterizations with XRD, TEM, NMR and FTIR showed that in addition to anatase type TiO2, a new active phase(Ti,Sn)O2 was also formed in the range of the studied doping concentration, The catalytic activity was evaluated by photocatalytic degradation of phenol as model reaction. SiO2 remained amphorous at all samples. It could prevent from growth of the size of nanopaticle and transformation from anatase to rutile. Compared with pure TiO2, or TiO2-SnO2 catalyst prepared by Sol-gel method, Nano-composite photo-catalyst showed significant improvement in catalytic activity, the photo-catalytic degradation rate of phenol in 7 h reached 88.7%. Application of the composite catalysts for the photocatalytic decomposition of phenol not only gave the same activity relative to pure ultrafine TiO2, but also reduced cost. The experimental results also proved that the thermal stability of TiO2 was greatly enhanced after mixing with small amount of SiO2. The optimized doping of SiO2 was 20.3%. The photo-catalyst prepared by SCFD combination technology was characterized with smaller particle size, larger surface area and higher activity.展开更多
文摘By sol-gel method and dip-coating technique,TiO2 particles were loaded to the surfaces of molecular sieve particles and porous Al2O3 beads,respectively.The XRD results indicated that TiO2 appeared on both supporting materials in anatase as nano-grade particle.Catalytic activities of the supported TiO2 photocatalysts were confirmed by degrading Rhodamine B in water.
文摘The transition metal ion doped TiO 2 nanoparticles were prepared with hydrothermal method, and the effects of doping different metal ions on the ability of TiO 2 in photocatalyzing degradation of rhodamine B(RB) were studied. The results showed that the doping of Fe 3+ , Co 2+ , Ni 2+ and Cr 3+ in TiO 2 nanoparticles made the photocatalytic efficiency of the TiO 2 particles reduce and the higher the initial content of Fe 3+ , the lower the ability of TiO 2 in photocatalyzing the degradation of RB. But the doping of Zn 2+ and Cd 2+ , especially Zn 2+ , made the photocatalytic efficiency of the TiO 2 particles enhance, showing a great increase of the rate constant( k ) and the initial reaction rate( r ini ).
文摘TiO2-SnO2-SiO2 nanocomposite photocatalysts were prepared with Na2SiO3·9H2O, SnCl4·5H2O and TiCl4 as precursors by chemistry coating processes and supercritical fluid drying (SCFD) method. Characterizations with XRD, TEM, NMR and FTIR showed that in addition to anatase type TiO2, a new active phase(Ti,Sn)O2 was also formed in the range of the studied doping concentration, The catalytic activity was evaluated by photocatalytic degradation of phenol as model reaction. SiO2 remained amphorous at all samples. It could prevent from growth of the size of nanopaticle and transformation from anatase to rutile. Compared with pure TiO2, or TiO2-SnO2 catalyst prepared by Sol-gel method, Nano-composite photo-catalyst showed significant improvement in catalytic activity, the photo-catalytic degradation rate of phenol in 7 h reached 88.7%. Application of the composite catalysts for the photocatalytic decomposition of phenol not only gave the same activity relative to pure ultrafine TiO2, but also reduced cost. The experimental results also proved that the thermal stability of TiO2 was greatly enhanced after mixing with small amount of SiO2. The optimized doping of SiO2 was 20.3%. The photo-catalyst prepared by SCFD combination technology was characterized with smaller particle size, larger surface area and higher activity.