SiO2-Al2O3-ZrO2 glasses with different nucleating agents were crystallized under special processing schedule. The microstructure and mechanical properties of the glass-ceramics in SiO2-Al2O3-ZrO2 system were investiga...SiO2-Al2O3-ZrO2 glasses with different nucleating agents were crystallized under special processing schedule. The microstructure and mechanical properties of the glass-ceramics in SiO2-Al2O3-ZrO2 system were investigated by differential scanning calorimetry, scanning electron microscopy, X-ray diffraction and three-point bending method. The results show that ZrO2 is not an effective nucleating agent in SiO2-Al2O3-ZrO2 system, while TiO2 is effective for the separation of spinel, and P2O5 facilitates solubility of ZrO2 in glass and crystallization. The main crystalline phases of the glass-ceramics are spinel, anorthite and tetragonal zirconia. With the increase of ZrO2 content in the glass, glass-ceramics show higher bending strength （120MPa） than others.展开更多
Thermogravimetric analysis and electrical resistivity were used to determine the hydration process of cement paste with rice husk ash(RHA)(0−15%)and water-cement ratio of 0.4 in this work.X-ray diffraction(XRD)method ...Thermogravimetric analysis and electrical resistivity were used to determine the hydration process of cement paste with rice husk ash(RHA)(0−15%)and water-cement ratio of 0.4 in this work.X-ray diffraction(XRD)method and scanning electron microscopy(SEM)were used to survey crystal composition and microstructures of specimens cured for 3 h,1 d,7 d and 28 d.Finally,electrical parameters(electrical resistance and AC impedance spectroscopy)of steel bars reinforced cement paste were investigated to study the effect of RHA on the corrosion resistance.Results showed that RHA could affect the cement hydration by hydration promotion and pozzolanic effect.The evaluation function for electrical resistivity and curing ages fitted well with linear increasing function.The addition of RHA higher than 5%demonstrated a decreasing role in the electrical resistivity of cement paste at earlier curing ages(3−7 d).Meanwhile,when at later curing ages(7−28 d)the result was the opposite.Moreover,RHA demonstrated positive effects on corrosion resistance of steel bars in cement paste.展开更多
ZnO-Bi2O3-based varistor ceramics doped with Yb2O3 in the range from 0 to 0.4% （molar fraction） were obtained by a solid reaction route. The X-ray diffractometry （XRD） and scanning electron microscopy （SEM） were...ZnO-Bi2O3-based varistor ceramics doped with Yb2O3 in the range from 0 to 0.4% （molar fraction） were obtained by a solid reaction route. The X-ray diffractometry （XRD） and scanning electron microscopy （SEM） were applied to characterize the phases and microstructure of the varistor ceramics, and a DC parameter instrument for varistor ceramics was applied to investigate their electrical properties and V-I characteristics. The XRD analysis of the samples shows that the ZnO phase, Bi2O3 phase, ZnTSbaOl2-type spinel phase and Zn2Bi3Sb3O14-type pyrochlore are present, and the Yb2O3 phases and Sb2O4 phases are found in varistor ceramics with increasing amounts of Yb2O3. The average size of ZnO grain firstly increases and then decreases with the increase of Yb2O3 content. The result also shows that the threshold voltage is between 656 V/nun and 1 232 V/mm, the nonlinear coefficient is in the range of 14.1-22.3, and the leakage current is between 0.60 μA and 19.6 μA. The 0.20% Yb2O3-added ZnO-Bi2O3-based varistor ceramics sintered at 900 ℃ have the best electrical characteristics.展开更多
The mechanical properties and cutting performance of the designed Cu Al Mn Zn Ti B shape memory alloy were studied by tensile test and microstructure observation. Using X-ray diffractometry, differential scanning calo...The mechanical properties and cutting performance of the designed Cu Al Mn Zn Ti B shape memory alloy were studied by tensile test and microstructure observation. Using X-ray diffractometry, differential scanning calorimetry(DSC) and semi-quantitative shape memory effect test, the microstructure and shape memory effect were analyzed. It is found that lots of βphase and few α phase are formed in the quenching of Cu-7.5Al-9.7Mn-3.4Zn-0.3Ti-0.14B(mass fraction, %) alloy, a great deal of martensite and few α phase are formed in the aging alloy, while the annealing alloy is composed of a great deal of α phase and few βphase. The tensile strength and elongation of the annealed alloy are 649 MPa and 17.1%, respectively. Some tiny and dispersion distributed second phase particles are generated in Ti and B precipitates, greatly improving the alloy machinability.展开更多
文摘SiO2-Al2O3-ZrO2 glasses with different nucleating agents were crystallized under special processing schedule. The microstructure and mechanical properties of the glass-ceramics in SiO2-Al2O3-ZrO2 system were investigated by differential scanning calorimetry, scanning electron microscopy, X-ray diffraction and three-point bending method. The results show that ZrO2 is not an effective nucleating agent in SiO2-Al2O3-ZrO2 system, while TiO2 is effective for the separation of spinel, and P2O5 facilitates solubility of ZrO2 in glass and crystallization. The main crystalline phases of the glass-ceramics are spinel, anorthite and tetragonal zirconia. With the increase of ZrO2 content in the glass, glass-ceramics show higher bending strength （120MPa） than others.
基金Projects(51808300,51778302)supported by the National Natural Science Foundation of ChinaProject supported by the K.C.Wong Magna Fund in Ningbo University,China。
文摘Thermogravimetric analysis and electrical resistivity were used to determine the hydration process of cement paste with rice husk ash(RHA)(0−15%)and water-cement ratio of 0.4 in this work.X-ray diffraction(XRD)method and scanning electron microscopy(SEM)were used to survey crystal composition and microstructures of specimens cured for 3 h,1 d,7 d and 28 d.Finally,electrical parameters(electrical resistance and AC impedance spectroscopy)of steel bars reinforced cement paste were investigated to study the effect of RHA on the corrosion resistance.Results showed that RHA could affect the cement hydration by hydration promotion and pozzolanic effect.The evaluation function for electrical resistivity and curing ages fitted well with linear increasing function.The addition of RHA higher than 5%demonstrated a decreasing role in the electrical resistivity of cement paste at earlier curing ages(3−7 d).Meanwhile,when at later curing ages(7−28 d)the result was the opposite.Moreover,RHA demonstrated positive effects on corrosion resistance of steel bars in cement paste.
基金Project(BK2011243) supported by the Natural Science Foundation of Jiangsu Province,ChinaProject(2007DA10512711408) supported by the Visiting Scholarship of State Key Laboratory of Power Transmission Equipment & System Security and New Technology (Chongqing University),China+4 种基金Project(EIPE11204) supported by the State Key Laboratory of Electrical Insulation and Power Equipment,ChinaProject(KF201104) supported by the State Key Laboratory of New Ceramic and Fine Processing,ChinaProject(KFJJ201105) supported by the Opening Project of State Key Laboratory of Electronic Thin Films and Integrated Devices,ChinaProject(10KJD430002) supported by the Universities Natural Science Research Project of Jiangsu Province,ChinaProject(11JDG084) supported by the Research Foundation of Jiangsu University,China
文摘ZnO-Bi2O3-based varistor ceramics doped with Yb2O3 in the range from 0 to 0.4% （molar fraction） were obtained by a solid reaction route. The X-ray diffractometry （XRD） and scanning electron microscopy （SEM） were applied to characterize the phases and microstructure of the varistor ceramics, and a DC parameter instrument for varistor ceramics was applied to investigate their electrical properties and V-I characteristics. The XRD analysis of the samples shows that the ZnO phase, Bi2O3 phase, ZnTSbaOl2-type spinel phase and Zn2Bi3Sb3O14-type pyrochlore are present, and the Yb2O3 phases and Sb2O4 phases are found in varistor ceramics with increasing amounts of Yb2O3. The average size of ZnO grain firstly increases and then decreases with the increase of Yb2O3 content. The result also shows that the threshold voltage is between 656 V/nun and 1 232 V/mm, the nonlinear coefficient is in the range of 14.1-22.3, and the leakage current is between 0.60 μA and 19.6 μA. The 0.20% Yb2O3-added ZnO-Bi2O3-based varistor ceramics sintered at 900 ℃ have the best electrical characteristics.
基金Project(51271203)supported by the National Natural Science Foundation of ChinaProject(CX2012B037)supported by Hunan Provincial Innovation Foundation for Postgraduate,China+1 种基金Project(2013zzts017)supported by the Graduate Degree Thesis Innovation Foundation of Central South University,ChinaProject(2012bjjxj015)supported by the Excellent Doctor Degree Thesis Support Foundation of Central South University,China
文摘The mechanical properties and cutting performance of the designed Cu Al Mn Zn Ti B shape memory alloy were studied by tensile test and microstructure observation. Using X-ray diffractometry, differential scanning calorimetry(DSC) and semi-quantitative shape memory effect test, the microstructure and shape memory effect were analyzed. It is found that lots of βphase and few α phase are formed in the quenching of Cu-7.5Al-9.7Mn-3.4Zn-0.3Ti-0.14B(mass fraction, %) alloy, a great deal of martensite and few α phase are formed in the aging alloy, while the annealing alloy is composed of a great deal of α phase and few βphase. The tensile strength and elongation of the annealed alloy are 649 MPa and 17.1%, respectively. Some tiny and dispersion distributed second phase particles are generated in Ti and B precipitates, greatly improving the alloy machinability.