A novel C60-styrene-maleic anhydride copolymer was prepared with radical polymerization. 50 mg of C60 and 1 g of styrene and 1 g of maleic anhydride were dissolved in 20 mL of o-dichlorobenzene, then was initiated by ...A novel C60-styrene-maleic anhydride copolymer was prepared with radical polymerization. 50 mg of C60 and 1 g of styrene and 1 g of maleic anhydride were dissolved in 20 mL of o-dichlorobenzene, then was initiated by 200 mg of BPO at 70 ℃ under the protection of Ar for 32 h. The copolymer was obtained as a brown solid. The structure of copolymer was characterized by UV and FTIR. GPC analyses shows that its average molecular weight Mw is 13 000. The copolymer is soluble in THF, DMSO and water. The surface tension of 0.5% of copolymer aqueous solution was determined to be 54.6×10-3 N/m（20 ℃）. TEM analyses shows that the copolymer is a kind of water-soluble nanosphere with the average diameter of about 60 nm.展开更多
文摘A novel C60-styrene-maleic anhydride copolymer was prepared with radical polymerization. 50 mg of C60 and 1 g of styrene and 1 g of maleic anhydride were dissolved in 20 mL of o-dichlorobenzene, then was initiated by 200 mg of BPO at 70 ℃ under the protection of Ar for 32 h. The copolymer was obtained as a brown solid. The structure of copolymer was characterized by UV and FTIR. GPC analyses shows that its average molecular weight Mw is 13 000. The copolymer is soluble in THF, DMSO and water. The surface tension of 0.5% of copolymer aqueous solution was determined to be 54.6×10-3 N/m（20 ℃）. TEM analyses shows that the copolymer is a kind of water-soluble nanosphere with the average diameter of about 60 nm.