采用固相合成法制备了La_(0.8)Sr_(0.2)(Ga_(0.8)Mg_(0.2))_(0.1)Fe_(0.9)O_(3-δ)(LSGMF)混合导体和La_(0.8)Sr_(0.2)Ga_(0.8)Mg_(0.2)O_(3-δ)(LSGM)固体电解质,利用XRD、TGA、范德堡直流四探针法和热膨胀仪等对试样进行了分析。以LS...采用固相合成法制备了La_(0.8)Sr_(0.2)(Ga_(0.8)Mg_(0.2))_(0.1)Fe_(0.9)O_(3-δ)(LSGMF)混合导体和La_(0.8)Sr_(0.2)Ga_(0.8)Mg_(0.2)O_(3-δ)(LSGM)固体电解质,利用XRD、TGA、范德堡直流四探针法和热膨胀仪等对试样进行了分析。以LSGMF为致密扩散障碍层,以LSGM为氧泵层,采用共压共烧结法制备了极限电流型氧传感器,利用SEM和EDS对LSGMF/LSGM陶瓷体横截面的微观形貌和成分进行了分析。结果表明:LSGMF具有菱方钙钛矿结构(R-3c空间群),它在650℃失重速率最快,其电导率随温度的升高而增大;300~1000℃范围,LSGM与LSGMF的热膨胀系数分别为12.51×10^(–6)/℃和12.80×10^(–6)/℃。650~850℃范围,氧传感器具有良好的极限电流平台,lg I_L(极限电流I_L)与1000/T呈线性关系,LSGMF中氧离子的扩散激活能为0.4008 e V。800℃、0.3mol%<x(O_2)<21.0mol%时,极限电流IL与氧含量x(O_2)间的关系为:I_L(m A)=10.285x(O_2)(mol%),R=0.9982。LSGMF和LSGM结合牢固,未产生裂纹,EDS分析基本符合各化合物的化学计量比。展开更多
文摘采用固相合成法制备了La_(0.8)Sr_(0.2)(Ga_(0.8)Mg_(0.2))_(0.1)Fe_(0.9)O_(3-δ)(LSGMF)混合导体和La_(0.8)Sr_(0.2)Ga_(0.8)Mg_(0.2)O_(3-δ)(LSGM)固体电解质,利用XRD、TGA、范德堡直流四探针法和热膨胀仪等对试样进行了分析。以LSGMF为致密扩散障碍层,以LSGM为氧泵层,采用共压共烧结法制备了极限电流型氧传感器,利用SEM和EDS对LSGMF/LSGM陶瓷体横截面的微观形貌和成分进行了分析。结果表明:LSGMF具有菱方钙钛矿结构(R-3c空间群),它在650℃失重速率最快,其电导率随温度的升高而增大;300~1000℃范围,LSGM与LSGMF的热膨胀系数分别为12.51×10^(–6)/℃和12.80×10^(–6)/℃。650~850℃范围,氧传感器具有良好的极限电流平台,lg I_L(极限电流I_L)与1000/T呈线性关系,LSGMF中氧离子的扩散激活能为0.4008 e V。800℃、0.3mol%<x(O_2)<21.0mol%时,极限电流IL与氧含量x(O_2)间的关系为:I_L(m A)=10.285x(O_2)(mol%),R=0.9982。LSGMF和LSGM结合牢固,未产生裂纹,EDS分析基本符合各化合物的化学计量比。