The cerium conversion film was applied to improving the corrosion resistance of Mg-Gd-Y-Zr magnesium alloy. The film was electrodeposited on the surface of the Mg-RE alloy in cerium nitrate solution. The compositions ...The cerium conversion film was applied to improving the corrosion resistance of Mg-Gd-Y-Zr magnesium alloy. The film was electrodeposited on the surface of the Mg-RE alloy in cerium nitrate solution. The compositions and morphologies were analyzed by X-ray diffraction(XRD), scanning election microscopy (SEM). The corrosion behaviors of the film were investigated electrochemical impedance spectroscopy (EIS), potentiodynamic polarization tests and immersion tests. The results show that the optimum parameters for electrochemical deposition are as follows: pH 10.0, time 30 min, 50 mmol/L Na2CO3 and temperature 25 ℃ by the designed experiments according to the orthogonal table L(9, 34). The corrosion protection efficiency is dependent on the deposition parameters. The cerium conversion film shows better corrosion protection behavior than chromate conversion film on Mg-Gd-Y-Zr magnesium alloy.展开更多
The three systems of pure Zn, Zn-0.10% Mg(mass fraction), and Zn-0.15% Mg(mass fraction) were cast under controlled atmosphere and their microstructures were characterized by SEM/EDS analysis. The electrochemical corr...The three systems of pure Zn, Zn-0.10% Mg(mass fraction), and Zn-0.15% Mg(mass fraction) were cast under controlled atmosphere and their microstructures were characterized by SEM/EDS analysis. The electrochemical corrosion behavior of these three samples was examined in the very aggressive solution of 50% H2SO4(mass fraction) using electrochemical impedance spectroscopy(EIS) and potentiodynamic polarization measurements. The results show that magnesium improves in some extent the corrosion resistance of pure Zn in 50% H2SO4(mass fraction) confirmed by EIS test. Results of polarization measurment also demonstrate that small amount of Mg significantly improves the passivation of Zn in the test solution. Results of surface morphology of the samples and EDS analysis reveal that Mg reduced the corrosion attacks to pure Zn.展开更多
基金Project (5133001E) supported by the Major State Basic Research and Development Program of China
文摘The cerium conversion film was applied to improving the corrosion resistance of Mg-Gd-Y-Zr magnesium alloy. The film was electrodeposited on the surface of the Mg-RE alloy in cerium nitrate solution. The compositions and morphologies were analyzed by X-ray diffraction(XRD), scanning election microscopy (SEM). The corrosion behaviors of the film were investigated electrochemical impedance spectroscopy (EIS), potentiodynamic polarization tests and immersion tests. The results show that the optimum parameters for electrochemical deposition are as follows: pH 10.0, time 30 min, 50 mmol/L Na2CO3 and temperature 25 ℃ by the designed experiments according to the orthogonal table L(9, 34). The corrosion protection efficiency is dependent on the deposition parameters. The cerium conversion film shows better corrosion protection behavior than chromate conversion film on Mg-Gd-Y-Zr magnesium alloy.
文摘The three systems of pure Zn, Zn-0.10% Mg(mass fraction), and Zn-0.15% Mg(mass fraction) were cast under controlled atmosphere and their microstructures were characterized by SEM/EDS analysis. The electrochemical corrosion behavior of these three samples was examined in the very aggressive solution of 50% H2SO4(mass fraction) using electrochemical impedance spectroscopy(EIS) and potentiodynamic polarization measurements. The results show that magnesium improves in some extent the corrosion resistance of pure Zn in 50% H2SO4(mass fraction) confirmed by EIS test. Results of polarization measurment also demonstrate that small amount of Mg significantly improves the passivation of Zn in the test solution. Results of surface morphology of the samples and EDS analysis reveal that Mg reduced the corrosion attacks to pure Zn.