采用热重分析对作为耐高温材料使用的聚砜酰胺基单聚合物复合材料(PSA SPCs)进行热性能研究。通过计算积分程序分解温度(IPDT)和温度指数Ts分别评价材料的热稳定性和长期使用温度,通过计算温度指数Tzg来表征耐热性能。PSA SPCs的IPDT、T...采用热重分析对作为耐高温材料使用的聚砜酰胺基单聚合物复合材料(PSA SPCs)进行热性能研究。通过计算积分程序分解温度(IPDT)和温度指数Ts分别评价材料的热稳定性和长期使用温度,通过计算温度指数Tzg来表征耐热性能。PSA SPCs的IPDT、Ts以及Tzg分别为1305℃,248℃和255℃,而PSA树脂材料相对应的参数值依次是1162℃,243℃和244℃,表明PSA SPCs的热性能优于PSA树脂材料。采用不同升温速率,分别用Flynn-Wall-Ozawa法和Kissenger法研究其热降解动力学,计算得到反应活化能(Ea)分别为152.26 k J/mol,146.85 k J/mol,优于PSA树脂材料的Ea值(133.54 k J/mol,127.88 k J/mol)。展开更多
Dendritic polyesters bearing COOH groups at the focal points were grafted onto nanometer silica premodified with 3-aminopropyltriethoxysilane by N,N′-dicyclohexylcarbodiimide mediated amidation. The products were cha...Dendritic polyesters bearing COOH groups at the focal points were grafted onto nanometer silica premodified with 3-aminopropyltriethoxysilane by N,N′-dicyclohexylcarbodiimide mediated amidation. The products were characterized qualitatively by FTIR, TGA and elemental analysis. It was shown that a significant grafting （10%15% net grafting for this reaction） was obtained despite the steric hindrance of the dendrons.展开更多
文摘采用热重分析对作为耐高温材料使用的聚砜酰胺基单聚合物复合材料(PSA SPCs)进行热性能研究。通过计算积分程序分解温度(IPDT)和温度指数Ts分别评价材料的热稳定性和长期使用温度,通过计算温度指数Tzg来表征耐热性能。PSA SPCs的IPDT、Ts以及Tzg分别为1305℃,248℃和255℃,而PSA树脂材料相对应的参数值依次是1162℃,243℃和244℃,表明PSA SPCs的热性能优于PSA树脂材料。采用不同升温速率,分别用Flynn-Wall-Ozawa法和Kissenger法研究其热降解动力学,计算得到反应活化能(Ea)分别为152.26 k J/mol,146.85 k J/mol,优于PSA树脂材料的Ea值(133.54 k J/mol,127.88 k J/mol)。
文摘Dendritic polyesters bearing COOH groups at the focal points were grafted onto nanometer silica premodified with 3-aminopropyltriethoxysilane by N,N′-dicyclohexylcarbodiimide mediated amidation. The products were characterized qualitatively by FTIR, TGA and elemental analysis. It was shown that a significant grafting （10%15% net grafting for this reaction） was obtained despite the steric hindrance of the dendrons.