Carbon materials with adjustable porosity,controllable het-eroatom doping and low-cost have been received considerable attention as supercapacitor electrodes.However,using carbon materials with abundant micropores,a h...Carbon materials with adjustable porosity,controllable het-eroatom doping and low-cost have been received considerable attention as supercapacitor electrodes.However,using carbon materials with abundant micropores,a high surface area and a high-dopant content for an aqueous su-percapacitor with a high energy output still remains a challenge.We report the easy synthesis of interconnected carbon spheres by a polymerization re-action between p-benzaldehyde and 2,6-diaminopyridine.The synthesis in-volves adjusting the mass ratio of the copolymer and KOH activator to achieve increased charge storage ability and high energy output,which are attributed to the high ion-accessible area provided by the large number of micropores,high N/O contents and rapid ion diffusion channels in the porous structure.At a PMEC∶KOH mass ratio of 1∶1,the high electrolyte ion-adsorption area(2599.76 m^(2) g^(−1))and the N/O dopant atoms of the conductive framework of a typical carbon electrode produce a superior specific capacity(303.2 F g^(−1)@0.5 A g^(−1))giving an assembled symmetric capacitor a high energy delivery of 11.3 Wh kg^(−1)@250 W kg^(−1).This study presents a simple strategy for synthesizing microporous carbon and highlights its potential use in KOH-based supercapacitors.展开更多
The synthesis, structure and performance of Li2Mg0.15Mn0.4Co0.45SiO4/C cathode material were studied. The Li2Mg0.15Mn0.4Co0.45SiO4/C solid solution with orthorhombic unit cell （space group Pmn21） was synthesized suc...The synthesis, structure and performance of Li2Mg0.15Mn0.4Co0.45SiO4/C cathode material were studied. The Li2Mg0.15Mn0.4Co0.45SiO4/C solid solution with orthorhombic unit cell （space group Pmn21） was synthesized successfully by combination of wet process and solid-state reaction at high temperature, and its electrochemical performance was investigated primarily. Li2Mg0.15Mn0.4Co0.45SiO4/C composite materials deliver a charge capacity of 302 mA-h/g and a discharge capacity of 171 mA.h/g in the first cycle. The discharge capacity is stabilized at about 100 mA-h/g after 10 cycles at a current density of 10 mA/g in the voltage of 1.5-4.8 V vs Li/Li^＋. The results show that Mg-substitution for the Co ions in Li2Mn0.4Co0.6SiO4 improves the stabilization of initial structure and the electrochemical nerformance.展开更多
基金financially supported by University-level key projects of Anhui University of Science and Technology(QNZD2021-04,QNZD2021-07)Scientific Research Foundation for High-level Talents of Anhui University of Science and Technology(2021yjrc22,13210572)+2 种基金Huainan Science and Technology Bureau Plan Project(2023A3111)Open Research Fund Program of Engineering Technology Research Center of Coal Resources Comprehensive Utilization(MTYJZX202204)Natural Science Research Project of Anhui Educational Committee(2023AH051184,2023AH051210)。
文摘Carbon materials with adjustable porosity,controllable het-eroatom doping and low-cost have been received considerable attention as supercapacitor electrodes.However,using carbon materials with abundant micropores,a high surface area and a high-dopant content for an aqueous su-percapacitor with a high energy output still remains a challenge.We report the easy synthesis of interconnected carbon spheres by a polymerization re-action between p-benzaldehyde and 2,6-diaminopyridine.The synthesis in-volves adjusting the mass ratio of the copolymer and KOH activator to achieve increased charge storage ability and high energy output,which are attributed to the high ion-accessible area provided by the large number of micropores,high N/O contents and rapid ion diffusion channels in the porous structure.At a PMEC∶KOH mass ratio of 1∶1,the high electrolyte ion-adsorption area(2599.76 m^(2) g^(−1))and the N/O dopant atoms of the conductive framework of a typical carbon electrode produce a superior specific capacity(303.2 F g^(−1)@0.5 A g^(−1))giving an assembled symmetric capacitor a high energy delivery of 11.3 Wh kg^(−1)@250 W kg^(−1).This study presents a simple strategy for synthesizing microporous carbon and highlights its potential use in KOH-based supercapacitors.
基金Project(10B054)supported by Scientific Research Fund of Hunan Provincial Education Department,ChinaProjects(2011GK2002,2011FJ3160)supported by the Planned Science and Technology Program of Hunan Province,China
文摘The synthesis, structure and performance of Li2Mg0.15Mn0.4Co0.45SiO4/C cathode material were studied. The Li2Mg0.15Mn0.4Co0.45SiO4/C solid solution with orthorhombic unit cell （space group Pmn21） was synthesized successfully by combination of wet process and solid-state reaction at high temperature, and its electrochemical performance was investigated primarily. Li2Mg0.15Mn0.4Co0.45SiO4/C composite materials deliver a charge capacity of 302 mA-h/g and a discharge capacity of 171 mA.h/g in the first cycle. The discharge capacity is stabilized at about 100 mA-h/g after 10 cycles at a current density of 10 mA/g in the voltage of 1.5-4.8 V vs Li/Li^＋. The results show that Mg-substitution for the Co ions in Li2Mn0.4Co0.6SiO4 improves the stabilization of initial structure and the electrochemical nerformance.