Porous sol-gel glass of CaO-SiO2-P2O5 system with macropores larger than 100 μm was prepared by adding stearic acid as pore former when the sintering was carried out at 700 ℃ for 3h.The sol-gel porous glass shows an...Porous sol-gel glass of CaO-SiO2-P2O5 system with macropores larger than 100 μm was prepared by adding stearic acid as pore former when the sintering was carried out at 700 ℃ for 3h.The sol-gel porous glass shows an amorphous structure. The diameter of the pore created by pore former varies from 100 to 300 μm, and macroporous glass has a narrow and small pore size distribution in mesoporous scale. The porosity and pore size of macroporous bioactive glass can be controlled.展开更多
Highly pure active γ-Al2O3 nanoparticles were synthesized from aluminum nitrate and ammonium carbonate with a little surfactant by chemical precipitation method. The factors affecting the synthesis process were studi...Highly pure active γ-Al2O3 nanoparticles were synthesized from aluminum nitrate and ammonium carbonate with a little surfactant by chemical precipitation method. The factors affecting the synthesis process were studied. The properties of γ-Al2O3 nanoparticles were characterized by DTA, XRD, BET, TEM, laser granularity analysis and impurity content analysis. The results show that the amorphous precursor AI（OH）3 sols are produced by using 0.1 mol/L Al（NO3）3·9H2O and 0.16 mol/L （NH4）2CO3·H2O reaction solutions, according to the volume ratio 1.33, adding 0.024%（volume fraction） surfactant PEG600, and reacting at 40℃, 1000 r/min stirring rate for 15min. Then, after stabilizing for 24 h, the precursors were extracted and filtrated by vacuum, washed thoroughly with deionized water and dehydrated ethanol, dried in vacuum at 80℃ for 8h, final calcined at 800℃ for 1h in the air, and high purity active γ-Al2O3 nanoparticles can be prepared with cubic in crystal system, OH^7-FD3M in space group, about 9 nm in crystal grain size, about 20 nm in particle size and uniform size distribution, 131.35 m^2/g in BET specific surface area, 7 - 11 nm in pore diameter, and not lower than 99.93% in purity.展开更多
基金Project(50174059) supported by the National Natural Science Foundation of China
文摘Porous sol-gel glass of CaO-SiO2-P2O5 system with macropores larger than 100 μm was prepared by adding stearic acid as pore former when the sintering was carried out at 700 ℃ for 3h.The sol-gel porous glass shows an amorphous structure. The diameter of the pore created by pore former varies from 100 to 300 μm, and macroporous glass has a narrow and small pore size distribution in mesoporous scale. The porosity and pore size of macroporous bioactive glass can be controlled.
文摘Highly pure active γ-Al2O3 nanoparticles were synthesized from aluminum nitrate and ammonium carbonate with a little surfactant by chemical precipitation method. The factors affecting the synthesis process were studied. The properties of γ-Al2O3 nanoparticles were characterized by DTA, XRD, BET, TEM, laser granularity analysis and impurity content analysis. The results show that the amorphous precursor AI（OH）3 sols are produced by using 0.1 mol/L Al（NO3）3·9H2O and 0.16 mol/L （NH4）2CO3·H2O reaction solutions, according to the volume ratio 1.33, adding 0.024%（volume fraction） surfactant PEG600, and reacting at 40℃, 1000 r/min stirring rate for 15min. Then, after stabilizing for 24 h, the precursors were extracted and filtrated by vacuum, washed thoroughly with deionized water and dehydrated ethanol, dried in vacuum at 80℃ for 8h, final calcined at 800℃ for 1h in the air, and high purity active γ-Al2O3 nanoparticles can be prepared with cubic in crystal system, OH^7-FD3M in space group, about 9 nm in crystal grain size, about 20 nm in particle size and uniform size distribution, 131.35 m^2/g in BET specific surface area, 7 - 11 nm in pore diameter, and not lower than 99.93% in purity.