TiC/Ti_(2)AlC core-shell structure reinforced Ti-based composite coating was prepared by laser cladding technology.The effect of Ti_(2)AlC content on the microstructure and mechanical behavior of the coating was studi...TiC/Ti_(2)AlC core-shell structure reinforced Ti-based composite coating was prepared by laser cladding technology.The effect of Ti_(2)AlC content on the microstructure and mechanical behavior of the coating was studied.The results showed that the reinforced phase was mainly TiC/Ti_(2)AlC MAX phase core-shell structure at 20%Ti_(2)AlC content.According to the synthesis mechanism,Ti_(2)AlC nucleated on TiC through the diffusion of Al atoms to further generate the core-shell structure.The friction and wear test results showed that the wear resistance of the coating was significantly improved under the load distribution effect of the core-shell structure.The friction coefficient decreased to 0.342,and the wear rate reached 8.19×10^(−5)mm^(3)/(N·m),which was only 47.07%of TC4 substrate.展开更多
基金Project(52365020) supported by the National Natural Science Foundation of ChinaProject([2022]06) supported by the Special Fund for Special Posts of Guizhou University,China+2 种基金Project([2024]03) supported by the Guizhou University Fund,ChinaProject(ZK[2023]78) supported by the Guizhou Provincial Basic Research Program(Natural Science),ChinaProject(BQW[2024]011) supported by the Guizhou Province Science and Technology Foundation,China。
文摘TiC/Ti_(2)AlC core-shell structure reinforced Ti-based composite coating was prepared by laser cladding technology.The effect of Ti_(2)AlC content on the microstructure and mechanical behavior of the coating was studied.The results showed that the reinforced phase was mainly TiC/Ti_(2)AlC MAX phase core-shell structure at 20%Ti_(2)AlC content.According to the synthesis mechanism,Ti_(2)AlC nucleated on TiC through the diffusion of Al atoms to further generate the core-shell structure.The friction and wear test results showed that the wear resistance of the coating was significantly improved under the load distribution effect of the core-shell structure.The friction coefficient decreased to 0.342,and the wear rate reached 8.19×10^(−5)mm^(3)/(N·m),which was only 47.07%of TC4 substrate.