将改性磷石膏晶须与高密度聚乙烯(High density polyethylene,HDPE)进行共混,通过注塑成型技术制备HDPE/磷石膏晶须复合材料,采用傅立叶转换红外光谱(FI-IR)、扫描电镜(SEM)、热分析(DSC)等技术,分析改性磷石膏晶须对HDPE复合材料力学...将改性磷石膏晶须与高密度聚乙烯(High density polyethylene,HDPE)进行共混,通过注塑成型技术制备HDPE/磷石膏晶须复合材料,采用傅立叶转换红外光谱(FI-IR)、扫描电镜(SEM)、热分析(DSC)等技术,分析改性磷石膏晶须对HDPE复合材料力学性能的影响。结果表明:改性后HDPE/磷石膏晶须复合材料的冲击强度、拉伸强度和弯曲强度分别为44.33 k J/m2、25.54 MPa和473.5 MPa,与纯HDPE相比,相应提高了31.5%、6.64%和25.15%;与未改性HDPE/磷石膏晶须复合材料相比,冲击强度提高69.13%,拉伸强度与弯曲强度分别降低1.28%和9.65%。故改性后HDPE/磷石膏晶须的综合性能较好。展开更多
Aiming at alkaline problem of bauxite residue,this work focused variation of alkaline characteristics in bauxite residue through phosphogypsum treatment.The results demonstrated that the pH of bauxite residue reduced ...Aiming at alkaline problem of bauxite residue,this work focused variation of alkaline characteristics in bauxite residue through phosphogypsum treatment.The results demonstrated that the pH of bauxite residue reduced from initial 10.83 to 8.70 when 1.50 wt%phosphogypsum was added for 91 d.The removal rates of free alkali and exchangeable sodium were 97.94%and 75.87%,respectively.Meanwhile,significant positive correlations(P<0.05)existed between pH and free alkali,exchangeable sodium.The effect of free alkali composition was CO3^2–>OH^–>AlO2^–>HCO3^–.In addition,alkaline phase decreased from 52.81%to 48.58%and gypsum stably presented in bauxite residue which continuously provided Ca^2+to inhibit dissolution of combined alkali.Furthermore,phosphogypsum promoted formation of macroaggregate structure,increased Ca^2+,decreased Na+and Al^3+on the surface of bauxite residue significantly,ultimately promoting soil formation in bauxite residue.展开更多
文摘将改性磷石膏晶须与高密度聚乙烯(High density polyethylene,HDPE)进行共混,通过注塑成型技术制备HDPE/磷石膏晶须复合材料,采用傅立叶转换红外光谱(FI-IR)、扫描电镜(SEM)、热分析(DSC)等技术,分析改性磷石膏晶须对HDPE复合材料力学性能的影响。结果表明:改性后HDPE/磷石膏晶须复合材料的冲击强度、拉伸强度和弯曲强度分别为44.33 k J/m2、25.54 MPa和473.5 MPa,与纯HDPE相比,相应提高了31.5%、6.64%和25.15%;与未改性HDPE/磷石膏晶须复合材料相比,冲击强度提高69.13%,拉伸强度与弯曲强度分别降低1.28%和9.65%。故改性后HDPE/磷石膏晶须的综合性能较好。
基金Projects(41877511,41842020)supported by the National Natural Science Foundation of China
文摘Aiming at alkaline problem of bauxite residue,this work focused variation of alkaline characteristics in bauxite residue through phosphogypsum treatment.The results demonstrated that the pH of bauxite residue reduced from initial 10.83 to 8.70 when 1.50 wt%phosphogypsum was added for 91 d.The removal rates of free alkali and exchangeable sodium were 97.94%and 75.87%,respectively.Meanwhile,significant positive correlations(P<0.05)existed between pH and free alkali,exchangeable sodium.The effect of free alkali composition was CO3^2–>OH^–>AlO2^–>HCO3^–.In addition,alkaline phase decreased from 52.81%to 48.58%and gypsum stably presented in bauxite residue which continuously provided Ca^2+to inhibit dissolution of combined alkali.Furthermore,phosphogypsum promoted formation of macroaggregate structure,increased Ca^2+,decreased Na+and Al^3+on the surface of bauxite residue significantly,ultimately promoting soil formation in bauxite residue.