The effect of sulfur addition/solids content(SA/SC)ratio on heavy metals(e.g.copper,zinc and lead)obtained from mine tailings by indigenous sulfur-oxidizing bacteria was studied,and the changes in the chemical forms o...The effect of sulfur addition/solids content(SA/SC)ratio on heavy metals(e.g.copper,zinc and lead)obtained from mine tailings by indigenous sulfur-oxidizing bacteria was studied,and the changes in the chemical forms of heavy metals after bioleaching were explored.The results show that the solubilization of metals is significantly influenced by SA/SC ratio,and SA/SC ratio of 2.50 is found to be the best for bacterial activity and metal solubilization among six SA/SC ratios tested(such as 1.00,1.33,1.50,1.67,2.00 and 2.50)under the chosen experimental conditions.The pH decreases fast and the maximum solubilizations of copper and zinc are respectively 81.76% and 84.35% while that of lead only reaches 40.36%.After bioleaching,the chemical forms of heavy metals have changed.The metals remained in mine tailings are mainly found in residual fractions,which is harmless to the surrounding environment.展开更多
Solid wastes derived from metallurgical industries pose a significant threat to environment. The utilization and disposal of these solid wastes are the major concern in the world. Semi-coke generated in coal-based dir...Solid wastes derived from metallurgical industries pose a significant threat to environment. The utilization and disposal of these solid wastes are the major concern in the world. Semi-coke generated in coal-based direct reduction process of iron ore is a by-product and its suitable utilization is not available so far. In order to handle it properly, the characteristics of this by-product were comprehensively investigated. A series of analysis methods were used to demonstrate its mineral compositions, petrography and physico-chemical properties. The results reveal that the semi-coke has poor washability. The fixed carbon content of semi-coke reaches 76.11% and the gross calorific value is 28.10 MJ/kg, both of which are similar to those of traditional sinter coke breeze. Also, semi-coke ash possesses lower content of SiO2, Al2O3, S and higher content of CaO and MgO, which could improve the strength of sinter ore when partially substituting for coke breeze in sintering. Semi-coke features well-development porous structure and higher reaction activity, which predicts that the sintering speed could be elevated to some extent when employing it as a partial replacement of coke breeze, so the studies further suggest that the potential adverse effect of the high reactivity on sintering process could be weakened by adequately coarsening the semi-coke's particle size.展开更多
基金Project(11JJ2031)supported by the Key Project of Natural Fund of Hunan Province,ChinaProject(2009SK3029)supported by the Plan of Hunan Provincial Science and Technology Department,China
文摘The effect of sulfur addition/solids content(SA/SC)ratio on heavy metals(e.g.copper,zinc and lead)obtained from mine tailings by indigenous sulfur-oxidizing bacteria was studied,and the changes in the chemical forms of heavy metals after bioleaching were explored.The results show that the solubilization of metals is significantly influenced by SA/SC ratio,and SA/SC ratio of 2.50 is found to be the best for bacterial activity and metal solubilization among six SA/SC ratios tested(such as 1.00,1.33,1.50,1.67,2.00 and 2.50)under the chosen experimental conditions.The pH decreases fast and the maximum solubilizations of copper and zinc are respectively 81.76% and 84.35% while that of lead only reaches 40.36%.After bioleaching,the chemical forms of heavy metals have changed.The metals remained in mine tailings are mainly found in residual fractions,which is harmless to the surrounding environment.
基金Project(2011GH561685)supported by the China Torch Program
文摘Solid wastes derived from metallurgical industries pose a significant threat to environment. The utilization and disposal of these solid wastes are the major concern in the world. Semi-coke generated in coal-based direct reduction process of iron ore is a by-product and its suitable utilization is not available so far. In order to handle it properly, the characteristics of this by-product were comprehensively investigated. A series of analysis methods were used to demonstrate its mineral compositions, petrography and physico-chemical properties. The results reveal that the semi-coke has poor washability. The fixed carbon content of semi-coke reaches 76.11% and the gross calorific value is 28.10 MJ/kg, both of which are similar to those of traditional sinter coke breeze. Also, semi-coke ash possesses lower content of SiO2, Al2O3, S and higher content of CaO and MgO, which could improve the strength of sinter ore when partially substituting for coke breeze in sintering. Semi-coke features well-development porous structure and higher reaction activity, which predicts that the sintering speed could be elevated to some extent when employing it as a partial replacement of coke breeze, so the studies further suggest that the potential adverse effect of the high reactivity on sintering process could be weakened by adequately coarsening the semi-coke's particle size.