The surface of 1Cr5 Mo heat-resistant steel welding joint was processed with CO2 laser, and the corrosion behaviors before and after laser heat treatment(LHT) were investigated in the salt spray corrosion environments...The surface of 1Cr5 Mo heat-resistant steel welding joint was processed with CO2 laser, and the corrosion behaviors before and after laser heat treatment(LHT) were investigated in the salt spray corrosion environments. The microstructures, phases, residual stresses and retained austenite content of 1Cr5 Mo steel welding joint before and after LHT were analyzed with optical microscope and X-ray diffraction, respectively. The cracking morphologies and chemical compositions of corrosion products after salt spray corrosion were analyzed with field emission scanning electron microscopy(FESEM) and energy disperse spectroscopy(EDS), respectively, the polarization curves were measured on a PS-268 A type electrochemical workstation, and the mechanism of corrosion resistance by LHT was investigated as well. The results show that the passive film of original sample is destroyed owing to the corrosive media penetrating into the subsurface, resulting in the redox reaction. The content of residual austenite in the surface and the self-corrosion potential are increased by LHT, which is contributed to improving the capability of salt spray corrosion resistance.展开更多
SiC foam ceramic reinforced aluminum matrix composites(SFCAMCs)were prepared by squeeze casting aluminum alloy(Al-23Si)into the SiC foam ceramic with different pore sizes,and the corrosion behavior of the SFCAMCs was ...SiC foam ceramic reinforced aluminum matrix composites(SFCAMCs)were prepared by squeeze casting aluminum alloy(Al-23Si)into the SiC foam ceramic with different pore sizes,and the corrosion behavior of the SFCAMCs was studied in NaCl solutions.Static immersion corrosion tests were conducted at 20°C,50°C and 80°C,respectively.Corrosion morphology and products were analyzed by scanning electron microscope,energy dispersive system and X-ray diffraction.It was found that the corrosion rate of SFCAMCs increases as the temperature rising,and the bigger pore size of SiC foam ceramic reinforcement,the better corrosion resistance of SFCAMCs.展开更多
The wettability,surfactivity and the correlation between wettability and surfactivity of sodium diethylhexylphosphate,sodium diethylhexyl polyoxyethylene phosphate and their complex in NaOH solutions were studied.A co...The wettability,surfactivity and the correlation between wettability and surfactivity of sodium diethylhexylphosphate,sodium diethylhexyl polyoxyethylene phosphate and their complex in NaOH solutions were studied.A complex alkali resistant phosphate surfactant with good permeability was prepared.The wettability of surfactants was investigated by measuring the immersion time,sinking time and capillary effects of nature cotton grey fabric in NaOH solutions.The surfactivity of the surfactants was characterized by measuring the surface tension.The effect of the complex on the surface appearance of cotton grey fabric was also investigated with a scanning electron microscope(SEM) .The results show that all the surfactants exhibit good wettability for cotton grey fabric in 0.5-5.0 mol/L of NaOH solutions,the complex system exhibits better wettability in 5.0-7.0 mol/L of NaOH solutions,in comparison with either corresponding single surfactant component employed,and wettability is well correlative with the surfactivities of the surfactant.SEM images indicate that the cotton grey fabric is well wetted by the alkaline surfactant solution and the quality of fabric is improved.展开更多
Molybdenum disilicide(MoSi_2) based composites with various contents of carbon nanotubes(CNTs) were fabricated by spark plasma sintering(SPS) in vacuum under a pressure of 25 MPa.The composites obtained under a sinter...Molybdenum disilicide(MoSi_2) based composites with various contents of carbon nanotubes(CNTs) were fabricated by spark plasma sintering(SPS) in vacuum under a pressure of 25 MPa.The composites obtained under a sintering temperature of 1500 °C and time of 10 min exhibited optimum mechanical properties at room temperature in terms of fracture toughness and transverse rupture strength.MoSi_2 based composite with 6.0% CNTs(volume fraction) had the highest fracture toughness,transverse rupture strength and hardness,which were improved by about 25.7%,51.5% and 24.4% respectively,as compared with pure MoSi_2.A Mo_(4.8)Si_3C_(0.6) phase was detected in CNTs/MoSi_2 composites by both X-ray diffraction(XRD) method and microstructure analysis with scanning electron microscopy(SEM).It is believed that the fine grains and well dispersed small Mo_(4.8)Si_3C_(0.6) particles had led to a higher hardness and strength of CNTs/MoSi_2 composites because of their particle pullout,crack deflection and micro-bridging effects.展开更多
基金Project(CXLX14-1098)supported by Jiangsu Province Postgraduate Scientific Research Innovation Program,China
文摘The surface of 1Cr5 Mo heat-resistant steel welding joint was processed with CO2 laser, and the corrosion behaviors before and after laser heat treatment(LHT) were investigated in the salt spray corrosion environments. The microstructures, phases, residual stresses and retained austenite content of 1Cr5 Mo steel welding joint before and after LHT were analyzed with optical microscope and X-ray diffraction, respectively. The cracking morphologies and chemical compositions of corrosion products after salt spray corrosion were analyzed with field emission scanning electron microscopy(FESEM) and energy disperse spectroscopy(EDS), respectively, the polarization curves were measured on a PS-268 A type electrochemical workstation, and the mechanism of corrosion resistance by LHT was investigated as well. The results show that the passive film of original sample is destroyed owing to the corrosive media penetrating into the subsurface, resulting in the redox reaction. The content of residual austenite in the surface and the self-corrosion potential are increased by LHT, which is contributed to improving the capability of salt spray corrosion resistance.
基金Project(00008713)supported by the Program of the Science and Technology Creative Team of Universities in Jiangxi,ChinaProject(2013-KLP-04)supported by the Open Foundation of Jiangxi Key Laboratory for Advanced Copper and Tungsten Materials,China
文摘SiC foam ceramic reinforced aluminum matrix composites(SFCAMCs)were prepared by squeeze casting aluminum alloy(Al-23Si)into the SiC foam ceramic with different pore sizes,and the corrosion behavior of the SFCAMCs was studied in NaCl solutions.Static immersion corrosion tests were conducted at 20°C,50°C and 80°C,respectively.Corrosion morphology and products were analyzed by scanning electron microscope,energy dispersive system and X-ray diffraction.It was found that the corrosion rate of SFCAMCs increases as the temperature rising,and the bigger pore size of SiC foam ceramic reinforcement,the better corrosion resistance of SFCAMCs.
基金Project(20573079) supported by the National Natural Science Foundation of China
文摘The wettability,surfactivity and the correlation between wettability and surfactivity of sodium diethylhexylphosphate,sodium diethylhexyl polyoxyethylene phosphate and their complex in NaOH solutions were studied.A complex alkali resistant phosphate surfactant with good permeability was prepared.The wettability of surfactants was investigated by measuring the immersion time,sinking time and capillary effects of nature cotton grey fabric in NaOH solutions.The surfactivity of the surfactants was characterized by measuring the surface tension.The effect of the complex on the surface appearance of cotton grey fabric was also investigated with a scanning electron microscope(SEM) .The results show that all the surfactants exhibit good wettability for cotton grey fabric in 0.5-5.0 mol/L of NaOH solutions,the complex system exhibits better wettability in 5.0-7.0 mol/L of NaOH solutions,in comparison with either corresponding single surfactant component employed,and wettability is well correlative with the surfactivities of the surfactant.SEM images indicate that the cotton grey fabric is well wetted by the alkaline surfactant solution and the quality of fabric is improved.
基金Project(51371155)supported by the National Natural Science Foundation of ChinaProject(2014H0046)supported by the Key Science and Technology Project of Fujian Province,China+2 种基金Project(3502Z20143036)supported by the Scientific Research Fund of Xiamen,ChinaProject(JB13149)supported by the Education Department Science and Technology Project of Fujian Province,ChinaProject(2012D131)supported by the Natural Science Foundation Guidance Project of Fujian Province,China
文摘Molybdenum disilicide(MoSi_2) based composites with various contents of carbon nanotubes(CNTs) were fabricated by spark plasma sintering(SPS) in vacuum under a pressure of 25 MPa.The composites obtained under a sintering temperature of 1500 °C and time of 10 min exhibited optimum mechanical properties at room temperature in terms of fracture toughness and transverse rupture strength.MoSi_2 based composite with 6.0% CNTs(volume fraction) had the highest fracture toughness,transverse rupture strength and hardness,which were improved by about 25.7%,51.5% and 24.4% respectively,as compared with pure MoSi_2.A Mo_(4.8)Si_3C_(0.6) phase was detected in CNTs/MoSi_2 composites by both X-ray diffraction(XRD) method and microstructure analysis with scanning electron microscopy(SEM).It is believed that the fine grains and well dispersed small Mo_(4.8)Si_3C_(0.6) particles had led to a higher hardness and strength of CNTs/MoSi_2 composites because of their particle pullout,crack deflection and micro-bridging effects.