The floatability of different crystalline structures of pyrrhotite(monoclinic and hexagonal) was studied.It is shown that the floatability of monoclinic and hexagonal has obvious difference,and that the flotation reco...The floatability of different crystalline structures of pyrrhotite(monoclinic and hexagonal) was studied.It is shown that the floatability of monoclinic and hexagonal has obvious difference,and that the flotation recovery of monoclinic pyrrhotite is larger than that of hexagonal pyrrhotite using different collectors.When butyl dithiophosphate is used as the collector,the recovery is larger than that by sodium butyl xanthate and sodium diethyl dithiocarbamate.At the pH values ranging from 6 to 9,monoclinic pyrrhotite can be floated well,and the flotation recovery is higher than 90%.Monoclinic and hexagonal pyrrhotites are more easily activated by Cu2+ in acidic conditions than in alkaline conditions.But Cu2+ cannot activate hexagonal pyrrhotite using sodium diethyldithiocarbamate as the collector.By the measurement of contact angle,it is indicated that monoclinic and hexagonal pyrrhotites float well and are easily activated by Cu2+ when dithiophosphate is used as the collector.Using sodium diethyl dithiocarbamate as a collector,the relationship between potential and pH range for pyrrhotite flotation is established.At pH 5,the optimal potential range for flotation of monoclinic pyrrhotite is about 125-580 mV(vs SHE),with the maximum flotation occurring at about 350 mV(vs SHE);the optimal potential range for flotation of hexagonal pyrrhotite is 200?580 mV(vs SHE),with the maximum flotation occurring at about 300 mV(vs SHE).展开更多
The electrode process of diethyldithiocarbamate on the surface of pyrrhotite was studied using systematic electrochemical analysis, including cyclic voltammetry, chronopotentiometry and galvanostatic. Experimental res...The electrode process of diethyldithiocarbamate on the surface of pyrrhotite was studied using systematic electrochemical analysis, including cyclic voltammetry, chronopotentiometry and galvanostatic. Experimental results show that tetraethylthioram disulphide（TETD） is electrodeposited on pyrrhotite electrode surface in the presence of 1.0×10^-4 mol/L diethyldithiocarbamate when the electrode potential is higher than 0.25 V. The electrochemical kinetics parameters of the electrode process of diethyldithiocarbamate on surface of pyrrhotite are calculated as follows： the exchange current density is 2.48μA/cm^2 , and the transmission coefficient is 0.46. The electrodeposition includes two steps electrochemical reaction. The first reaction is electrochemical adsorption of diethyldithiocarbamatc ion, then the adsorbed ion associates with a diethyldithiocarbamate ion from the solution and forms tetraethylthioram disulphide on the surface of pyrrhotite.展开更多
基金Project(50774094) supported by the National Natural Science Foundation of China
文摘The floatability of different crystalline structures of pyrrhotite(monoclinic and hexagonal) was studied.It is shown that the floatability of monoclinic and hexagonal has obvious difference,and that the flotation recovery of monoclinic pyrrhotite is larger than that of hexagonal pyrrhotite using different collectors.When butyl dithiophosphate is used as the collector,the recovery is larger than that by sodium butyl xanthate and sodium diethyl dithiocarbamate.At the pH values ranging from 6 to 9,monoclinic pyrrhotite can be floated well,and the flotation recovery is higher than 90%.Monoclinic and hexagonal pyrrhotites are more easily activated by Cu2+ in acidic conditions than in alkaline conditions.But Cu2+ cannot activate hexagonal pyrrhotite using sodium diethyldithiocarbamate as the collector.By the measurement of contact angle,it is indicated that monoclinic and hexagonal pyrrhotites float well and are easily activated by Cu2+ when dithiophosphate is used as the collector.Using sodium diethyl dithiocarbamate as a collector,the relationship between potential and pH range for pyrrhotite flotation is established.At pH 5,the optimal potential range for flotation of monoclinic pyrrhotite is about 125-580 mV(vs SHE),with the maximum flotation occurring at about 350 mV(vs SHE);the optimal potential range for flotation of hexagonal pyrrhotite is 200?580 mV(vs SHE),with the maximum flotation occurring at about 300 mV(vs SHE).
文摘The electrode process of diethyldithiocarbamate on the surface of pyrrhotite was studied using systematic electrochemical analysis, including cyclic voltammetry, chronopotentiometry and galvanostatic. Experimental results show that tetraethylthioram disulphide（TETD） is electrodeposited on pyrrhotite electrode surface in the presence of 1.0×10^-4 mol/L diethyldithiocarbamate when the electrode potential is higher than 0.25 V. The electrochemical kinetics parameters of the electrode process of diethyldithiocarbamate on surface of pyrrhotite are calculated as follows： the exchange current density is 2.48μA/cm^2 , and the transmission coefficient is 0.46. The electrodeposition includes two steps electrochemical reaction. The first reaction is electrochemical adsorption of diethyldithiocarbamatc ion, then the adsorbed ion associates with a diethyldithiocarbamate ion from the solution and forms tetraethylthioram disulphide on the surface of pyrrhotite.