TQ171．11 2005032247 Ag-Cu离子注入玻璃后不同气氛退火的光吸收研究=Op- tical absorption of nanoclusters by sequentially implanting into SiO2 glass and subsequently annealing in a selected at- mosphere[刊,中]／张丽(武汉...TQ171．11 2005032247 Ag-Cu离子注入玻璃后不同气氛退火的光吸收研究=Op- tical absorption of nanoclusters by sequentially implanting into SiO2 glass and subsequently annealing in a selected at- mosphere[刊,中]／张丽(武汉大学物理科学与技术学院． 湖北,武汉(430072)),蒋昌忠…∥物理学报．-2004,53 (9).-2910-2914 采用MEVVA(metal vapot vacuum arc ion source)引 出的强束流脉冲Ag,Cu离子先后注入到SiO2玻璃,X射 线光电子能谱仪(XPS)分析显示Ag,Cu大多仍为金属态,展开更多
Glasses based on ZnO-Bi_2O_3-B_2O_3 system are expected to be a new kind of sealing glasses because of their low melting temperature and other properties.In order to reveal the effect of B_2O_3 on the rheological beha...Glasses based on ZnO-Bi_2O_3-B_2O_3 system are expected to be a new kind of sealing glasses because of their low melting temperature and other properties.In order to reveal the effect of B_2O_3 on the rheological behavior of ZnO-Bi_2O_3-B_2O_3 system glass melt,the properties of viscosity,thermal expansion,fluxion property and wetting process between cylinder samples and stainless steel were investigated with the rotating crucible viscometer,dilato meter and high-temperature microscope.The structure of sintered glass samples was investigated with scanning electron microscope.The results show that the B_2O_3 content increasing in B_1-B_3 at the given temperature between 400 ℃ and 500 ℃ leads to the increasing of the sample viscosity.When the amount of B_2O_3 increases from 5.24%to 9.24%(mass fraction),the coefficients of thermal expansion of glass samples decrease smoothly from 10.94×10^(-6) to10.71×10^(-6) and 10.38×10^(-6) ℃^(-1) respectively.In the case of sealing temperature,its value increases from 453 ℃ to 494 ℃.ZnO-Bi_2O_3-B_2O_3 system low-melting glass powder sintering was with viscous liquid to participate,which could make the densification of glass sample more effective and more efficient.With the content of B_2O_3 increasing,the wetting angle between the glasses samples and stainless steel could also increase,and the resulting appropriate sealing temperature range is 460-490 ℃.展开更多
文摘TQ171．11 2005032247 Ag-Cu离子注入玻璃后不同气氛退火的光吸收研究=Op- tical absorption of nanoclusters by sequentially implanting into SiO2 glass and subsequently annealing in a selected at- mosphere[刊,中]／张丽(武汉大学物理科学与技术学院． 湖北,武汉(430072)),蒋昌忠…∥物理学报．-2004,53 (9).-2910-2914 采用MEVVA(metal vapot vacuum arc ion source)引 出的强束流脉冲Ag,Cu离子先后注入到SiO2玻璃,X射 线光电子能谱仪(XPS)分析显示Ag,Cu大多仍为金属态,
基金Project(2012BAA08B04)supported by the National“Twelfth Five-Year”Plan for Science&Technology Support of China
文摘Glasses based on ZnO-Bi_2O_3-B_2O_3 system are expected to be a new kind of sealing glasses because of their low melting temperature and other properties.In order to reveal the effect of B_2O_3 on the rheological behavior of ZnO-Bi_2O_3-B_2O_3 system glass melt,the properties of viscosity,thermal expansion,fluxion property and wetting process between cylinder samples and stainless steel were investigated with the rotating crucible viscometer,dilato meter and high-temperature microscope.The structure of sintered glass samples was investigated with scanning electron microscope.The results show that the B_2O_3 content increasing in B_1-B_3 at the given temperature between 400 ℃ and 500 ℃ leads to the increasing of the sample viscosity.When the amount of B_2O_3 increases from 5.24%to 9.24%(mass fraction),the coefficients of thermal expansion of glass samples decrease smoothly from 10.94×10^(-6) to10.71×10^(-6) and 10.38×10^(-6) ℃^(-1) respectively.In the case of sealing temperature,its value increases from 453 ℃ to 494 ℃.ZnO-Bi_2O_3-B_2O_3 system low-melting glass powder sintering was with viscous liquid to participate,which could make the densification of glass sample more effective and more efficient.With the content of B_2O_3 increasing,the wetting angle between the glasses samples and stainless steel could also increase,and the resulting appropriate sealing temperature range is 460-490 ℃.