The galvanic corrosion behaviour of alumiuium 3004 - ∝ brass with different area ratios was studied in the tropical marine atmosphere at Tuticorin harbour over a period of 426 days. The area ratios, viz. AAluminiurn...The galvanic corrosion behaviour of alumiuium 3004 - ∝ brass with different area ratios was studied in the tropical marine atmosphere at Tuticorin harbour over a period of 426 days. The area ratios, viz. AAluminiurn：A∝ brass, studied were 0.125, 0.25, 0.5, 1, 2, 4 and 8. The galvanic corrosion behaviour of the metals was studied in terms of the relative increase in the corrosion rate of aluminium due to galvanic coupling with oc brass, the relative decrease in the corrosion rate of ∝ brass due to galvanic coupling with aluminium, and the susceptibility of aluminium to pitting owing to galvanic coupling with ∝ brass. The galvanic potential and galvanic current of the system were monitored. Pits of different dimensions ranging from mild etchings to perforations were experienced on the borders arid the surfaces of the interface of aluminium in contact with ∝ brass. The corrosion products resulting from galvanic corrosion were analysed using XRD and the pitting on aluminium as a result of galvanic corrosion was highlighted in terms of pit depth, size and density of pit, using a high resolution microscope. The most favourable area ratio of aluminium - ∝ brass in marine atmosphere in terms of gravimetric corrosion rate is 8：1 and the most unfavourable area ratio of aluminium - ∝ brass is 1：4.展开更多
基金Supported by the CSIR-CECRI under project No.MLP 0008
文摘The galvanic corrosion behaviour of alumiuium 3004 - ∝ brass with different area ratios was studied in the tropical marine atmosphere at Tuticorin harbour over a period of 426 days. The area ratios, viz. AAluminiurn：A∝ brass, studied were 0.125, 0.25, 0.5, 1, 2, 4 and 8. The galvanic corrosion behaviour of the metals was studied in terms of the relative increase in the corrosion rate of aluminium due to galvanic coupling with oc brass, the relative decrease in the corrosion rate of ∝ brass due to galvanic coupling with aluminium, and the susceptibility of aluminium to pitting owing to galvanic coupling with ∝ brass. The galvanic potential and galvanic current of the system were monitored. Pits of different dimensions ranging from mild etchings to perforations were experienced on the borders arid the surfaces of the interface of aluminium in contact with ∝ brass. The corrosion products resulting from galvanic corrosion were analysed using XRD and the pitting on aluminium as a result of galvanic corrosion was highlighted in terms of pit depth, size and density of pit, using a high resolution microscope. The most favourable area ratio of aluminium - ∝ brass in marine atmosphere in terms of gravimetric corrosion rate is 8：1 and the most unfavourable area ratio of aluminium - ∝ brass is 1：4.