Based on the steady-state strain measured by single-pass hot compression tests,the method by a double-pass hot compression testing was developed to measure the metadynamic-recrystallization kinetics.The metadynamic re...Based on the steady-state strain measured by single-pass hot compression tests,the method by a double-pass hot compression testing was developed to measure the metadynamic-recrystallization kinetics.The metadynamic recrystallization behavior of low-alloy steel Q345B during hot compression deformation was investigated in the temperature range of 1 000-1 100℃,the strain rate range of 0.01-0.10 s -1 and the interpass time range of 0.5-50 s on a Gleeble-3500 thermo-simulation machine.The results show that metadynamic recrystallization during the interpass time can be observed.As the deformation temperature and strain rate increase,softening caused by metadynamic recrystallization is obvious.According to the data of thermo-simulation,the metadynamic recrystallization activation energy is obtained to be Qmd=100.674 kJ/mol and metadynamic recrystallization kinetics model is set up.Finally,the error analysis of metadynamic recrystallization kinetics model proves that the model has high accuracy(correlation coefficient R=0.988 6).展开更多
The plastic deformation simulation of AZ31 magnesium alloy at different elevated temperatures （from 473 to 723 K） was performed on Gleeble-1500 thermal mechanical simulator at the strain rates of 0.01, 0.1, 1, 5 and...The plastic deformation simulation of AZ31 magnesium alloy at different elevated temperatures （from 473 to 723 K） was performed on Gleeble-1500 thermal mechanical simulator at the strain rates of 0.01, 0.1, 1, 5 and 10 s-t and the maximum deformation degree of 80%. The relationship between the flow stress and deformation temperature as well as strain rate was analyzed. The materials parameters and the apparent activation energy were calculated. The constitutive relationship was established with a Zener-Hollomon （Z） parameter. The results show that the flow stress increases with the increase of strain rate at a constant temperature, but it decreases with the increase of deformation temperature at a constant strain rate. The apparent activation energy is estimated to be 129-153 kJ/mol, which is close to that for self-diffusion of magnesium. The established constitutive relationship can reflect the change of flow stress during hot deformation.展开更多
基金Project(101048) supported by Fok Ying Tung Education FoundationProject(E2008000835) supported by the Natural Science Foundation of Hebei Province,China
文摘Based on the steady-state strain measured by single-pass hot compression tests,the method by a double-pass hot compression testing was developed to measure the metadynamic-recrystallization kinetics.The metadynamic recrystallization behavior of low-alloy steel Q345B during hot compression deformation was investigated in the temperature range of 1 000-1 100℃,the strain rate range of 0.01-0.10 s -1 and the interpass time range of 0.5-50 s on a Gleeble-3500 thermo-simulation machine.The results show that metadynamic recrystallization during the interpass time can be observed.As the deformation temperature and strain rate increase,softening caused by metadynamic recrystallization is obvious.According to the data of thermo-simulation,the metadynamic recrystallization activation energy is obtained to be Qmd=100.674 kJ/mol and metadynamic recrystallization kinetics model is set up.Finally,the error analysis of metadynamic recrystallization kinetics model proves that the model has high accuracy(correlation coefficient R=0.988 6).
基金Project supported by China-Canada-USA Collaborative Research and Development Project (Magnesium Front End Research and Development (MFERD))
文摘The plastic deformation simulation of AZ31 magnesium alloy at different elevated temperatures （from 473 to 723 K） was performed on Gleeble-1500 thermal mechanical simulator at the strain rates of 0.01, 0.1, 1, 5 and 10 s-t and the maximum deformation degree of 80%. The relationship between the flow stress and deformation temperature as well as strain rate was analyzed. The materials parameters and the apparent activation energy were calculated. The constitutive relationship was established with a Zener-Hollomon （Z） parameter. The results show that the flow stress increases with the increase of strain rate at a constant temperature, but it decreases with the increase of deformation temperature at a constant strain rate. The apparent activation energy is estimated to be 129-153 kJ/mol, which is close to that for self-diffusion of magnesium. The established constitutive relationship can reflect the change of flow stress during hot deformation.