As a main charging burden of blast furnace(BF)ironmaking process,pellets play an important role in ironmaking process.However,compared with sinters,there are some inevitable disadvantages for traditional acid pellets,...As a main charging burden of blast furnace(BF)ironmaking process,pellets play an important role in ironmaking process.However,compared with sinters,there are some inevitable disadvantages for traditional acid pellets,e.g.,reduction swell,low melting temperature.Therefore,the fluxed-pellets have been applied in BF,especially MgO-fluxed pellets.In the present study,the effects of category and content of MgO bearing additive on the compressive strength(CS),reduction swelling index(RSI),reduction disintegration index(RDI)and melting-dripping properties of the pellets were investigated.Minerals composition,pore distribution and microstructure of MgO-flux pellets were studied by X-ray powder diffraction(XRD),mercury intrusion method and scanning electron microscopy(SEM),respectively.The results show that the light burned magnesite(LBM)is more suitable MgO bearing additive for fluxed-pellets.With increasing LBM content from 0 to 2.0%,the CS decreases from 3066 to 2689 N,RSI decreases from 16.43%to 9.97%and RDI decreases from 19.2%to 12.99%.The most appropriate MgO bearing additive content in the fluxed-pellets is 2.0%according to principal component analysis(PCA).展开更多
基金Projects(51874080,51604069)supported by the National Natural Science Foundation of ChinaProject(N162504004)supported by the Fundamental Research Funds for the Central Universities,China
文摘As a main charging burden of blast furnace(BF)ironmaking process,pellets play an important role in ironmaking process.However,compared with sinters,there are some inevitable disadvantages for traditional acid pellets,e.g.,reduction swell,low melting temperature.Therefore,the fluxed-pellets have been applied in BF,especially MgO-fluxed pellets.In the present study,the effects of category and content of MgO bearing additive on the compressive strength(CS),reduction swelling index(RSI),reduction disintegration index(RDI)and melting-dripping properties of the pellets were investigated.Minerals composition,pore distribution and microstructure of MgO-flux pellets were studied by X-ray powder diffraction(XRD),mercury intrusion method and scanning electron microscopy(SEM),respectively.The results show that the light burned magnesite(LBM)is more suitable MgO bearing additive for fluxed-pellets.With increasing LBM content from 0 to 2.0%,the CS decreases from 3066 to 2689 N,RSI decreases from 16.43%to 9.97%and RDI decreases from 19.2%to 12.99%.The most appropriate MgO bearing additive content in the fluxed-pellets is 2.0%according to principal component analysis(PCA).