A novel kind of waterborne epoxy coating pigmented by nano-sized aluminium powders on high strength steel was formulated. Several coatings with different pigment volume content (PVC) were prepared. The coating morphol...A novel kind of waterborne epoxy coating pigmented by nano-sized aluminium powders on high strength steel was formulated. Several coatings with different pigment volume content (PVC) were prepared. The coating morphology was observed using scanning electron microscopy (SEM), and the electrochemical properties were investigated by electrochemical impedance spectroscopy (EIS). Immersion test and neutral salt spray test were also conducted to investigate the corrosion resistance of the coating. It is demonstrated that the critical pigment volume content (CPVC) value is between 30% and 40%. The coating with PVC of 30% exhibits good corrosion resistance in 3.5% (mass fraction) NaCl solution.展开更多
Abstract： PAN （Polyacrylonitrile）-based carbonaceous fibers were prepared at the heat treatment temperature （HTT） range of 650 to 900 ℃. The relationships among HTT, carbon content and volume resistivity of the ...Abstract： PAN （Polyacrylonitrile）-based carbonaceous fibers were prepared at the heat treatment temperature （HTT） range of 650 to 900 ℃. The relationships among HTT, carbon content and volume resistivity of the carbonaceous fibers were investigated. The carbonaceous fibers/PTFE （Polytetrafluoroethylene） antistatic coatings were prepared by the spraying technology and the effects of carbonaceous fibers and pigments on surface resistivity of the coatings were systematically discussed. Micrographs provide insight into the antistatic mechanism of the coating. The results show that carbon content of the carbonaceous fibers increases from 68.8% to 74.8% （mass fraction） and the volume resistivity decreases drastically from 1.94× 10^-3 to 8.27× 10 ^-2.cm. The surface resistivity of the antistatic coating is adjustable between 10^5 and 10^8Ω2 to fit the different antistatic materials. Static is dissipated by a conductive network of short fibers and the tunneling effect between the neighboring fibers and conductive pigments. Conductive pigments make the conductive network more perfect and improve the antistatic ability, but insulating pigments acting as barriers for the formation of conductive channel increases the surface resistivity of the coatings. The influence of pigments on the surface resistivity drops gradually with the decrease of the carbonaceous fibers volume resistivity.展开更多
基金Project(51001007) supported by the National Natural Science Foundation of ChinaProject(2011ZE51057) supported by the Aero Science Foundation of China
文摘A novel kind of waterborne epoxy coating pigmented by nano-sized aluminium powders on high strength steel was formulated. Several coatings with different pigment volume content (PVC) were prepared. The coating morphology was observed using scanning electron microscopy (SEM), and the electrochemical properties were investigated by electrochemical impedance spectroscopy (EIS). Immersion test and neutral salt spray test were also conducted to investigate the corrosion resistance of the coating. It is demonstrated that the critical pigment volume content (CPVC) value is between 30% and 40%. The coating with PVC of 30% exhibits good corrosion resistance in 3.5% (mass fraction) NaCl solution.
基金Project(2011CB605601)supported by the National Basic Research Program(973 Program)of ChinaProject(50902088)supported by the National Natural Science Foundation of China+1 种基金Project(ZR2011EMM002)supported by the Natural Science Foundation in Shandong Province,ChinaProject(2009AA035301)supported by the National High Technology Research and Development Program(863 Program)of China
文摘Abstract： PAN （Polyacrylonitrile）-based carbonaceous fibers were prepared at the heat treatment temperature （HTT） range of 650 to 900 ℃. The relationships among HTT, carbon content and volume resistivity of the carbonaceous fibers were investigated. The carbonaceous fibers/PTFE （Polytetrafluoroethylene） antistatic coatings were prepared by the spraying technology and the effects of carbonaceous fibers and pigments on surface resistivity of the coatings were systematically discussed. Micrographs provide insight into the antistatic mechanism of the coating. The results show that carbon content of the carbonaceous fibers increases from 68.8% to 74.8% （mass fraction） and the volume resistivity decreases drastically from 1.94× 10^-3 to 8.27× 10 ^-2.cm. The surface resistivity of the antistatic coating is adjustable between 10^5 and 10^8Ω2 to fit the different antistatic materials. Static is dissipated by a conductive network of short fibers and the tunneling effect between the neighboring fibers and conductive pigments. Conductive pigments make the conductive network more perfect and improve the antistatic ability, but insulating pigments acting as barriers for the formation of conductive channel increases the surface resistivity of the coatings. The influence of pigments on the surface resistivity drops gradually with the decrease of the carbonaceous fibers volume resistivity.