The extraction of zinc from zinc sulfate solution was investigated, using 20% saponified D2EHPA as an extractam and 260^# sulfonate kerosene as a diluent. The solution was stirred for 8 min at phase ratio （Vσ/Va） o...The extraction of zinc from zinc sulfate solution was investigated, using 20% saponified D2EHPA as an extractam and 260^# sulfonate kerosene as a diluent. The solution was stirred for 8 min at phase ratio （Vσ/Va） of 1.0：1.0, initial pH of 2.0 and stirring speed of 200 r/min. The results show that 75% zinc can be extracted from the zinc sulfate solution when the concentration of zinc is 18.7 g/L after being settled for 10 min. 88.60% zinc can be stripped by 196 g/L sulfuric acid, and zinc ion can be separated from ferric ion.展开更多
The size of bubbles created in the flotation process is of great importance to the efficiency of the mineral separation achieved.Meanwhile,it is believed that frother transport between phases is perhaps the most impor...The size of bubbles created in the flotation process is of great importance to the efficiency of the mineral separation achieved.Meanwhile,it is believed that frother transport between phases is perhaps the most important reason for the interactive nature of the phenomena occurring in the bulk and froth phases in flotation,as frother adsorbed in the surface of rising bubbles is removed from the bulk phase and then released into the froth as a fraction of the bubbles burst.This causes the increased concentration in the froth compared to the bulk concentration,named as frother partitioning.Partitioning reflects the adsorption of frother on bubbles and how to influence bubble size is not known.There currently exists no such a topic aiming to link these two key parameters.To fill this vacancy,the correspondence between bubble size and frother partitioning was examined.Bubble size was measured by sampling-for-imaging(SFI)technique.Using total organic carbon(TOC)analysis to measure the frother partitioning between froth and bulk phases was determined.Measurements have shown,with no exceptions including four different frothers,higher frother concentration is in the bulk than in the froth.The results also show strong partitioning giving an increase in bubble size which implies there is a compelling relationship between these two,represented by CFroth/CBulk and D32.The CFroth/CBulkand D32 curves show similar exponential decay relationships as a function of added frother in the system,strongly suggesting that the frother concentration gradient between the bulk solution and the bubble interface is the driving force contributing to bubble size reduction.展开更多
Chloride-induced corrosion of the reinforcement is considered as one of the major mechanisms resulting in the reduction of structural resistance of reinforced concrete structural elements located in marine and other a...Chloride-induced corrosion of the reinforcement is considered as one of the major mechanisms resulting in the reduction of structural resistance of reinforced concrete structural elements located in marine and other aggressive environments. A study of reinforced concrete structures located at the Fangcheng dock in the Beibu Gulf port, China, was present. The result from field survey indicates that the concrete cover depth and chloride diffusion coefficient fit best normal distribution and lognormal distribution, respectively. The service life of structure is about 55 a, while initiation time is 45 a. Sensitivity analysis indicates that the most influential factor of the structure service life prediction is concrete cover, followed by diffusion coefficient, diffusion decay index, critical chloride concentration, surface chloride concentration, current density and localized pitting corrosion. Finally, the effects of diffusion decay index and critical chloride concentration on structure service life prediction are discussed.展开更多
In this research combustion of aluminum dust particles in a quiescent medium with spatially discrete sources distributed in a random way was studied by a numerical approach.A new thermal model was generated to estimat...In this research combustion of aluminum dust particles in a quiescent medium with spatially discrete sources distributed in a random way was studied by a numerical approach.A new thermal model was generated to estimate flame propagation speed in a lean/rich reaction medium.Flame speed for different particle diameters and the effects of various oxidizers such as carbon dioxide and oxygen on flame speed were studied.Nitrogen was considered the inert gas.In addition,the quenching distance and the minimum ignition energy(MIE) were studied as a function of dust concentration.Different burning time models for aluminum were employed and their results were compared with each other.The model was based on conduction heat transfer mechanism using the heat point source method.The combustion of single-particle was first studied and the solution was presented.Then the dust combustion was investigated using the superposition principle to include the effects of surrounding particles.It is found that larger particles have higher values of quenching distance in comparison with smaller particles in an assumed dust concentration.With the increase of dust concentration the value of MIE would be decreased for an assumed particle diameter.Considering random discrete heat sources method,the obtained results of random distribution of fuel particles in space provide closer and realistic predictions of the combustion physics of aluminum dust flame as compared with the experimental findings.展开更多
基金Project(50774094) supported by the National Natural Science Foundation of China
文摘The extraction of zinc from zinc sulfate solution was investigated, using 20% saponified D2EHPA as an extractam and 260^# sulfonate kerosene as a diluent. The solution was stirred for 8 min at phase ratio （Vσ/Va） of 1.0：1.0, initial pH of 2.0 and stirring speed of 200 r/min. The results show that 75% zinc can be extracted from the zinc sulfate solution when the concentration of zinc is 18.7 g/L after being settled for 10 min. 88.60% zinc can be stripped by 196 g/L sulfuric acid, and zinc ion can be separated from ferric ion.
基金Project supported by the Collaborative Research and Development Program of Natural Sciences and Engineering Research Council of Canada
文摘The size of bubbles created in the flotation process is of great importance to the efficiency of the mineral separation achieved.Meanwhile,it is believed that frother transport between phases is perhaps the most important reason for the interactive nature of the phenomena occurring in the bulk and froth phases in flotation,as frother adsorbed in the surface of rising bubbles is removed from the bulk phase and then released into the froth as a fraction of the bubbles burst.This causes the increased concentration in the froth compared to the bulk concentration,named as frother partitioning.Partitioning reflects the adsorption of frother on bubbles and how to influence bubble size is not known.There currently exists no such a topic aiming to link these two key parameters.To fill this vacancy,the correspondence between bubble size and frother partitioning was examined.Bubble size was measured by sampling-for-imaging(SFI)technique.Using total organic carbon(TOC)analysis to measure the frother partitioning between froth and bulk phases was determined.Measurements have shown,with no exceptions including four different frothers,higher frother concentration is in the bulk than in the froth.The results also show strong partitioning giving an increase in bubble size which implies there is a compelling relationship between these two,represented by CFroth/CBulk and D32.The CFroth/CBulkand D32 curves show similar exponential decay relationships as a function of added frother in the system,strongly suggesting that the frother concentration gradient between the bulk solution and the bubble interface is the driving force contributing to bubble size reduction.
基金Project(41274012) supported by the National Natural Science Foundation of China
文摘Chloride-induced corrosion of the reinforcement is considered as one of the major mechanisms resulting in the reduction of structural resistance of reinforced concrete structural elements located in marine and other aggressive environments. A study of reinforced concrete structures located at the Fangcheng dock in the Beibu Gulf port, China, was present. The result from field survey indicates that the concrete cover depth and chloride diffusion coefficient fit best normal distribution and lognormal distribution, respectively. The service life of structure is about 55 a, while initiation time is 45 a. Sensitivity analysis indicates that the most influential factor of the structure service life prediction is concrete cover, followed by diffusion coefficient, diffusion decay index, critical chloride concentration, surface chloride concentration, current density and localized pitting corrosion. Finally, the effects of diffusion decay index and critical chloride concentration on structure service life prediction are discussed.
文摘In this research combustion of aluminum dust particles in a quiescent medium with spatially discrete sources distributed in a random way was studied by a numerical approach.A new thermal model was generated to estimate flame propagation speed in a lean/rich reaction medium.Flame speed for different particle diameters and the effects of various oxidizers such as carbon dioxide and oxygen on flame speed were studied.Nitrogen was considered the inert gas.In addition,the quenching distance and the minimum ignition energy(MIE) were studied as a function of dust concentration.Different burning time models for aluminum were employed and their results were compared with each other.The model was based on conduction heat transfer mechanism using the heat point source method.The combustion of single-particle was first studied and the solution was presented.Then the dust combustion was investigated using the superposition principle to include the effects of surrounding particles.It is found that larger particles have higher values of quenching distance in comparison with smaller particles in an assumed dust concentration.With the increase of dust concentration the value of MIE would be decreased for an assumed particle diameter.Considering random discrete heat sources method,the obtained results of random distribution of fuel particles in space provide closer and realistic predictions of the combustion physics of aluminum dust flame as compared with the experimental findings.