The isotherm,mechanism and kinetics of carbon tetrachloride(CT) adsorption by polyacrylonitrile-based activated carbon fiber(PAN-ACF) were investigated in batch reactors and a continuous flow reactor,and the regenerat...The isotherm,mechanism and kinetics of carbon tetrachloride(CT) adsorption by polyacrylonitrile-based activated carbon fiber(PAN-ACF) were investigated in batch reactors and a continuous flow reactor,and the regeneration of PAN-ACF was also studied.Freundlich and Dubinin-Radushkevich(D-R) adsorption equations can well describe the adsorption isotherm.CT is mainly adsorbed on the exterior surface of PAN-ACF with low boundary layer effect and rate-controlling step of intra-particle diffusion.The adsorption dynamics in the batch reactor well fits with the pseudo-first-order model,and the breakthrough curves in the continuous flow reactor can be well described by the Yoon-Nelson model.The ACF can be recycled through thermal regeneration,whereas the adsorption capacity decreases from 7.87 to 4.98 mg/g after the fourth regeneration.78%-94%of CT can be removed from the wastewater of a fluorine chemical plant on a pilot scale,which confirms the efficacy of ACF under industrial conditions.The results indicate that PAN-ACF is applicable to CT removal from wastewater.展开更多
Fibrous activated alumina is widely applied in catalysts,adsorbents,and composite materials.This work presents a green approach in preparing the fibrous activated Al_(2)O_(3) with high purity and specific surface area...Fibrous activated alumina is widely applied in catalysts,adsorbents,and composite materials.This work presents a green approach in preparing the fibrous activated Al_(2)O_(3) with high purity and specific surface area through multistep phase transformation of aluminum-bearing substances using intermediate dawsonite as a template.Thermodynamic calculations and experimental results show that increasing the concentration of Na_(2)CO_(3) and(NH_(4))_(2)CO_(3) is remarkably beneficial to the formation of dawsonite and ammonium aluminum carbonate hydroxide,respectively.Based on determination of dissolution and precipitation mechanism,the ultrafine granular gibbsite is converted to the uniform fibrous dawsonite with a ratio of length to diameter over 50,and the fibrous dawsonite changes into the long fibrous ammonium aluminum carbonate hydroxide with a ratio of length to diameter is about 80 in above 70 g/L(NH_(4))_(2)CO_(3) solution.Furthermore,the activated alumina remains fibrous morphology after roasting ammonium aluminum carbonate hydroxide at a slow heating rate,plentiful open mesopore and weak aggregation of particles,which contributes to the high specific surface area of 159.37 m^(2)/g at 1273 K for the activated alumina.The complete transformation of dawsonite to ammonium aluminum carbonate hydroxide and high specific surface area contribute to the purity of the activated fibrous alumina above 99.9%with low Na and Fe content.展开更多
Before densification by chemical vapor infiltration,carbon or SiC nanofibers were grown on the surface of carbon fibers by catalytic chemical vapor deposition using electroplated Ni as catalyst.The modification and me...Before densification by chemical vapor infiltration,carbon or SiC nanofibers were grown on the surface of carbon fibers by catalytic chemical vapor deposition using electroplated Ni as catalyst.The modification and mechanism of nanofibers on the pyrocarbon deposition during chemical vapor infiltration were investigated.The results show that the nanofibers improve the surface activity of the carbon fibers and become active nucleation centers during chemical vapor infiltration.They can induce the ordered deposition of pyrocarbon and adjust the interface bonding between pyrocarbon and carbon fibers during the infiltration.展开更多
The preparation process of amorphous nanometer boron powders through combustion synthesis was investigated, and the effects of the reactant ratio, the heating agent and the milling rate on the activity and particle si...The preparation process of amorphous nanometer boron powders through combustion synthesis was investigated, and the effects of the reactant ratio, the heating agent and the milling rate on the activity and particle size of amorphous boron powders were studied. The results show that the boron powders exist in the form of an amorphous phase which has the crystallinity lower than 30.4%, and the panicle size of boron powder decreases with an increase of the high-energy ball milling rate. The purity of amorphous boron powder is 94.8% and panicle sizes are much smaller than 100 nm when the mass ratio of B2O3/Mg/KClO3 is 100：105：17 and the ball milling time is 20 min with the milling rate of 300 r/min. At the same time, the amorphous boron nano-fibers appear in the boron powders.展开更多
Nano-fibrous polyaniline was synthesized on stainless steel electrode in 0.5mol·L-1 H2SO4 solution by pulse galvanostatic method. The effects of synthetic conditions of pulse galvanostatic method on the electroac...Nano-fibrous polyaniline was synthesized on stainless steel electrode in 0.5mol·L-1 H2SO4 solution by pulse galvanostatic method. The effects of synthetic conditions of pulse galvanostatic method on the electroactivity of polyaniline were investigated. The results show that the electroactivity of polyaniline film strongly depends on the synthetic conditions, such as the ratio of “on time” to “off time”(ton/toff), frequency, monomer concentration, temperature and mean current density. Different electroactivities of polyaniline are caused by different morphologies of polyaniline. The nano-fibrous polyaniline has higher electroactivity than polyaniline with other morphologies. Under the following conditions: mean current density of pulse galvanostatic method 13mA·cm-2, ton/toff 1, frequency 200Hz, monomer concentration 0.3mol·L-1 and temperature 20℃, nano-fibrous polyaniline film with the highest electroactivity can be obtained.展开更多
基金Project(2004C33068) supported by the Science and Technology Programs of Zhejiang Province,ChinaProject(20100933B17) supported by the Social Development and Science Research Program of Hangzhou,China
文摘The isotherm,mechanism and kinetics of carbon tetrachloride(CT) adsorption by polyacrylonitrile-based activated carbon fiber(PAN-ACF) were investigated in batch reactors and a continuous flow reactor,and the regeneration of PAN-ACF was also studied.Freundlich and Dubinin-Radushkevich(D-R) adsorption equations can well describe the adsorption isotherm.CT is mainly adsorbed on the exterior surface of PAN-ACF with low boundary layer effect and rate-controlling step of intra-particle diffusion.The adsorption dynamics in the batch reactor well fits with the pseudo-first-order model,and the breakthrough curves in the continuous flow reactor can be well described by the Yoon-Nelson model.The ACF can be recycled through thermal regeneration,whereas the adsorption capacity decreases from 7.87 to 4.98 mg/g after the fourth regeneration.78%-94%of CT can be removed from the wastewater of a fluorine chemical plant on a pilot scale,which confirms the efficacy of ACF under industrial conditions.The results indicate that PAN-ACF is applicable to CT removal from wastewater.
基金Project(51874372)supported by the National Natural Science Foundation of China。
文摘Fibrous activated alumina is widely applied in catalysts,adsorbents,and composite materials.This work presents a green approach in preparing the fibrous activated Al_(2)O_(3) with high purity and specific surface area through multistep phase transformation of aluminum-bearing substances using intermediate dawsonite as a template.Thermodynamic calculations and experimental results show that increasing the concentration of Na_(2)CO_(3) and(NH_(4))_(2)CO_(3) is remarkably beneficial to the formation of dawsonite and ammonium aluminum carbonate hydroxide,respectively.Based on determination of dissolution and precipitation mechanism,the ultrafine granular gibbsite is converted to the uniform fibrous dawsonite with a ratio of length to diameter over 50,and the fibrous dawsonite changes into the long fibrous ammonium aluminum carbonate hydroxide with a ratio of length to diameter is about 80 in above 70 g/L(NH_(4))_(2)CO_(3) solution.Furthermore,the activated alumina remains fibrous morphology after roasting ammonium aluminum carbonate hydroxide at a slow heating rate,plentiful open mesopore and weak aggregation of particles,which contributes to the high specific surface area of 159.37 m^(2)/g at 1273 K for the activated alumina.The complete transformation of dawsonite to ammonium aluminum carbonate hydroxide and high specific surface area contribute to the purity of the activated fibrous alumina above 99.9%with low Na and Fe content.
基金Project(12JJ6051) supported by the Natural Science Foundation of Hunan Province,ChinaProject(2011CB605806) supported by the National Basic Research Program of China
文摘Before densification by chemical vapor infiltration,carbon or SiC nanofibers were grown on the surface of carbon fibers by catalytic chemical vapor deposition using electroplated Ni as catalyst.The modification and mechanism of nanofibers on the pyrocarbon deposition during chemical vapor infiltration were investigated.The results show that the nanofibers improve the surface activity of the carbon fibers and become active nucleation centers during chemical vapor infiltration.They can induce the ordered deposition of pyrocarbon and adjust the interface bonding between pyrocarbon and carbon fibers during the infiltration.
基金Project(51002025) supported by the National Natural Science Foundation of China
文摘The preparation process of amorphous nanometer boron powders through combustion synthesis was investigated, and the effects of the reactant ratio, the heating agent and the milling rate on the activity and particle size of amorphous boron powders were studied. The results show that the boron powders exist in the form of an amorphous phase which has the crystallinity lower than 30.4%, and the panicle size of boron powder decreases with an increase of the high-energy ball milling rate. The purity of amorphous boron powder is 94.8% and panicle sizes are much smaller than 100 nm when the mass ratio of B2O3/Mg/KClO3 is 100：105：17 and the ball milling time is 20 min with the milling rate of 300 r/min. At the same time, the amorphous boron nano-fibers appear in the boron powders.
基金Project(50473022) supported by the National Natural Science Foundation project supported by the State Key Laboratoryof Chemo/Biosensing and Chemometrics of China
文摘Nano-fibrous polyaniline was synthesized on stainless steel electrode in 0.5mol·L-1 H2SO4 solution by pulse galvanostatic method. The effects of synthetic conditions of pulse galvanostatic method on the electroactivity of polyaniline were investigated. The results show that the electroactivity of polyaniline film strongly depends on the synthetic conditions, such as the ratio of “on time” to “off time”(ton/toff), frequency, monomer concentration, temperature and mean current density. Different electroactivities of polyaniline are caused by different morphologies of polyaniline. The nano-fibrous polyaniline has higher electroactivity than polyaniline with other morphologies. Under the following conditions: mean current density of pulse galvanostatic method 13mA·cm-2, ton/toff 1, frequency 200Hz, monomer concentration 0.3mol·L-1 and temperature 20℃, nano-fibrous polyaniline film with the highest electroactivity can be obtained.