Gypsum sludge,a hazardous waste generated by the non-ferrous smelting industry,presents a significant challenge for disposal and utilization.To investigate the feasibility of substituting gypsum sludge for limestone a...Gypsum sludge,a hazardous waste generated by the non-ferrous smelting industry,presents a significant challenge for disposal and utilization.To investigate the feasibility of substituting gypsum sludge for limestone as a flux for smelting,the effects of calcium sulfate(CaSO_(4))and smelting conditions on oxygen-rich smelting of lead concentrate were studied.The interaction between CaSO_(4)and sulfides facilitates the conversion of CaSO_(4)into CaO,which is crucial for slag formation.The order of the influence of sulfide minerals on the conversion of CaSO_(4)is pyrite>sphalerite>galena.When using gypsum sludge exclusively as the calcium source,under optimal conditions with a CaO/SiO_(2)mass ratio of 0.8,an FeO/SiO_(2)mass ratio of 1.2,a melting temperature of 1150℃,an oxygen flow rate of 1.3 L/min,the recovery rates of Pb and Zn in the lead-rich slag reached 85.01%and 95.69%,respectively,with a sulfur content of 2.65 wt%.The As content in the smelting slag obtained by reduction smelting was 0.02 wt%.Resource utilization of gypsum sludge in lead smelting is a feasible method.展开更多
基金Project(2020YFC1909203)supported by the National Key R&D Project of ChinaProjects(51974364,52074355,51904339)supported by the National Natural Science Foundation of China。
文摘Gypsum sludge,a hazardous waste generated by the non-ferrous smelting industry,presents a significant challenge for disposal and utilization.To investigate the feasibility of substituting gypsum sludge for limestone as a flux for smelting,the effects of calcium sulfate(CaSO_(4))and smelting conditions on oxygen-rich smelting of lead concentrate were studied.The interaction between CaSO_(4)and sulfides facilitates the conversion of CaSO_(4)into CaO,which is crucial for slag formation.The order of the influence of sulfide minerals on the conversion of CaSO_(4)is pyrite>sphalerite>galena.When using gypsum sludge exclusively as the calcium source,under optimal conditions with a CaO/SiO_(2)mass ratio of 0.8,an FeO/SiO_(2)mass ratio of 1.2,a melting temperature of 1150℃,an oxygen flow rate of 1.3 L/min,the recovery rates of Pb and Zn in the lead-rich slag reached 85.01%and 95.69%,respectively,with a sulfur content of 2.65 wt%.The As content in the smelting slag obtained by reduction smelting was 0.02 wt%.Resource utilization of gypsum sludge in lead smelting is a feasible method.