Proper utilization of the FeSO4·7H2O waste slag generated from TiO2 industry is an urgent need, and Fe3O4 particles are currently being widely used in the wastewater flocculation field. In this work, magnetite wa...Proper utilization of the FeSO4·7H2O waste slag generated from TiO2 industry is an urgent need, and Fe3O4 particles are currently being widely used in the wastewater flocculation field. In this work, magnetite was recovered from ferrous sulphate by a novel co-precipitation method with calcium hydroxide as the precipitant. Under optimum conditions, the obtained spherical magnetite particles are well crystallized with a Fe304 purity of 88.78%, but apt to aggregate with a median particle size of 1.83 μm. Magnetic measurement reveals the obtained Fe304 particles are soft magnetic with a saturation magnetization of 81.73 A-m2/kg. In addition, a highly crystallized gypsum co-product is obtained in blocky or irregular shape. Predictably, this study would provide additional opportunities for future application of low-cost Fe3O4 particles in water treatment field.展开更多
The solid sodium hydroxide neutralized acidic As-containing wastewater till pH value was 6. Green copper arsenite was prepared after copper sulfate was added into the neutralized wastewater when the molar ratio of Cu ...The solid sodium hydroxide neutralized acidic As-containing wastewater till pH value was 6. Green copper arsenite was prepared after copper sulfate was added into the neutralized wastewater when the molar ratio of Cu to As was 2：1 and pH value of the neutralized wastewater was adjusted to 8.0 by sodium hydroxide. The arsenious acid solution and red residue were produced after copper arsenite mixed with water according to the ratio of liquid to solid of 4：1 and copper arsenite was reduced by SO2 at 60℃ for 1 h. The white powder was gained after the arsenious acid solution was evaporated and cooled. Copper sulfate solution was obtained after the red residue was leached by H2SO4 solution under the action of air. The results show that red residue is Cu3（SO3）2·2H2O and the white powder is As2O3. The leaching rate of Cu reaches 99.00% when the leaching time is 1.5 h, molar ratio of H2SO4 to Cu is 1.70, H2SO4 concentration is 24% and the leaching temperature is 80 ℃. The direct recovery rate of copper sulfate is 79.11% and the content of CuSOa·5H2O is up to 98.33% in the product after evaporating and cooling the copper sulfate solution.展开更多
Ultrasonic treatment and hydrothermal method were applied in the traditional homogeneous precipitation for nano-TiO_2 preparation, which was used as carrier material for the production of honeycomb selective catalytic...Ultrasonic treatment and hydrothermal method were applied in the traditional homogeneous precipitation for nano-TiO_2 preparation, which was used as carrier material for the production of honeycomb selective catalytic reduction(SCR) catalyst. The influence rules of the two improved methods on characterization of TiO_2 samples, denitration activity and mechanical strength of honeycomb SCR catalyst samples were mainly focused on. The results indicate that the specific surface area, particle size and uniformity of TiO_2 samples are significantly improved by both of the ultrasonic and hydrothermal treatments compared with the traditional homogeneous precipitation. Also, the denitration activities of catalyst samples are enhanced by the two improved methods(the NO_x reduction ratio increases from 88.89% to 95.45% by ultrasonic homogeneous precipitation process, and to 94.12% by hydrothermal homogeneous precipitation process). On the other hand, because of good spherical shape and high particle distribution of TiO_2 sample from hydrothermal homogeneous precipitation process, the corresponding honeycomb catalyst samples get the best mechanical strength, which is even higher than that of the reference sample from commercial nano-TiO_2. So, it is concluded that the hydrothermal homogeneous precipitation can be a feasible and effective preparation method of TiO_2 carrier for the honeycomb SCR catalyst production.展开更多
基金Project(2013A090100013)supported by the Special Project on the Integration of Industry,Education and Research of Guangdong Province,ChinaProject(201407300993)supported by the High-Tech Research and Development Program of Xinjiang Uygur Autonomous Region,China
文摘Proper utilization of the FeSO4·7H2O waste slag generated from TiO2 industry is an urgent need, and Fe3O4 particles are currently being widely used in the wastewater flocculation field. In this work, magnetite was recovered from ferrous sulphate by a novel co-precipitation method with calcium hydroxide as the precipitant. Under optimum conditions, the obtained spherical magnetite particles are well crystallized with a Fe304 purity of 88.78%, but apt to aggregate with a median particle size of 1.83 μm. Magnetic measurement reveals the obtained Fe304 particles are soft magnetic with a saturation magnetization of 81.73 A-m2/kg. In addition, a highly crystallized gypsum co-product is obtained in blocky or irregular shape. Predictably, this study would provide additional opportunities for future application of low-cost Fe3O4 particles in water treatment field.
文摘The solid sodium hydroxide neutralized acidic As-containing wastewater till pH value was 6. Green copper arsenite was prepared after copper sulfate was added into the neutralized wastewater when the molar ratio of Cu to As was 2：1 and pH value of the neutralized wastewater was adjusted to 8.0 by sodium hydroxide. The arsenious acid solution and red residue were produced after copper arsenite mixed with water according to the ratio of liquid to solid of 4：1 and copper arsenite was reduced by SO2 at 60℃ for 1 h. The white powder was gained after the arsenious acid solution was evaporated and cooled. Copper sulfate solution was obtained after the red residue was leached by H2SO4 solution under the action of air. The results show that red residue is Cu3（SO3）2·2H2O and the white powder is As2O3. The leaching rate of Cu reaches 99.00% when the leaching time is 1.5 h, molar ratio of H2SO4 to Cu is 1.70, H2SO4 concentration is 24% and the leaching temperature is 80 ℃. The direct recovery rate of copper sulfate is 79.11% and the content of CuSOa·5H2O is up to 98.33% in the product after evaporating and cooling the copper sulfate solution.
基金Project(201031)supported by the Environmental Protection Scientific Research of Jiangsu Province,ChinaProject(BE2010184)supported by the Technology Support Program of Jiangsu Province-Industrial Parts,China
文摘Ultrasonic treatment and hydrothermal method were applied in the traditional homogeneous precipitation for nano-TiO_2 preparation, which was used as carrier material for the production of honeycomb selective catalytic reduction(SCR) catalyst. The influence rules of the two improved methods on characterization of TiO_2 samples, denitration activity and mechanical strength of honeycomb SCR catalyst samples were mainly focused on. The results indicate that the specific surface area, particle size and uniformity of TiO_2 samples are significantly improved by both of the ultrasonic and hydrothermal treatments compared with the traditional homogeneous precipitation. Also, the denitration activities of catalyst samples are enhanced by the two improved methods(the NO_x reduction ratio increases from 88.89% to 95.45% by ultrasonic homogeneous precipitation process, and to 94.12% by hydrothermal homogeneous precipitation process). On the other hand, because of good spherical shape and high particle distribution of TiO_2 sample from hydrothermal homogeneous precipitation process, the corresponding honeycomb catalyst samples get the best mechanical strength, which is even higher than that of the reference sample from commercial nano-TiO_2. So, it is concluded that the hydrothermal homogeneous precipitation can be a feasible and effective preparation method of TiO_2 carrier for the honeycomb SCR catalyst production.