A series of sulfided PtMo/ γ Al 2O 3 catalysts[ w (Mo)=9.0%] with different contents of Pt were characterized by using low temperature FTIR spectroscopy of adsorbed CO, while their HDS activity was investigated with ...A series of sulfided PtMo/ γ Al 2O 3 catalysts[ w (Mo)=9.0%] with different contents of Pt were characterized by using low temperature FTIR spectroscopy of adsorbed CO, while their HDS activity was investigated with thiophene as a model substrate. Experimentally, it was found that no existence of the bands related to the surface complexes of Al 3+ ←CO and Pt 0←CO→Pt 0 was observed at 77 K and that the rate of the thiophene HDS reaction(573 K) is well linearly proportional to the area of the Pt 0←CO band at 2 093 cm -1 with a higher extrapolated HDS rate compared to that of sulfided Mo/ γ Al 2O 3 catalyst at the zero content of platinum. On the basis of the results here, the conclusion may be made that the active monolayer phase of Pt Mo S may be formed over sulfided PtMo/ γ Al 2O 3 catalysts during the sulfidation process and that both Mo 2+ and Pt 0 sites for CO adsorption should be the active reaction centers of thiophene HDS.展开更多
采用常压微反、程序升温还原(TPR)、程序升温硫化(TPS)及原位红外光谱(IR)等技术,对Co Mo Al2O3催化剂的表征研究发现:在Co Mo Al2O3催化剂中不仅存在着Co、Mo中心,而且存在由Co、Mo相互作用产生的中心,Co Mo Al2O3催化剂的催化性能是...采用常压微反、程序升温还原(TPR)、程序升温硫化(TPS)及原位红外光谱(IR)等技术,对Co Mo Al2O3催化剂的表征研究发现:在Co Mo Al2O3催化剂中不仅存在着Co、Mo中心,而且存在由Co、Mo相互作用产生的中心,Co Mo Al2O3催化剂的催化性能是由Co、Mo中心和Co、Mo相互作用产生的中心共同作用的结果。展开更多
文摘A series of sulfided PtMo/ γ Al 2O 3 catalysts[ w (Mo)=9.0%] with different contents of Pt were characterized by using low temperature FTIR spectroscopy of adsorbed CO, while their HDS activity was investigated with thiophene as a model substrate. Experimentally, it was found that no existence of the bands related to the surface complexes of Al 3+ ←CO and Pt 0←CO→Pt 0 was observed at 77 K and that the rate of the thiophene HDS reaction(573 K) is well linearly proportional to the area of the Pt 0←CO band at 2 093 cm -1 with a higher extrapolated HDS rate compared to that of sulfided Mo/ γ Al 2O 3 catalyst at the zero content of platinum. On the basis of the results here, the conclusion may be made that the active monolayer phase of Pt Mo S may be formed over sulfided PtMo/ γ Al 2O 3 catalysts during the sulfidation process and that both Mo 2+ and Pt 0 sites for CO adsorption should be the active reaction centers of thiophene HDS.
文摘采用常压微反、程序升温还原(TPR)、程序升温硫化(TPS)及原位红外光谱(IR)等技术,对Co Mo Al2O3催化剂的表征研究发现:在Co Mo Al2O3催化剂中不仅存在着Co、Mo中心,而且存在由Co、Mo相互作用产生的中心,Co Mo Al2O3催化剂的催化性能是由Co、Mo中心和Co、Mo相互作用产生的中心共同作用的结果。