Many researchers found that the Fe2+together with less amount of Cu2+can accelerate the leaching of chalcopyrite.In this work,the leaching of chalcopyrite with Cu2+was investigated.The leaching residuals were examined...Many researchers found that the Fe2+together with less amount of Cu2+can accelerate the leaching of chalcopyrite.In this work,the leaching of chalcopyrite with Cu2+was investigated.The leaching residuals were examined by Raman spectroscopy.Based on the leaching experiments,the chemical equilibrium in solution was calculated using Visual MINTEQ.The results showed that the Fe in chalcopyrite lattice was replaced by Cu2+;therefore,the chalcopyrite transformed into covellite.Furthermore,the formation of chalcocite occurred when Fe2+and Fe3+were added to the solution containing Cu2+.The copper extraction increased with a decrease of the initial redox potential(or the ratio of Fe3+/Fe2+).展开更多
Reduction roasting-acid leaching process was utilized to process high-iron-content manganese oxide ore using black charcoal as reductant. The results indicate that, compared with the traditional reductant of anthracit...Reduction roasting-acid leaching process was utilized to process high-iron-content manganese oxide ore using black charcoal as reductant. The results indicate that, compared with the traditional reductant of anthracite, higher manganese extraction efficiency is achieved at lower roasting temperature and shorter residence time. The effects of roasting parameters on the leaching efficiency of Mn and Fe were studied, and the optimal parameters are determined as follows: roasting temperature is 650 °C, residence time is 40 min, and black charcoal dosage is 10%(mass fraction). Under these conditions, the leaching efficiency of Mn reaches 82.37% while that of Fe is controlled below 7%. XRD results show that a majority of MnO2 and Fe2O3 in the raw ore are reduced to MnO and Fe3O4, respectively.展开更多
基金Project(2016RS2016)supported by the Hunan Provincial Science and Technology Leader(Innovation Team of Interface Chemistry of Efficient and Clean Utilization of Complex Mineral Resources),ChinaProject supported by the Co-Innovation Centre for Clean and Efficient Utilization of Strategic Metal Mineral Resources,ChinaProject(2015CX005)supported by the Innovation Driven Plan of Central South University,China
文摘Many researchers found that the Fe2+together with less amount of Cu2+can accelerate the leaching of chalcopyrite.In this work,the leaching of chalcopyrite with Cu2+was investigated.The leaching residuals were examined by Raman spectroscopy.Based on the leaching experiments,the chemical equilibrium in solution was calculated using Visual MINTEQ.The results showed that the Fe in chalcopyrite lattice was replaced by Cu2+;therefore,the chalcopyrite transformed into covellite.Furthermore,the formation of chalcocite occurred when Fe2+and Fe3+were added to the solution containing Cu2+.The copper extraction increased with a decrease of the initial redox potential(or the ratio of Fe3+/Fe2+).
基金Project(2013JSJJ028)supported by the Teachers’Research Fund of Central South University,ChinaProject supported by Co-Innovation Center for Clean and Efficient Utilization of Strategic Mineral Resources,China
文摘Reduction roasting-acid leaching process was utilized to process high-iron-content manganese oxide ore using black charcoal as reductant. The results indicate that, compared with the traditional reductant of anthracite, higher manganese extraction efficiency is achieved at lower roasting temperature and shorter residence time. The effects of roasting parameters on the leaching efficiency of Mn and Fe were studied, and the optimal parameters are determined as follows: roasting temperature is 650 °C, residence time is 40 min, and black charcoal dosage is 10%(mass fraction). Under these conditions, the leaching efficiency of Mn reaches 82.37% while that of Fe is controlled below 7%. XRD results show that a majority of MnO2 and Fe2O3 in the raw ore are reduced to MnO and Fe3O4, respectively.