In the South Yellow Sea Basin,Mesozoic–Paleozoic marine strata are generally well developed with large thickness,and no substantial breakthroughs have been made in hydrocarbon exploration.Through research,it is belie...In the South Yellow Sea Basin,Mesozoic–Paleozoic marine strata are generally well developed with large thickness,and no substantial breakthroughs have been made in hydrocarbon exploration.Through research,it is believed that the Upper Permian–Lower Triassic can be regarded as a long-term base-level cycle.Based on drilling data,characteristics of the lithology–electric property combination cyclicity,and the special lithology,the long-term base-level cycle was divided into five medium-term base-level cycles(MC1–MC5).On this basis,the Permian–Triassic sedimentary systems and their filling model were analyzed in accordance with the change of base-level cycle and transition of sedimentary environment,as well as characteristics of the drilling sedimentary facies and seismic facies.The results show that there were six sedimentary systems(fluvial,delta,tidal flat,open platform,restricted platform,and continental shelf)developed in the Upper Permian–Lower Triassic,the sedimentary systems were distributed such that the water was deep in the northwest and shallow in the southeast,and there were two base-level cycle filling models(a relatively stable tidal flat facies and a rapidly transgressive continental shelf facies to stable platform facies)developed in the Upper Permian–Lower Triassic.These models can provide a basis for evaluation of the Mesozoic–Paleozoic hydrocarbon geology in the South Yellow Sea Basin.展开更多
For the purpose of describing the deformation characteristics of rocks,the effect of volume changes on mechanical properties of rocks should be taken into account with relation to the development of constitutive model...For the purpose of describing the deformation characteristics of rocks,the effect of volume changes on mechanical properties of rocks should be taken into account with relation to the development of constitutive model.Firstly,rocks are divided into three parts,i.e.,voids,a damaged part and an undamaged part in the course of loading.The void ratio was applied to describing the changes of voids or pores during the deformation process.Then,using statistical damage theory,a constitutive model was developed for rocks to describe their strain softening and hardening on the basis of investigating the relationship between the net stress and apparent stress,in which the influence of volume changes on rock behavior was correctly taken into account,such as the initial phase of compaction and the latter stage of dilation.Thirdly,a method of determining model parameters was also presented.Finally,this model was used to compare the theoretical results with those observed from experiments under conventional triaxial loading conditions.展开更多
It is of great significance for safety reason to obtain the triaxial compressive properties of cemented tailings backfill(CTB).The influence of cement content,curing age and confining pressure on strength and deformat...It is of great significance for safety reason to obtain the triaxial compressive properties of cemented tailings backfill(CTB).The influence of cement content,curing age and confining pressure on strength and deformation properties of CTB was examined and discussed.Results indicate that the triaxial compressive and deformation behavior of CTB is strongly affected by the cement content,curing age and confining pressure.The increase in cement content,curing age and confining pressure leads to a change in stress−strain behavior and an increase in the axial strain at failure and post-peak strength loss.The cohesion of CTB rises as the curing age and cement content increase.However,the enhancement in internal friction angle is trivial and negligible.It should be noted that the failure pattern of CTB samples in triaxial compression is mainly along a shear plane,the confining pressure restrains the lateral expansion and the bulging failure pattern is dominantly detected in CTB samples as curing age length and cement content increase.The results will help to better understand the triaxial mechanical and deformation behavior of CTB.展开更多
Porous and dense TiNi alloys were successfully fabricated by powder metallurgy(P/M) method, and to further improve their surface biocompatibility, surface modification techniques including grind using silicon-carbide(...Porous and dense TiNi alloys were successfully fabricated by powder metallurgy(P/M) method, and to further improve their surface biocompatibility, surface modification techniques including grind using silicon-carbide(SiC) paper, acid etching and alkali treatment were employed to produce either irregularly rough surface or micro-porous surface roughness. X-ray diffractometry(XRD), scanning electron microscopy(SEM) and energy dispersive X-ray spectroscopy(EDX) attached to SEM were used to characterize surface structure and the Ca-P coatings. Effects of the above surface treatments on the surface morphology, apatite forming ability were systematically investigated. Results indicate that all the above surface treatments increase the apatite forming ability of TiNi alloys in varying degrees when soaked in simulated body fluid(SBF). More apatite coatings formed on TiNi samples sintered at 1050℃ and 1100℃ due to their high porosity and pure TiNi phase that is beneficial to heterogeneous nucleation. Furthermore, more uniform apatite was fabricated on the sample sintered from the mixture of Ni and Ti powders.展开更多
Additive manufacturing(AM),also known as 3D-printing(3DP)technology,is an advanced manufacturing technology that has developed rapidly in the past 40 years.However,the ceramic material printing is still challenging be...Additive manufacturing(AM),also known as 3D-printing(3DP)technology,is an advanced manufacturing technology that has developed rapidly in the past 40 years.However,the ceramic material printing is still challenging because of the issue of cracking.Indirect 3D printing has been designed and drawn attention because of its high manufacturing speed and low cost.Indirect 3D printing separates the one-step forming process of direct 3D printing into binding and material sintering,avoiding the internal stress caused by rapid cooling,making it possible to realize the highquality ceramic component with complex shape.This paper presents the research progress of leading indirect 3D printing technologies,including binder jetting(BJ),stereolithography(SLA),and fused deposition modeling(FDM).At present,the additive manufacturing of ceramic materials is mainly achieved through indirect 3D printing technology,and these materials include silicon nitride,hydroxyapatite functional ceramics,silicon carbide structural ceramics.展开更多
基金Projects(41506080,41702162)supported by the National Natural Science Foundation of ChinaProjects(DD20160152,DD20160147,GZH200800503)supported by China Geological Survey+1 种基金Projects(XQ-2005-01,2009GYXQ10)supported by China Ministry of Land and ResourcesProject(201602004)supported by the Postdoctoral Innovation Foundation of Shandong Province,China
文摘In the South Yellow Sea Basin,Mesozoic–Paleozoic marine strata are generally well developed with large thickness,and no substantial breakthroughs have been made in hydrocarbon exploration.Through research,it is believed that the Upper Permian–Lower Triassic can be regarded as a long-term base-level cycle.Based on drilling data,characteristics of the lithology–electric property combination cyclicity,and the special lithology,the long-term base-level cycle was divided into five medium-term base-level cycles(MC1–MC5).On this basis,the Permian–Triassic sedimentary systems and their filling model were analyzed in accordance with the change of base-level cycle and transition of sedimentary environment,as well as characteristics of the drilling sedimentary facies and seismic facies.The results show that there were six sedimentary systems(fluvial,delta,tidal flat,open platform,restricted platform,and continental shelf)developed in the Upper Permian–Lower Triassic,the sedimentary systems were distributed such that the water was deep in the northwest and shallow in the southeast,and there were two base-level cycle filling models(a relatively stable tidal flat facies and a rapidly transgressive continental shelf facies to stable platform facies)developed in the Upper Permian–Lower Triassic.These models can provide a basis for evaluation of the Mesozoic–Paleozoic hydrocarbon geology in the South Yellow Sea Basin.
基金Project(2006AA11Z104) supported by the National High-Tech Research and Development Program of China
文摘For the purpose of describing the deformation characteristics of rocks,the effect of volume changes on mechanical properties of rocks should be taken into account with relation to the development of constitutive model.Firstly,rocks are divided into three parts,i.e.,voids,a damaged part and an undamaged part in the course of loading.The void ratio was applied to describing the changes of voids or pores during the deformation process.Then,using statistical damage theory,a constitutive model was developed for rocks to describe their strain softening and hardening on the basis of investigating the relationship between the net stress and apparent stress,in which the influence of volume changes on rock behavior was correctly taken into account,such as the initial phase of compaction and the latter stage of dilation.Thirdly,a method of determining model parameters was also presented.Finally,this model was used to compare the theoretical results with those observed from experiments under conventional triaxial loading conditions.
基金Projects(2018YFC0808403,2018YFE0123000)supported by the National Key Technologies Research&Development Program of ChinaProject(800015Z1185)supported by the Yueqi Young Scholar Project,ChinaProject(2020YJSNY04)supported by the Fundamental Research Funds for the Central Universities,China。
文摘It is of great significance for safety reason to obtain the triaxial compressive properties of cemented tailings backfill(CTB).The influence of cement content,curing age and confining pressure on strength and deformation properties of CTB was examined and discussed.Results indicate that the triaxial compressive and deformation behavior of CTB is strongly affected by the cement content,curing age and confining pressure.The increase in cement content,curing age and confining pressure leads to a change in stress−strain behavior and an increase in the axial strain at failure and post-peak strength loss.The cohesion of CTB rises as the curing age and cement content increase.However,the enhancement in internal friction angle is trivial and negligible.It should be noted that the failure pattern of CTB samples in triaxial compression is mainly along a shear plane,the confining pressure restrains the lateral expansion and the bulging failure pattern is dominantly detected in CTB samples as curing age length and cement content increase.The results will help to better understand the triaxial mechanical and deformation behavior of CTB.
基金Project(51274247) supported by the National Natural Science Foundation of ChinaProject(2014zzts177) support by the Fundamental Research Funds for the Central Universities,China
文摘Porous and dense TiNi alloys were successfully fabricated by powder metallurgy(P/M) method, and to further improve their surface biocompatibility, surface modification techniques including grind using silicon-carbide(SiC) paper, acid etching and alkali treatment were employed to produce either irregularly rough surface or micro-porous surface roughness. X-ray diffractometry(XRD), scanning electron microscopy(SEM) and energy dispersive X-ray spectroscopy(EDX) attached to SEM were used to characterize surface structure and the Ca-P coatings. Effects of the above surface treatments on the surface morphology, apatite forming ability were systematically investigated. Results indicate that all the above surface treatments increase the apatite forming ability of TiNi alloys in varying degrees when soaked in simulated body fluid(SBF). More apatite coatings formed on TiNi samples sintered at 1050℃ and 1100℃ due to their high porosity and pure TiNi phase that is beneficial to heterogeneous nucleation. Furthermore, more uniform apatite was fabricated on the sample sintered from the mixture of Ni and Ti powders.
基金Project(51901020)supported by the National Natural Science Foundation of ChinaProject(2019JZZY010327)supported by Shandong Key Research and Development Plan,China+1 种基金Project(201942074001)supported by Aeronautical Science Foundation of ChinaProject(FRF-IP-20-05)supported by the Fundamental Research Funds for the Central Universities,China。
文摘Additive manufacturing(AM),also known as 3D-printing(3DP)technology,is an advanced manufacturing technology that has developed rapidly in the past 40 years.However,the ceramic material printing is still challenging because of the issue of cracking.Indirect 3D printing has been designed and drawn attention because of its high manufacturing speed and low cost.Indirect 3D printing separates the one-step forming process of direct 3D printing into binding and material sintering,avoiding the internal stress caused by rapid cooling,making it possible to realize the highquality ceramic component with complex shape.This paper presents the research progress of leading indirect 3D printing technologies,including binder jetting(BJ),stereolithography(SLA),and fused deposition modeling(FDM).At present,the additive manufacturing of ceramic materials is mainly achieved through indirect 3D printing technology,and these materials include silicon nitride,hydroxyapatite functional ceramics,silicon carbide structural ceramics.