A toughener that can effectively improve the interlaminar toughness in carbon fiber composites is crucial for various applications.We investigated,the toughening effects of phenolphthalein-based cardo poly(ether sulfo...A toughener that can effectively improve the interlaminar toughness in carbon fiber composites is crucial for various applications.We investigated,the toughening effects of phenolphthalein-based cardo poly(ether sulfone)(PES-C)on E51/DETDA epoxy and its carbon fiber composites(CFCs).Scanning electron microscopy showed that the phase structures of PES-C/epoxy blends change from island(of dispersed phase)structures to bi-continuous structures(of the matrix)as the PES-C content increased,which is associated with reaction-induced phase separation.After adding 15 phr PES-C,the glass transition temperature(T_(g))of the blends increased by 51.5℃,and the flexural strength,impact strength and fracture toughness of the blends were improved by 41.1%,186.2%and 42.7%,respectively.These improvements could be attributed to the phase separation structure of the PES-C/epoxy sys-tem.A PES-C film was used to improve the mode-II fracture toughness(G_(IIC))of CFCs.The G_(IIC) value of the 7μm PES-C film toughened laminate was improved by 80.3%compared to that of the control laminate.The increase in G_(IIC) was attributed to cohesive failure and plastic deformation in the interleaving region.展开更多
Resin matrix carbon brush composites(RMCBCs)are critical materials for high-powered electric tools.However,effectively improving their wear resistance and heat dissipation remains a challenge.RMCBCs prepared with flak...Resin matrix carbon brush composites(RMCBCs)are critical materials for high-powered electric tools.However,effectively improving their wear resistance and heat dissipation remains a challenge.RMCBCs prepared with flake graphite powders that were evenly loaded with tungsten copper composite powder(RMCBCs-W@Cu)exhibited a low wear rate of 1.63 mm^(3)/h,exhibiting 48.6%reduction in the wear rate relative to RCMBCs without additives(RMCBCs-0).In addition,RMCBCs-W@Cu achieved a low friction coefficient of 0.243 and low electric spark grade.These findings indicate that tungsten copper composite powders provide particle reinforcement and generate a gradation effect for the epoxy resin(i.e.,connecting phase)in RMCBCs,which weakens the wear of RMCBCs caused by fatigue under a cyclic current-carrying wear.展开更多
In order to increase the understanding of the pyrolysis mechanism, Fourier transform infrared spectroscopy (FT-IR) and thermogravimetry-mass spectrometric coupling technique (TG-MS) were used to study the pyrolysis be...In order to increase the understanding of the pyrolysis mechanism, Fourier transform infrared spectroscopy (FT-IR) and thermogravimetry-mass spectrometric coupling technique (TG-MS) were used to study the pyrolysis behavior of furfural-acetone resin used for new carbon materials. The curing and carbonization mechanisms of furfural-acetone resin were mainly investigated; structural changes and volatile products evolved during pyrolysis were analyzed. The results indicate that, during pyrolysis of furfural-acetone resin adding 7% (mass fraction) phosphorous acid as curing agent, the rupture of C—O bond in the five-membered heterocycle firstly takes place to release oxygen atoms and then does the C—H bond, which enable the molecular chain to cross-link and condense, then lead to the formation of three dimensional networking structure. With the increase of pyrolyzing temperature, the scission of methyl and the opening of furan ring are generated. As a result, the recomposition of molecular chain structure is generated and a hexatomic fused ring containing double bonds is built. The main volatile products during pyrolysis of furfural- acetone resin are H2O, and a small mount of CO, CO2 and CH4. At elevated temperatures, dehydrogenation takes place and hydrogen gas is evolved.展开更多
文摘A toughener that can effectively improve the interlaminar toughness in carbon fiber composites is crucial for various applications.We investigated,the toughening effects of phenolphthalein-based cardo poly(ether sulfone)(PES-C)on E51/DETDA epoxy and its carbon fiber composites(CFCs).Scanning electron microscopy showed that the phase structures of PES-C/epoxy blends change from island(of dispersed phase)structures to bi-continuous structures(of the matrix)as the PES-C content increased,which is associated with reaction-induced phase separation.After adding 15 phr PES-C,the glass transition temperature(T_(g))of the blends increased by 51.5℃,and the flexural strength,impact strength and fracture toughness of the blends were improved by 41.1%,186.2%and 42.7%,respectively.These improvements could be attributed to the phase separation structure of the PES-C/epoxy sys-tem.A PES-C film was used to improve the mode-II fracture toughness(G_(IIC))of CFCs.The G_(IIC) value of the 7μm PES-C film toughened laminate was improved by 80.3%compared to that of the control laminate.The increase in G_(IIC) was attributed to cohesive failure and plastic deformation in the interleaving region.
基金Projects(51772081,51837009,51971091)supported by the National Natural Science Foundation of ChinaProject(HFZL2018CXY003-4)supported by the Industry-University-Research Cooperation of AECC,ChinaProject(kq1902046)supported by the Major Science and Technology Projects of Changsha City,China。
文摘Resin matrix carbon brush composites(RMCBCs)are critical materials for high-powered electric tools.However,effectively improving their wear resistance and heat dissipation remains a challenge.RMCBCs prepared with flake graphite powders that were evenly loaded with tungsten copper composite powder(RMCBCs-W@Cu)exhibited a low wear rate of 1.63 mm^(3)/h,exhibiting 48.6%reduction in the wear rate relative to RCMBCs without additives(RMCBCs-0).In addition,RMCBCs-W@Cu achieved a low friction coefficient of 0.243 and low electric spark grade.These findings indicate that tungsten copper composite powders provide particle reinforcement and generate a gradation effect for the epoxy resin(i.e.,connecting phase)in RMCBCs,which weakens the wear of RMCBCs caused by fatigue under a cyclic current-carrying wear.
基金Project(2006CB600902) supported by the Major State Basic Research and Development Program of China
文摘In order to increase the understanding of the pyrolysis mechanism, Fourier transform infrared spectroscopy (FT-IR) and thermogravimetry-mass spectrometric coupling technique (TG-MS) were used to study the pyrolysis behavior of furfural-acetone resin used for new carbon materials. The curing and carbonization mechanisms of furfural-acetone resin were mainly investigated; structural changes and volatile products evolved during pyrolysis were analyzed. The results indicate that, during pyrolysis of furfural-acetone resin adding 7% (mass fraction) phosphorous acid as curing agent, the rupture of C—O bond in the five-membered heterocycle firstly takes place to release oxygen atoms and then does the C—H bond, which enable the molecular chain to cross-link and condense, then lead to the formation of three dimensional networking structure. With the increase of pyrolyzing temperature, the scission of methyl and the opening of furan ring are generated. As a result, the recomposition of molecular chain structure is generated and a hexatomic fused ring containing double bonds is built. The main volatile products during pyrolysis of furfural- acetone resin are H2O, and a small mount of CO, CO2 and CH4. At elevated temperatures, dehydrogenation takes place and hydrogen gas is evolved.