The cathode material Li 1+ x Mn 2O 4 was prepared by a modified citric acid complexation method. The influences of temperature, sintering time and n (Li)/ n (Mn) ratio on the structure of the products have been explor...The cathode material Li 1+ x Mn 2O 4 was prepared by a modified citric acid complexation method. The influences of temperature, sintering time and n (Li)/ n (Mn) ratio on the structure of the products have been explored, characterized and tested by XRD, TEM, BET measurements. The sample sintered at 750 ℃ for 12 h had greater charge/discharge capacity, better cyclic stability under electric current charge/discharge cycle. The initial capacity reached 120 mA·h/g with the charge/discharge efficieney of 98% and maintained 115 mA·h/g after 50 cycles.展开更多
用柠檬酸络合法制备了钙钛矿型 La Fe O3及 La Fe1 - x Cux O3化合物 ,测定了其对酸性红 3B等水溶性染料的光催化降解活性 .利用红外、紫外和光声光谱、正电子寿命谱及光电子能谱等技术分析了 La Fe O3的光催化性能及掺杂对其活性的影...用柠檬酸络合法制备了钙钛矿型 La Fe O3及 La Fe1 - x Cux O3化合物 ,测定了其对酸性红 3B等水溶性染料的光催化降解活性 .利用红外、紫外和光声光谱、正电子寿命谱及光电子能谱等技术分析了 La Fe O3的光催化性能及掺杂对其活性的影响 .结果表明 ,掺杂 Cu2 + 可使 La Fe展开更多
文摘The cathode material Li 1+ x Mn 2O 4 was prepared by a modified citric acid complexation method. The influences of temperature, sintering time and n (Li)/ n (Mn) ratio on the structure of the products have been explored, characterized and tested by XRD, TEM, BET measurements. The sample sintered at 750 ℃ for 12 h had greater charge/discharge capacity, better cyclic stability under electric current charge/discharge cycle. The initial capacity reached 120 mA·h/g with the charge/discharge efficieney of 98% and maintained 115 mA·h/g after 50 cycles.
文摘用柠檬酸络合法制备了钙钛矿型 La Fe O3及 La Fe1 - x Cux O3化合物 ,测定了其对酸性红 3B等水溶性染料的光催化降解活性 .利用红外、紫外和光声光谱、正电子寿命谱及光电子能谱等技术分析了 La Fe O3的光催化性能及掺杂对其活性的影响 .结果表明 ,掺杂 Cu2 + 可使 La Fe