A process of purification of coal-based coke powder as anode the treatment of coke powder with dilute hydrofluoric acid solution, for Li-ion batteries was attempted. The process started with followed by united-acid-le...A process of purification of coal-based coke powder as anode the treatment of coke powder with dilute hydrofluoric acid solution, for Li-ion batteries was attempted. The process started with followed by united-acid-leaching using sulfuric acid and hydrochloric acid. The effects of altering the hydrofluoric acid addition, hydrofluoric acid concentration, contact time, temperature and acid type were investigated. A minimum ash content of 0.35% was obtained when proper conditions were applied. The electrochemical performance of purified coke powder shows greatly improved electrochemical performance. The as-purified coke powder presented an initial reversible capacity of 257.4 mAh/g and a retention rate of 95% after 50 cycles. The proposed purification process paves a way to prepare a promising anode material with good performance with low cost of coke powder for Li-ion batteries.展开更多
Li Fe PO4/C was prepared via solid state reaction and characterized with X-ray powder diffraction and charge–discharge test. As-prepared Li Fe PO4/C has a triphylite structure and exhibits an excellent rate capabilit...Li Fe PO4/C was prepared via solid state reaction and characterized with X-ray powder diffraction and charge–discharge test. As-prepared Li Fe PO4/C has a triphylite structure and exhibits an excellent rate capability and capacity retention. Electrochemical impedance spectroscopy(EIS) was applied to investigate LixFe PO4/C(0<x<1) electrode on temperature variation. The valid equivalent circuit for EIS fitting was determined which contains an intercalation capacitance for Li+ ion accumulation and consumption in the electrode reaction. The surface layer impedance needs to be included in the equivalent circuit when Li Fe PO4/C is deeply delithiated at a relatively high temperature. EIS examination indicates that a temperature rise leads to a better reversibility, lower charge transfer resistance, higher exchange current density J0 and greater Li+ ion diffusion coefficient for the LixFe PO4/C electrode process. The Li+ ion concentration in LixFe PO4/C is potential to impact the Li+ ion diffusion coefficient, and a decrease in the former results in an increase in the latter.展开更多
The electrochemical degradation of reed pulp black liquor containing lignin pretreated by acidification method was investigated using a three-dimensional electrode reactor. Using activated carbon as particle electrode...The electrochemical degradation of reed pulp black liquor containing lignin pretreated by acidification method was investigated using a three-dimensional electrode reactor. Using activated carbon as particle electrode, the effects of p H value, reaction temperature, electrolysis time and current on residual concentration of total organic carbon(TOC) were discussed in detail. The optimal conditions were obtained: pH 2.5, influent flow rate of 200 mL/min, 25 °C, 300 mA and 2h of electrolysis time, and the removal efficiency of TOC maintains at 35.57 %. The results of the electrochemical method indicate that ·OH radicals are produced in activated carbon anode in the electrolysis process and then adsorbed on the activated carbon surface. Microcell consists of ·OH radicals and the absorbed lignin. With the microcell reaction, the lignin is degraded, while the anodic polarized curve illustrates that the lignin is obviously oxidized in the anode. The contributions of direct and indirect electrolyses to the TOC removal ratio are about 50%, respectively.展开更多
基金Projects(51274240,51204209) supported by the National Natural Science Foundation of ChinaProject(2012M521545) supported by the National Postdoctoral Science Foundation of China
文摘A process of purification of coal-based coke powder as anode the treatment of coke powder with dilute hydrofluoric acid solution, for Li-ion batteries was attempted. The process started with followed by united-acid-leaching using sulfuric acid and hydrochloric acid. The effects of altering the hydrofluoric acid addition, hydrofluoric acid concentration, contact time, temperature and acid type were investigated. A minimum ash content of 0.35% was obtained when proper conditions were applied. The electrochemical performance of purified coke powder shows greatly improved electrochemical performance. The as-purified coke powder presented an initial reversible capacity of 257.4 mAh/g and a retention rate of 95% after 50 cycles. The proposed purification process paves a way to prepare a promising anode material with good performance with low cost of coke powder for Li-ion batteries.
基金Project(2010ZC051)supported by the Natural Science Foundation of Yunnan Province,ChinaProject(20140439)supported by Analysis and Testing Foundation from Kunming University of Science and Technology,ChinaProject(14118245)supported by Starting Research Fund from Kunming University of Science and Technology,China
文摘Li Fe PO4/C was prepared via solid state reaction and characterized with X-ray powder diffraction and charge–discharge test. As-prepared Li Fe PO4/C has a triphylite structure and exhibits an excellent rate capability and capacity retention. Electrochemical impedance spectroscopy(EIS) was applied to investigate LixFe PO4/C(0<x<1) electrode on temperature variation. The valid equivalent circuit for EIS fitting was determined which contains an intercalation capacitance for Li+ ion accumulation and consumption in the electrode reaction. The surface layer impedance needs to be included in the equivalent circuit when Li Fe PO4/C is deeply delithiated at a relatively high temperature. EIS examination indicates that a temperature rise leads to a better reversibility, lower charge transfer resistance, higher exchange current density J0 and greater Li+ ion diffusion coefficient for the LixFe PO4/C electrode process. The Li+ ion concentration in LixFe PO4/C is potential to impact the Li+ ion diffusion coefficient, and a decrease in the former results in an increase in the latter.
基金Project(50925417)supported by the National Natureal Science Foundation for Distinguished Young Scholar of ChinaProject(51074191)supported by the National Natural Science Foundation of China
文摘The electrochemical degradation of reed pulp black liquor containing lignin pretreated by acidification method was investigated using a three-dimensional electrode reactor. Using activated carbon as particle electrode, the effects of p H value, reaction temperature, electrolysis time and current on residual concentration of total organic carbon(TOC) were discussed in detail. The optimal conditions were obtained: pH 2.5, influent flow rate of 200 mL/min, 25 °C, 300 mA and 2h of electrolysis time, and the removal efficiency of TOC maintains at 35.57 %. The results of the electrochemical method indicate that ·OH radicals are produced in activated carbon anode in the electrolysis process and then adsorbed on the activated carbon surface. Microcell consists of ·OH radicals and the absorbed lignin. With the microcell reaction, the lignin is degraded, while the anodic polarized curve illustrates that the lignin is obviously oxidized in the anode. The contributions of direct and indirect electrolyses to the TOC removal ratio are about 50%, respectively.