To enhance the separation selectivity of Mg-MOF-74 towards CO_(2) in a CO_(2)/N_(2) mixture,a series of Mg-MOF-74 and Ni_(x)/Mg_(1-x)-MOF-74 adsorbents were prepared by solvothermal synthesis in this paper.It was foun...To enhance the separation selectivity of Mg-MOF-74 towards CO_(2) in a CO_(2)/N_(2) mixture,a series of Mg-MOF-74 and Ni_(x)/Mg_(1-x)-MOF-74 adsorbents were prepared by solvothermal synthesis in this paper.It was found that the adsorption capacity of Mg-MOF-74 for CO_(2) could be effectively increased by optimizing the amount of acetic acid.On this basis,the bimetal MOF-74 adsorbent was prepared by metal modification.The multi-component dynamic adsorption penetration analysis was utilized to examine the CO_(2) adsorption capacity and CO_(2)/N_(2) selectivity of the diverse adsorbent materials.The results showed that Ni0.11/Mg0.89-MOF-74 showed a CO_(2) adsorption capacity of 7.02 mmol/g under pure CO_(2) atmosphere and had a selectivity of 20.50 for CO_(2)/N_(2) under 15% CO_(2)/85%N_(2) conditions,which was 10.2% and 18.02% higher than that of Mg-MOF-74 respectively.Combining XPS,SEM and N_(2) adsorption-desorption characterization analysis,it was attributed to the effect of the more stable unsaturated metal sites Ni into the Mg-MOF-74 on the pore structure and the synergistic interaction between the two metals.Density Functional Theory(DFT)simulations revealed that the synergistic interaction between modulated the electrostatic potential strength and gradient of the material,which was more favorable for the adsorption of CO_(2) molecules with small diameters and large quadrupole moment.In addition,the Ni0.11/Mg0.89-MOF-74 showed commendable cyclic stability,underscoring its promising potential for practical applications.展开更多
To study the physical and mechanical properties of coal rock after treatment at different temperatures under impact loading, dynamic compression experiments were conducted by using a split Hopkinson pressure bar(SHPB)...To study the physical and mechanical properties of coal rock after treatment at different temperatures under impact loading, dynamic compression experiments were conducted by using a split Hopkinson pressure bar(SHPB). The stress–strain curves of specimens under impact loading were obtained, and then four indexes affected by temperature were analyzed in the experiment: the longitudinal wave velocity, elastic modulus, peak stress and peak strain. Among these indexes, the elastic modulus was utilized to express the specimens' damage characteristics. The results show that the stress–strain curves under impact loading lack the stage of micro-fissure closure and the slope of the elastic deformation stage is higher than that under static loading. Due to the dynamic loading effect, the peak stress increases while peak strain decreases. The dynamic mechanical properties of coal rock show obvious temperature effects. The longitudinal wave velocity, elastic modulus and peak stress all decrease to different extents with increasing temperature, while the peak strain increases continuously. During the whole heating process, the thermal damage value continues to increase linearly, which indicates that the internal structure of coal rock is gradually damaged by high temperature.展开更多
The size of bubbles created in the flotation process is of great importance to the efficiency of the mineral separation achieved.Meanwhile,it is believed that frother transport between phases is perhaps the most impor...The size of bubbles created in the flotation process is of great importance to the efficiency of the mineral separation achieved.Meanwhile,it is believed that frother transport between phases is perhaps the most important reason for the interactive nature of the phenomena occurring in the bulk and froth phases in flotation,as frother adsorbed in the surface of rising bubbles is removed from the bulk phase and then released into the froth as a fraction of the bubbles burst.This causes the increased concentration in the froth compared to the bulk concentration,named as frother partitioning.Partitioning reflects the adsorption of frother on bubbles and how to influence bubble size is not known.There currently exists no such a topic aiming to link these two key parameters.To fill this vacancy,the correspondence between bubble size and frother partitioning was examined.Bubble size was measured by sampling-for-imaging(SFI)technique.Using total organic carbon(TOC)analysis to measure the frother partitioning between froth and bulk phases was determined.Measurements have shown,with no exceptions including four different frothers,higher frother concentration is in the bulk than in the froth.The results also show strong partitioning giving an increase in bubble size which implies there is a compelling relationship between these two,represented by CFroth/CBulk and D32.The CFroth/CBulkand D32 curves show similar exponential decay relationships as a function of added frother in the system,strongly suggesting that the frother concentration gradient between the bulk solution and the bubble interface is the driving force contributing to bubble size reduction.展开更多
基金supported by National Natural Science Foundation of China(U23A20100)the Strategic Priority Research Program(A)of the Chinese Academy of Sciences(XDA0390404)+5 种基金ICC CAS SCJC-DT-2023-03,the Foundation of State Key Laboratory of Coal Conversion(J24-25-619)Youth Innovation Promotion Association CAS(2018209,2020179)Key R&D Program of Shanxi Province(202102090301008,202202090301013)the special fund for S&T Innovation Team of Shanxi Province(202204051001012)Project of International Cooperation and Exchange NSFC-RFBR(22011530069)Tianjin Science and Technology Plan Project(22YFYSHZ00290)。
文摘To enhance the separation selectivity of Mg-MOF-74 towards CO_(2) in a CO_(2)/N_(2) mixture,a series of Mg-MOF-74 and Ni_(x)/Mg_(1-x)-MOF-74 adsorbents were prepared by solvothermal synthesis in this paper.It was found that the adsorption capacity of Mg-MOF-74 for CO_(2) could be effectively increased by optimizing the amount of acetic acid.On this basis,the bimetal MOF-74 adsorbent was prepared by metal modification.The multi-component dynamic adsorption penetration analysis was utilized to examine the CO_(2) adsorption capacity and CO_(2)/N_(2) selectivity of the diverse adsorbent materials.The results showed that Ni0.11/Mg0.89-MOF-74 showed a CO_(2) adsorption capacity of 7.02 mmol/g under pure CO_(2) atmosphere and had a selectivity of 20.50 for CO_(2)/N_(2) under 15% CO_(2)/85%N_(2) conditions,which was 10.2% and 18.02% higher than that of Mg-MOF-74 respectively.Combining XPS,SEM and N_(2) adsorption-desorption characterization analysis,it was attributed to the effect of the more stable unsaturated metal sites Ni into the Mg-MOF-74 on the pore structure and the synergistic interaction between the two metals.Density Functional Theory(DFT)simulations revealed that the synergistic interaction between modulated the electrostatic potential strength and gradient of the material,which was more favorable for the adsorption of CO_(2) molecules with small diameters and large quadrupole moment.In addition,the Ni0.11/Mg0.89-MOF-74 showed commendable cyclic stability,underscoring its promising potential for practical applications.
基金Projects(41272304,51304241,51204068)supported by the National Natural Science Foundation of ChinaProject(2014M552164)supported by the Postdoctoral Science Foundation of ChinaProject(20130162120015)supported by the PhD Programs Foundation of Ministry of Education of China
文摘To study the physical and mechanical properties of coal rock after treatment at different temperatures under impact loading, dynamic compression experiments were conducted by using a split Hopkinson pressure bar(SHPB). The stress–strain curves of specimens under impact loading were obtained, and then four indexes affected by temperature were analyzed in the experiment: the longitudinal wave velocity, elastic modulus, peak stress and peak strain. Among these indexes, the elastic modulus was utilized to express the specimens' damage characteristics. The results show that the stress–strain curves under impact loading lack the stage of micro-fissure closure and the slope of the elastic deformation stage is higher than that under static loading. Due to the dynamic loading effect, the peak stress increases while peak strain decreases. The dynamic mechanical properties of coal rock show obvious temperature effects. The longitudinal wave velocity, elastic modulus and peak stress all decrease to different extents with increasing temperature, while the peak strain increases continuously. During the whole heating process, the thermal damage value continues to increase linearly, which indicates that the internal structure of coal rock is gradually damaged by high temperature.
基金Project supported by the Collaborative Research and Development Program of Natural Sciences and Engineering Research Council of Canada
文摘The size of bubbles created in the flotation process is of great importance to the efficiency of the mineral separation achieved.Meanwhile,it is believed that frother transport between phases is perhaps the most important reason for the interactive nature of the phenomena occurring in the bulk and froth phases in flotation,as frother adsorbed in the surface of rising bubbles is removed from the bulk phase and then released into the froth as a fraction of the bubbles burst.This causes the increased concentration in the froth compared to the bulk concentration,named as frother partitioning.Partitioning reflects the adsorption of frother on bubbles and how to influence bubble size is not known.There currently exists no such a topic aiming to link these two key parameters.To fill this vacancy,the correspondence between bubble size and frother partitioning was examined.Bubble size was measured by sampling-for-imaging(SFI)technique.Using total organic carbon(TOC)analysis to measure the frother partitioning between froth and bulk phases was determined.Measurements have shown,with no exceptions including four different frothers,higher frother concentration is in the bulk than in the froth.The results also show strong partitioning giving an increase in bubble size which implies there is a compelling relationship between these two,represented by CFroth/CBulk and D32.The CFroth/CBulkand D32 curves show similar exponential decay relationships as a function of added frother in the system,strongly suggesting that the frother concentration gradient between the bulk solution and the bubble interface is the driving force contributing to bubble size reduction.