In the printing industry,the common method of coloring relies on inks,which contains amounts of chemical agents,causing environment pollution.However,structural color achieves coloration through the refraction and dif...In the printing industry,the common method of coloring relies on inks,which contains amounts of chemical agents,causing environment pollution.However,structural color achieves coloration through the refraction and diffraction of light by periodic structure,offering eco-friendly and fade-resistant advantages,as well as colorful.In this study,screen printing was used to create patterned mask on paper substrates.Then,coated SiO_(2)microspheres on the mask to create structural color patterns with angle-dependent color characteristics.The patterns showed color changes from rose-red to orange to green by changing the viewing angle.By changing the color grayscale,the absorption of stray light by the substrate was enhanced,thereby the brightness and saturation of the structural color improved too.This method is simple,cost-effective,and environmentally friendly,and it has highly promising for the application in printing and anti-counterfeiting.展开更多
The crystal structure,formation kinetics and micro-morphology of CaO·SiO2 during high-temperature sintering process were studied in low-calcium system by XRD,FT-IR,Raman and SEM-EDS methods.When the molar ratio o...The crystal structure,formation kinetics and micro-morphology of CaO·SiO2 during high-temperature sintering process were studied in low-calcium system by XRD,FT-IR,Raman and SEM-EDS methods.When the molar ratio of CaCO3 to SiO2 is 1.0,β-2CaO·SiO2 forms firstly during the heating process,and then CaO·SiO2 is generated by the transformation reaction of pre-formed 2CaO·SiO2 with SiO2.3CaO·SiO2 and 3CaO·2SiO2 do not form either in the heating or sintering process.Rising the sintering temperature and prolonging the holding time promote the phase transition of 2CaO·SiO2 to CaO·SiO2,resulting in the sintered products a small blue shift and broadening in Raman spectra.The content of CS can reach 97.4%when sintered at 1400℃ for 1 h.The formation kinetics of CaO·SiO2 follows the second-order chemical reaction model,and the corresponding apparent activation energy and pre-exponential factor are 505.82 kJ/mol and 2.16×10^14 s^−1 respectively.展开更多
文摘In the printing industry,the common method of coloring relies on inks,which contains amounts of chemical agents,causing environment pollution.However,structural color achieves coloration through the refraction and diffraction of light by periodic structure,offering eco-friendly and fade-resistant advantages,as well as colorful.In this study,screen printing was used to create patterned mask on paper substrates.Then,coated SiO_(2)microspheres on the mask to create structural color patterns with angle-dependent color characteristics.The patterns showed color changes from rose-red to orange to green by changing the viewing angle.By changing the color grayscale,the absorption of stray light by the substrate was enhanced,thereby the brightness and saturation of the structural color improved too.This method is simple,cost-effective,and environmentally friendly,and it has highly promising for the application in printing and anti-counterfeiting.
基金Projects(51674075,51774079)supported by the National Natural Science Foundation of ChinaProject(2018YFC1901903)supported by the National Key R&D Program of ChinaProject(N182508026)supported by the Fundamental Research Funds for the Central Universities of China。
文摘The crystal structure,formation kinetics and micro-morphology of CaO·SiO2 during high-temperature sintering process were studied in low-calcium system by XRD,FT-IR,Raman and SEM-EDS methods.When the molar ratio of CaCO3 to SiO2 is 1.0,β-2CaO·SiO2 forms firstly during the heating process,and then CaO·SiO2 is generated by the transformation reaction of pre-formed 2CaO·SiO2 with SiO2.3CaO·SiO2 and 3CaO·2SiO2 do not form either in the heating or sintering process.Rising the sintering temperature and prolonging the holding time promote the phase transition of 2CaO·SiO2 to CaO·SiO2,resulting in the sintered products a small blue shift and broadening in Raman spectra.The content of CS can reach 97.4%when sintered at 1400℃ for 1 h.The formation kinetics of CaO·SiO2 follows the second-order chemical reaction model,and the corresponding apparent activation energy and pre-exponential factor are 505.82 kJ/mol and 2.16×10^14 s^−1 respectively.