Mg-8Sn-1Al-1Zn-xNi(x=0.5%, 1.0%, 1.5%, 2.0%, mass fraction) alloys were designed and prepared. The microstructures and the mechanical properties were studied by using optical microscope, scanning electronic microscope...Mg-8Sn-1Al-1Zn-xNi(x=0.5%, 1.0%, 1.5%, 2.0%, mass fraction) alloys were designed and prepared. The microstructures and the mechanical properties were studied by using optical microscope, scanning electronic microscope, energy dispersive X-ray spectroscope, X-ray diffraction and a standard universal testing machine. The results show that the microstructure of Ni-containing alloys consist of α-Mg, Mg2 Sn, β-Mg-Ni-Al and γ-AlNi phases. No β-Mg-Ni-Al phase was observed in TAZ811-2.0Ni alloy due to its 1:1 atomic ratio of Ni/Al. The addition of Ni refines the α-Mg dendrites and suppresses the formation of coarse Mg2 Sn phase. The tensile properties results show that the TAZ811-0.5Ni alloy presented the best mechanical properties, which is due to the rod-like β-Mg-Ni-Al phase, refined α-Mg dendrites and Mg2 Sn phase, as well as γ-AlNi phase. The tensile fracture mechanism transits from cleavage to quasi-cleavage fracture with the increasing Ni addition.展开更多
基金Projects supported by the Shanxi Selective Funds for Returned Scholars,ChinaProject(2013021013-4)supported by the Shanxi Province Science Foundation for Youths China+1 种基金Projects(2012L053,2012L003)supported by the Taiyuan University of Technology Funds for Young Scientists,ChinaProject(2014021017-2)supported by the Natural Science Foundation for Young Scientists for Shanxi Province,China
文摘Mg-8Sn-1Al-1Zn-xNi(x=0.5%, 1.0%, 1.5%, 2.0%, mass fraction) alloys were designed and prepared. The microstructures and the mechanical properties were studied by using optical microscope, scanning electronic microscope, energy dispersive X-ray spectroscope, X-ray diffraction and a standard universal testing machine. The results show that the microstructure of Ni-containing alloys consist of α-Mg, Mg2 Sn, β-Mg-Ni-Al and γ-AlNi phases. No β-Mg-Ni-Al phase was observed in TAZ811-2.0Ni alloy due to its 1:1 atomic ratio of Ni/Al. The addition of Ni refines the α-Mg dendrites and suppresses the formation of coarse Mg2 Sn phase. The tensile properties results show that the TAZ811-0.5Ni alloy presented the best mechanical properties, which is due to the rod-like β-Mg-Ni-Al phase, refined α-Mg dendrites and Mg2 Sn phase, as well as γ-AlNi phase. The tensile fracture mechanism transits from cleavage to quasi-cleavage fracture with the increasing Ni addition.