The reinforcement corrosion is the pitting corrosion of chloride corrosion.Hence,in this study,the variations of reinforcement tensile strength due to stress concentration of pitting corrosion are analyzed.The stress ...The reinforcement corrosion is the pitting corrosion of chloride corrosion.Hence,in this study,the variations of reinforcement tensile strength due to stress concentration of pitting corrosion are analyzed.The stress concentration consequence of corrosion on the reinforcement tensile capacity is studied utilizing tension tests and creating different ABAQUS software models.According to the modelling in various corrosion depths,strength reduction is less than 5%in corrosion with pit radius to reinforcement diameter ratio up to 0.3 and for corrosions higher than 0.4,the measure of capacity reduction is increased more to 30%.展开更多
In order to investigate the tensile bond anchorage properties of Australian 500N steel bars in concrete, 111 pullout tests were conducted. The precise bond slip values have been gained by using the laser displacement ...In order to investigate the tensile bond anchorage properties of Australian 500N steel bars in concrete, 111 pullout tests were conducted. The precise bond slip values have been gained by using the laser displacement sensor with high resolution, including the complete bond-slip curves. How the main anchorage factors such as concrete strength, bar diameter （8, I0, 12, 16, 20, 24, 28, 32 and 36 mm） the concrete covered, embedded length and transverse reinforcement influencing the bond anchorage properties was studied under tensile condition. The process of the tensile force-slip failure for Australian 500N reinforcing steel can be divided into five stages： elastic stage, local slip stage, slip in ascent stage, slip in descent stage and remnant stage. The formula for calculating the tensile bond strength of Australian 500N reinforcing bar in concrete was proposed according to the test results, including the consistent model for tensile bond-slip relationship.展开更多
文摘The reinforcement corrosion is the pitting corrosion of chloride corrosion.Hence,in this study,the variations of reinforcement tensile strength due to stress concentration of pitting corrosion are analyzed.The stress concentration consequence of corrosion on the reinforcement tensile capacity is studied utilizing tension tests and creating different ABAQUS software models.According to the modelling in various corrosion depths,strength reduction is less than 5%in corrosion with pit radius to reinforcement diameter ratio up to 0.3 and for corrosions higher than 0.4,the measure of capacity reduction is increased more to 30%.
基金Project(DP0988940) supported by Australian Research Council Discovery Grant Program Project(2011M500930) supported by Postdoctoral Science Foundation of China+1 种基金Project(11KJB560003) supported by College Natural Science Foundation of Jiangsu Province,ChinaProject(163050072) supported by the Talent Introduction Foundation of Nanjing Forestry University,China
文摘In order to investigate the tensile bond anchorage properties of Australian 500N steel bars in concrete, 111 pullout tests were conducted. The precise bond slip values have been gained by using the laser displacement sensor with high resolution, including the complete bond-slip curves. How the main anchorage factors such as concrete strength, bar diameter （8, I0, 12, 16, 20, 24, 28, 32 and 36 mm） the concrete covered, embedded length and transverse reinforcement influencing the bond anchorage properties was studied under tensile condition. The process of the tensile force-slip failure for Australian 500N reinforcing steel can be divided into five stages： elastic stage, local slip stage, slip in ascent stage, slip in descent stage and remnant stage. The formula for calculating the tensile bond strength of Australian 500N reinforcing bar in concrete was proposed according to the test results, including the consistent model for tensile bond-slip relationship.