The fatigue behavior, indirect tensile strength （ITS） and resilient modulus test results for warm mix asphalt （WMA） as well as hot mix asphalt （HMA） at different ageing levels were evaluated. Laboratory-prepared...The fatigue behavior, indirect tensile strength （ITS） and resilient modulus test results for warm mix asphalt （WMA） as well as hot mix asphalt （HMA） at different ageing levels were evaluated. Laboratory-prepared samples were aged artificially in the oven to simulate short-term and long term ageing in accordance with AASHTO R30 and then compared with unaged specimens. Beam fatigue testing was performed using beam specimens at 25 ℃ based on AASHTO T321 standard. Fatigue life, bending stiffness and dissipated energy for both unaged and aged mixtures were calculated using four-point beam fatigue test results. Three-point bending tests were performed using semi-circular bend （SCB） specimens at -10 ℃ and the critical mode I stress intensity factor K1 was then calculated using the peak load obtained from the load-displacement curve. It is observed that Sasobit and Rheofalt warm mix asphalt additives have a significant effect on indirect tensile strength, resilient modulus, fatigue behavior and stress intensity factor of aged and unaged mixtures.展开更多
The reinforcement and stabilization of loess soil are duscussed by using fibers as the reinforcement and cement as the stabilization materials.To study the strength characteristics of loess soil reinforced by modified...The reinforcement and stabilization of loess soil are duscussed by using fibers as the reinforcement and cement as the stabilization materials.To study the strength characteristics of loess soil reinforced by modified polypropylene(MPP) fiber and cement,samples were prepared with six different fiber contents,three different cement contents,three different curing periods and three kinds of fiber length.The samples were tested under submergence and non-submergence conditions for the unconfined compressive strength(UCS),the splitting tensile strength and the compressive resilient modulus.The results indicated that combined reinforcement by PP fiber and cement could significantly improve the early strength of loess to 3.65–5.99 MPa in three days.With an increase in cement content,the specimens exhibited brittle fracture.However,the addition of fibers gradually modified the mode of fracture from brittle to ductile to plastic.The optimal dosage of fiber to reinforce loess was in the range of 0.3%–0.45% and the optimum fiber length was 12 mm,for which the unconfined compressive strength and tensile strength reached their maxima.Based on the analysis of failure properties,cement-reinforced loess specimens were susceptible to brittle damage under pressure,and the effect of modified polypropylene fiber as the connecting "bridge" could help the specimens achieve a satisfactory level of ductility when under pressure.展开更多
文摘The fatigue behavior, indirect tensile strength （ITS） and resilient modulus test results for warm mix asphalt （WMA） as well as hot mix asphalt （HMA） at different ageing levels were evaluated. Laboratory-prepared samples were aged artificially in the oven to simulate short-term and long term ageing in accordance with AASHTO R30 and then compared with unaged specimens. Beam fatigue testing was performed using beam specimens at 25 ℃ based on AASHTO T321 standard. Fatigue life, bending stiffness and dissipated energy for both unaged and aged mixtures were calculated using four-point beam fatigue test results. Three-point bending tests were performed using semi-circular bend （SCB） specimens at -10 ℃ and the critical mode I stress intensity factor K1 was then calculated using the peak load obtained from the load-displacement curve. It is observed that Sasobit and Rheofalt warm mix asphalt additives have a significant effect on indirect tensile strength, resilient modulus, fatigue behavior and stress intensity factor of aged and unaged mixtures.
基金Project(050101)supported by Horizontal Research Foundation of PLA Air Force Engineering University,ChinaProject(51478462)supported by the National Natural Science Foundation of China
文摘The reinforcement and stabilization of loess soil are duscussed by using fibers as the reinforcement and cement as the stabilization materials.To study the strength characteristics of loess soil reinforced by modified polypropylene(MPP) fiber and cement,samples were prepared with six different fiber contents,three different cement contents,three different curing periods and three kinds of fiber length.The samples were tested under submergence and non-submergence conditions for the unconfined compressive strength(UCS),the splitting tensile strength and the compressive resilient modulus.The results indicated that combined reinforcement by PP fiber and cement could significantly improve the early strength of loess to 3.65–5.99 MPa in three days.With an increase in cement content,the specimens exhibited brittle fracture.However,the addition of fibers gradually modified the mode of fracture from brittle to ductile to plastic.The optimal dosage of fiber to reinforce loess was in the range of 0.3%–0.45% and the optimum fiber length was 12 mm,for which the unconfined compressive strength and tensile strength reached their maxima.Based on the analysis of failure properties,cement-reinforced loess specimens were susceptible to brittle damage under pressure,and the effect of modified polypropylene fiber as the connecting "bridge" could help the specimens achieve a satisfactory level of ductility when under pressure.