Calcium phosphate film was prepared by electrochemical deposition technology. Subsequently, the alkaline treatment process of calcium phosphate film in 0.1 mol/L NaOH solution was monitored on real time by the piezoel...Calcium phosphate film was prepared by electrochemical deposition technology. Subsequently, the alkaline treatment process of calcium phosphate film in 0.1 mol/L NaOH solution was monitored on real time by the piezoelectric quartz crystal impedance （PQCI） technique. The variations of morphology and composition for the alkaline treatment products were characterized by scanning electron microscopy （SEM）, Fourier transform infrared （FT-IR） and X-ray diffraction （XRD）, respectively. The dynamic variations of calcium phosphate can be characterized by the change of equivalent circuit parameters. The results show that the forming process of hydroxyapatite （HA） is composed of three stages： （1） acidic calcium phosphate dissolution; （2） phase transformation; and （3） HA formation. Furthermore, the correlative kinetic equations and parameters are obtained by fitting the static capacitance （C8）-time curves.展开更多
The corrosion behavior of 907 steel under thin electrolyte layer(TEL) has been investigated by means of cathodic polarization curve measurement, electrochemical impedance spectroscopy(EIS) and scanning electron micros...The corrosion behavior of 907 steel under thin electrolyte layer(TEL) has been investigated by means of cathodic polarization curve measurement, electrochemical impedance spectroscopy(EIS) and scanning electron microscopy(SEM). The results show that the cathodic diffusion current density presents the variation trend of initial increase and subsequent decrease with the decrease of TEL thickness, and the maximum deposits at 58 μm. The cotangent-hyperbolic impedance(O) is rationally first introduced to study the diffusion process of the reactants through the corrosion products layer with many permeable holes. The initial corrosion rate of 907 steel under different TEL thickness increases with the decrease of TEL thickness except that of 104 μm,whereas the corrosion rate after long time corrosion can be ranked as 104 μm﹥402 μm﹥198 μm﹥301 μm﹥bulk solution.展开更多
The stability of ionic liquid additive 1-butyl-3-methylimidazolium hydrogen sulfate （[BMIM]HSO4） during zinc electrowinning from acidic sulfate solution was investigated by cyclic voltammetry, electrochemical impeda...The stability of ionic liquid additive 1-butyl-3-methylimidazolium hydrogen sulfate （[BMIM]HSO4） during zinc electrowinning from acidic sulfate solution was investigated by cyclic voltammetry, electrochemical impedance spectroscopy and scanning electron microscopy. Compared with the traditional industrial additives, gelatine and gum arabic, [BMIM]HSO4 has more excellent chemical and thermal stabilities. The inhibition effects of gelatine and gum arabic on the zinc electrocrystallization are observed to markedly weaken due to their part degradation after 12 h longtime successive electrolysis and high temperature （90 ℃） treatments. In contrast, the activity of [BMIM]HSO4 is practically unaffected after 24 h longtime successive electrolysis and high temperature treatments. These results are corroborated with the corresponding morphological analysis of the cathodic deposits.展开更多
Co3O4/graphite composites were synthesized by precipitation of cobalt oxalate on the surface of graphite and pyrolysis of the precipitate, and the effects of graphite content and calcination temperature on the electro...Co3O4/graphite composites were synthesized by precipitation of cobalt oxalate on the surface of graphite and pyrolysis of the precipitate, and the effects of graphite content and calcination temperature on the electrochemical properties of the composites were investigated. The samples were characterized by thermogravimetry and differential thermal analysis （TG/DTA）, X-ray diffractometry （XRD）, scanning electron microscopy （SEM）, cyclic voltammetry （CV）, electrochemical impedance spectroscopy （EIS） and charge/discharge measurements. With increasing the graphite content, the reversible capacity of the Co3O4/graphite composites decreases, while cycling stability improves dramatically, and the addition of graphite obviously decreases the average potential of lithium intercalation/deintercalation. The reversible capacity of the composites with 50% graphite rises from 583 to 725 mA-h/g as the calcination temperature increases from 300 to 500 ℃, and the Co304/graphite composites synthesized at 400 ℃ show the best cycling stability without capacity loss in the initial 20 cycles. peaks, corresponding to the lithium intercalaction/deintercalation for The CV profile of the composite presents two couples of redox graphite and Co3O4, respectively. EIS studies indicate that the electrochemical impedance decreases with increasing the graphite content.展开更多
基金Project(2005CB623901) supported by the Major State Basic Research and Development Program of China
文摘Calcium phosphate film was prepared by electrochemical deposition technology. Subsequently, the alkaline treatment process of calcium phosphate film in 0.1 mol/L NaOH solution was monitored on real time by the piezoelectric quartz crystal impedance （PQCI） technique. The variations of morphology and composition for the alkaline treatment products were characterized by scanning electron microscopy （SEM）, Fourier transform infrared （FT-IR） and X-ray diffraction （XRD）, respectively. The dynamic variations of calcium phosphate can be characterized by the change of equivalent circuit parameters. The results show that the forming process of hydroxyapatite （HA） is composed of three stages： （1） acidic calcium phosphate dissolution; （2） phase transformation; and （3） HA formation. Furthermore, the correlative kinetic equations and parameters are obtained by fitting the static capacitance （C8）-time curves.
基金Projects(21073162,21273199) supported by the National Natural Science Foundation of ChinaProject(GCTKF2012013) supported by the Science and Technology Bureau of Jiaxing Municipality and the State Key Laboratory Breeding Base of Green Chemistry-Synthesis Technology,China
文摘The corrosion behavior of 907 steel under thin electrolyte layer(TEL) has been investigated by means of cathodic polarization curve measurement, electrochemical impedance spectroscopy(EIS) and scanning electron microscopy(SEM). The results show that the cathodic diffusion current density presents the variation trend of initial increase and subsequent decrease with the decrease of TEL thickness, and the maximum deposits at 58 μm. The cotangent-hyperbolic impedance(O) is rationally first introduced to study the diffusion process of the reactants through the corrosion products layer with many permeable holes. The initial corrosion rate of 907 steel under different TEL thickness increases with the decrease of TEL thickness except that of 104 μm,whereas the corrosion rate after long time corrosion can be ranked as 104 μm﹥402 μm﹥198 μm﹥301 μm﹥bulk solution.
基金Project(2011FA009) supported by the Natural Science Foundation of Yunnan Province,ChinaProject(2011FZ020) supported by the Application Foundation Research of Yunnan Province,China
文摘The stability of ionic liquid additive 1-butyl-3-methylimidazolium hydrogen sulfate （[BMIM]HSO4） during zinc electrowinning from acidic sulfate solution was investigated by cyclic voltammetry, electrochemical impedance spectroscopy and scanning electron microscopy. Compared with the traditional industrial additives, gelatine and gum arabic, [BMIM]HSO4 has more excellent chemical and thermal stabilities. The inhibition effects of gelatine and gum arabic on the zinc electrocrystallization are observed to markedly weaken due to their part degradation after 12 h longtime successive electrolysis and high temperature （90 ℃） treatments. In contrast, the activity of [BMIM]HSO4 is practically unaffected after 24 h longtime successive electrolysis and high temperature treatments. These results are corroborated with the corresponding morphological analysis of the cathodic deposits.
基金Project(2007CB613607) supported by the National Basic Research Program of China Projects(2009FJ1002, 2009CK3062) supported by the Science and Technology Program of Hunan Province, China
文摘Co3O4/graphite composites were synthesized by precipitation of cobalt oxalate on the surface of graphite and pyrolysis of the precipitate, and the effects of graphite content and calcination temperature on the electrochemical properties of the composites were investigated. The samples were characterized by thermogravimetry and differential thermal analysis （TG/DTA）, X-ray diffractometry （XRD）, scanning electron microscopy （SEM）, cyclic voltammetry （CV）, electrochemical impedance spectroscopy （EIS） and charge/discharge measurements. With increasing the graphite content, the reversible capacity of the Co3O4/graphite composites decreases, while cycling stability improves dramatically, and the addition of graphite obviously decreases the average potential of lithium intercalation/deintercalation. The reversible capacity of the composites with 50% graphite rises from 583 to 725 mA-h/g as the calcination temperature increases from 300 to 500 ℃, and the Co304/graphite composites synthesized at 400 ℃ show the best cycling stability without capacity loss in the initial 20 cycles. peaks, corresponding to the lithium intercalaction/deintercalation for The CV profile of the composite presents two couples of redox graphite and Co3O4, respectively. EIS studies indicate that the electrochemical impedance decreases with increasing the graphite content.