One of the key problems by diffusion-rolling bonding with small reduction for carbon steel plates is the bonding assistant coat. Abonding assitant coat used below 850℃ was developed. It contained copper as basic elem...One of the key problems by diffusion-rolling bonding with small reduction for carbon steel plates is the bonding assistant coat. Abonding assitant coat used below 850℃ was developed. It contained copper as basic element and zinc as main alloy element. Other small elements and rear metals were added to decrease the melting point and to obtain a better clouding and bigh plasticity. Based on the theory of brazing and transient liquid diffusion welding, two carbon steel plates were rolled with small reduction by using self-made bonding assistant coat. Temperature, pressure and holding time are the main technology parameters for controlling the process of diffusion-rolling. The results show that the bonding strength is the greatest when the bonding temperature is 830℃, holding time is 3 min and the reduction rate is 9%.展开更多
文摘One of the key problems by diffusion-rolling bonding with small reduction for carbon steel plates is the bonding assistant coat. Abonding assitant coat used below 850℃ was developed. It contained copper as basic element and zinc as main alloy element. Other small elements and rear metals were added to decrease the melting point and to obtain a better clouding and bigh plasticity. Based on the theory of brazing and transient liquid diffusion welding, two carbon steel plates were rolled with small reduction by using self-made bonding assistant coat. Temperature, pressure and holding time are the main technology parameters for controlling the process of diffusion-rolling. The results show that the bonding strength is the greatest when the bonding temperature is 830℃, holding time is 3 min and the reduction rate is 9%.