The surface morphology of alloy layer of tinplate was studied by means of scanning electron microscopy. By using the layer on layer debonding technology of glow discharge spectrum, the contents of C and O at the bound...The surface morphology of alloy layer of tinplate was studied by means of scanning electron microscopy. By using the layer on layer debonding technology of glow discharge spectrum, the contents of C and O at the boundary of alloy layer and black plate were analyzed. And the corrosion characteristic of cavity of tinplate alloy layer was studied on-line and in-situ by means of electrochemical atomic force microscope. The corrosion depth of cavity of alloy layer in-situ after different corrosion time was measured. The results show that the cavity of alloy layer is a critical factor causing rapid decline of corrosion resistance of tinplate, and the formation of cavity of alloy layer is due to incorrect pretreatment of black plate before electrotinning. The cavity of alloy layer is the internal factor causing pitting corrosion of tinplate when the tinplate is applied to food packaging material. And the dynamic equation of pitting corrosion generated in the cavity of alloy layer conforms to logarithm law.展开更多
文摘The surface morphology of alloy layer of tinplate was studied by means of scanning electron microscopy. By using the layer on layer debonding technology of glow discharge spectrum, the contents of C and O at the boundary of alloy layer and black plate were analyzed. And the corrosion characteristic of cavity of tinplate alloy layer was studied on-line and in-situ by means of electrochemical atomic force microscope. The corrosion depth of cavity of alloy layer in-situ after different corrosion time was measured. The results show that the cavity of alloy layer is a critical factor causing rapid decline of corrosion resistance of tinplate, and the formation of cavity of alloy layer is due to incorrect pretreatment of black plate before electrotinning. The cavity of alloy layer is the internal factor causing pitting corrosion of tinplate when the tinplate is applied to food packaging material. And the dynamic equation of pitting corrosion generated in the cavity of alloy layer conforms to logarithm law.