Traditional manufacturing processes for lightweight curved profiles are often associated with lengthy procedures,high costs,low efficiency,and high energy consumption.In order to solve this problem,a new staggered ext...Traditional manufacturing processes for lightweight curved profiles are often associated with lengthy procedures,high costs,low efficiency,and high energy consumption.In order to solve this problem,a new staggered extrusion(SE)process was used to form the curved profile of AZ31 magnesium alloy in this paper.The study investigates the mapping relationship between the curvature,microstructure,and mechanical properties of the formed profiles by using different eccentricities of the die.Scanning electron microscopy(SEM)and electron backscatter diffraction techniques are employed to examine the effects of different eccentricity values(e)on grain morphology,recrystallization mechanisms,texture,and Schmid factors of the products.The results demonstrate that the staggered extrusion method promotes the deep refinement of grain size in the extruded products,with an average grain size of only 15%of the original billet,reaching 12.28μm.The tensile strength and elongation of the curved profiles after extrusion under the eccentricity value of 10 mm,20 mm and 30 mm are significantly higher than those of the billet,with the tensile strength is increased to 250,270,235 MPa,and the engineering strain elongation increased to 10.5%,12.1%,15.9%.This indicates that staggered extrusion enables curvature control of the profiles while improving their strength.展开更多
High-entropy alloy composites(HEACs)have attracted significant attention due to their exceptional mechanical properties and chemical stability.By adjusting the content of reinforcing particles in the high-entropy allo...High-entropy alloy composites(HEACs)have attracted significant attention due to their exceptional mechanical properties and chemical stability.By adjusting the content of reinforcing particles in the high-entropy alloy and by employing advanced additive manufacturing techniques,high-performance HEACs can be fabricated.However,there is still considerable room for improvement in their performance.In this study,CoCrFeMnNi HEA powders were used as the matrix,and NiCoFeAlTi high-entropy intermetallic powders were used as the high-entropy reinforcement(HER).CoCrFeMnNi/NiCoFeAlTi HEACs were fabricated using selective laser melting technology.The study results indicate that after aging,the microstructure of HEACs with HER exhibits Al-and Ti-rich nano-oxide precipitates with an orthorhombic CMCM type structure system.After aging at 873 K for 2 h,HEACs with HER achieved excellent overall mechanical properties,with an ultimate tensile strength of 731 MPa.This is attributed to the combined and synergistic effects of precipitation strengthening,dislocation strengthening,and the high lattice distortion caused by high intragranular defects,which provide a multi-scale strengthening and hardening mechanism for the plastic deformation of HEACs with HER.This study demonstrates that aging plays a crucial role in controlling the precipitate phases in complex multi-element alloys.展开更多
Wire-arc additive manufacture(WAAM)has great potential for manufacturing of Al-Cu components.However,inferior mechanical properties of WAAM deposited material restrict its industrial application.Inter-layer cold rolli...Wire-arc additive manufacture(WAAM)has great potential for manufacturing of Al-Cu components.However,inferior mechanical properties of WAAM deposited material restrict its industrial application.Inter-layer cold rolling and thermo-mechanical heat treatment(T8)with pre-stretching deformation between solution and aging treatment were adopted in this study.Their effects on hardness,mechanical properties and microstructure were analyzed and compared to the conventional heat treatment(T6).The results show that cold rolling increases the hardness and strengths,which further increase with T8 treatment.The ultimate tensile strength(UTS)of 513 MPa and yield stress(YS)of 413 MPa can be obtained in the inter-layer cold-rolled sample with T8 treatment,which is much higher than that in the as-deposited samples.The cold-rolled samples show higher elongation than that of as-deposited ones due to significant elimination of porosity in cold rolling;while both the T6 and T8 treatments decrease the elongation.The cold rolling and pre-stretching deformation both contribute to the formation of dense and dispersive precipitatedθ′phases,which inhibits the dislocation movement and enhances the strengths;as a result,T8 treatment shows better strengthening effect than the T6 treatment.The strengthening mechanism was analyzed and it was mainly related to work hardening and precipitation strengthening.展开更多
In this work,a novel type of short-process deformation technology of Mg alloys,bifurcation-equal channel angular pressing(B-ECAP),was proposed to refine grain and improve the basal texture.The cylindrical billets were...In this work,a novel type of short-process deformation technology of Mg alloys,bifurcation-equal channel angular pressing(B-ECAP),was proposed to refine grain and improve the basal texture.The cylindrical billets were first compressed into the die cavity,then sequentially flowed downward through a 90°corner and two 120°shear steps.The total strain of B-ECAP process could reach 3.924 in a single pass.The results of microstructure observation showed that DRX occurred at upsetting process in the die cavity and completed at position D.The grains were refined to 6.3μm at being extruded at 300℃ and grew obviously with the extrusion temperature increase.The shear tress induced by 900 corner and two 120°shear steps resulted in the basal poles of most grains tilted to extrusion direction(ED)by±25°.Compared with the original billets,the extruded sheets exhibited higher yield strengths(YS),which was mainly attributed to the grain refinement.The higher Schmid factor caused by ED-tilt texture resulted in a fracture elongation(FE)more than that of the original bar in ED,while was equivalent to that in transverse direction(TD).As the extrusion temperature increased,the variation of UTS and YS in ED and TD decreased gradually without ductility obviously decrease.展开更多
Mg–8Li–3Al–0.7Si alloy was prepared by casting and deformed by hot extrusion in this study.And the microstructure of as-cast and extruded specimens was analyzed with OM,XRD,SEM and EDS.Results show that the specime...Mg–8Li–3Al–0.7Si alloy was prepared by casting and deformed by hot extrusion in this study.And the microstructure of as-cast and extruded specimens was analyzed with OM,XRD,SEM and EDS.Results show that the specimens are composed ofα-Mg,β-Li,AlLi,MgLiAl2 and Mg2Si phases.In as-extruded specimen,the microstructure is refined and theβ-Li phase has the effect of coordination during deformation.After hot extrusion,Chinese script Mg2Si phase is crushed into block-like and distributes uniformly in the matrix.Mechanical properties results show that the strength and elongation are both improved after hot extrusion.展开更多
As the next generation biomedical titanium alloy, β-type titanium alloys are excellent candidates for biomedical applications due to the relative low elastic modulus and the contained non-toxic elements. However, the...As the next generation biomedical titanium alloy, β-type titanium alloys are excellent candidates for biomedical applications due to the relative low elastic modulus and the contained non-toxic elements. However, the relative low strength and unsatisfactory tribological property are undesired for load-bearing implant applications. In this study, 0-5 at% Si was added to the classic Ti-35Nb-5Ta-7Zr alloy to improve its strength and wear resistance, and the(Ti-35Nb-5Ta-7Zr)1-x-Six(x=0, 1 at% and 5 at%) alloy were fabricated by selective electron beam melting(SEBM)technology. The results indicated that Si addition significantly increases in compressive yield strength, which is mainly due to grain refinement strengthening. At the same time, the wear rate of the as-built TNTZ-5Si alloy in SBF solution was only ~30% of the Ti-6Al-4V alloy. Consequently, the TNTZ-5Si alloy showed an excellent combination of compressive yield strength, elastic modulus and wear resistance for potential load-bearing implant applications.展开更多
In this paper, 3 mm 6061 aluminum alloy sheets were welded by laser MIG hybrid welding. Based on the experiment, the best welding parameters were determined to ensure the penetration welding. The detailed microstructu...In this paper, 3 mm 6061 aluminum alloy sheets were welded by laser MIG hybrid welding. Based on the experiment, the best welding parameters were determined to ensure the penetration welding. The detailed microstructure,tensile and fatigue fracture morphology and surface fatigue damage of the welded joints were analyzed by optical microscope(OM), scanning electron microscope(SEM) and energy dispersive spectrometer(EDS). The results show that there are two main kinds of precipitates, one is the long Si rich precipitates at the grain boundaries, the other is the intragranular Cu rich precipitates. The tensile test results show that the tensile strength of the joint is 224 MPa, which is only 70.2% of the base metal. Through the analysis of tensile fracture, there are great differences in the formation of tensile dimple. In the tensile-tensile fatigue test with a stress rate of 0.1, the conditional fatigue limits of base metal and welded joint are 101.9 MPa and 54.4 MPa, respectively. By comparing the fatigue fracture of the welded joints under different stress amplitudes, it was found that the main factor leading to the fracture of the joint is porosity. Through further analysis of the pore defects, it was found that there are transgranular and intergranular propagation ways of microcracks in the pores, and the mixed propagation way was also found.展开更多
Ti185 alloy is widely used in key industrial fields such as aerospace due to its excellent mechanical properties.The traditional method of preparing Ti185 alloy will inevitably appear“βfleck”,resulting in the decre...Ti185 alloy is widely used in key industrial fields such as aerospace due to its excellent mechanical properties.The traditional method of preparing Ti185 alloy will inevitably appear“βfleck”,resulting in the decrease of mechanical properties,and the high price of V element limits the wide application of Ti185.In this paper,a low-cost master alloy V-Fe powder is used,a dense block is prepared by spark plasma sintering(SPS)technology,and a high-performance Ti185 alloy is prepared by controlling the sintering parameters.XRD and SEM were used to investigate the phase and microstructure of the samples prepared under different parameters.The compressive strength and friction properties of the directly prepared samples were studied.The samples with a sintering temperature of 1350 ℃ and a holding time of 30 min exhibited the most excellent comprehensive performance,with the highest compressive strength and lowest friction coefficient of 1931.59 MPa and 0.47,respectively.展开更多
In this study,nano-graphene reinforced titanium matrix composites(GNPs/Ti)with a honeycomb porous structure were fabricated by selective laser melting(SLM).The effects of graphene on the microstructure,mechanical prop...In this study,nano-graphene reinforced titanium matrix composites(GNPs/Ti)with a honeycomb porous structure were fabricated by selective laser melting(SLM).The effects of graphene on the microstructure,mechanical properties and corrosion performance of the SLM GNPs/Ti were systematically investigated.Results of microstructure characterization show that:1)the density of the SLM GNPs/Ti was improved as compared to that of the SLM Ti;2)abundant TiC particles were formed in the SLM GNPs/Ti.The hardness and compressive strength of the composite increased by 90%(from HV 236 to HV 503)and 14%(from 277 MPa to 316 MPa),respectively,attributed to the uniformly distributed TiC and fine GNPs in the Ti matrix.Electrochemical tests reveal that the corrosion current density of the SLM GNPs/Ti is only 0.328μA/cm^(2),that is about 25%less than that of the SLM Ti.The results indicate that the incorporation of nano-graphene is a potential method to strengthen the Ti by SLM.展开更多
In this work, laser heat conduction lap welding(LHCLW) of AZ31B magnesium alloy sheet and DP780galvanized steel sheet was carried out by the defocused laser beam. The effects of laser power on the microstructure and m...In this work, laser heat conduction lap welding(LHCLW) of AZ31B magnesium alloy sheet and DP780galvanized steel sheet was carried out by the defocused laser beam. The effects of laser power on the microstructure and mechanical properties of the joint were studied. The pros and cons of the joint were identified and evaluated by measuring the tensile shear strength, microhardness and microstructure observation. The formation mechanism of various phases at the Mg/steel interface was analyzed. The results indicated that the galvanized layer could promote the metallurgical bonding between magnesium alloy and steel by improving the diffusion ability of molten magnesium alloy at the steel interface and reacting with Mg, so as to enhance the strength of the joint. A continuous dense layered eutectic structure(α-Mg+MgZn) was formed at the interface of the joint, while MgZn_(2)and MgZn phase was formed at the weld edge zone and heat affective zone(HAZ), whereas no reaction layer was generated between the uncoated steel and magnesium alloy. A sound joint could be obtained at 2.5 kW, and the corresponding tensile shear strength reached the maximum value of 42.9 N/mm. The strength was slightly reduced at 2.6 kW due to the existence of microcracks in the eutectic reaction layer.展开更多
Effects of interrupted ageing(T6I6) and asymmetric rolling on microstructures, mechanical properties, and intergranular corrosion(IGC) behaviors of Al-Mg-Si-Zn alloy were investigated. Results showed that the T6 alloy...Effects of interrupted ageing(T6I6) and asymmetric rolling on microstructures, mechanical properties, and intergranular corrosion(IGC) behaviors of Al-Mg-Si-Zn alloy were investigated. Results showed that the T6 alloy has the lowest strength and the worst IGC resistance, while the T6I6 alloy has higher strength and better IGC resistance.What’ s more, the alloy treated by pre-rolling deformation has higher strength and better IGC resistance;and the alloy treated by the pre-asymmetry rolling achieves the highest strength, the best IGC resistance and lower elongation. The mechanical properties depend on microstructures such as the grain size, texture, dislocation density and precipitation, the grain boundary misorientation and grain boundary microstructure are responsible for the IGC resistance.展开更多
The influence of different ageing processes on the microstructure, corrosion behaviors and mechanical properties of extruded Al-5.6Zn-1.6Mg-0.05Zr(wt.%) alloy was studied in this work. The changes of morphology, size ...The influence of different ageing processes on the microstructure, corrosion behaviors and mechanical properties of extruded Al-5.6Zn-1.6Mg-0.05Zr(wt.%) alloy was studied in this work. The changes of morphology, size and distribution of MgZn_(2)precipitate with ageing temperature and time were revealed by optical and electron microscopy. Intergranular corrosion(IGC) and exfoliation corrosion(EXCO) tests were carried out to assess the changes in corrosion susceptibility of the tempered alloy, and some white spots on the surface of the sample aged for longer time were found to be precursors of pits. Electrochemical cyclic polarization test depicted the corrosion behavior under different tempers. Ageing influences on the mechanical behaviors of the alloy were revealed by evaluating its microhardness and tensile strength. The microscopic features of the strengthening phases determined by the ageing procedure directly affect the corrosion resistance and mechanical properties of the alloy.展开更多
The influences of hot stamping parameters such as heating temperature,soaking time,deformation temperature and cooling medium on the phase transformation,microstructure and mechanical properties of 30MnB5 and 22MnB5 a...The influences of hot stamping parameters such as heating temperature,soaking time,deformation temperature and cooling medium on the phase transformation,microstructure and mechanical properties of 30MnB5 and 22MnB5 are investigated and analyzed in this work.The quenching experiment,tensile testing,hardness measurement and microstructure observation were conducted to obtain the mechanical and microstructural data.The results indicate that 30MnB5 possesses a higher tensile strength but a lower elongation than 22MnB5,if hot stamped at the same process parameter.The tensile strength and hardness of the hot stamped specimens decrease under inappropriate heating conditions for two reasons,insufficient austenitization or coarse austenite grains.The austenitic forming rate of 30MnB5 is higher than that of 22MnB5,because more cementite leads to higher nucleation rate and diffusion coefficient of carbon atom.More amount of fine martensite forms under the higher deformation temperature or the quicker cooling rate.展开更多
The effect of Li(2.0 wt%)addition on mechanical properties and ageing precipitation behavior of Al-3.0 Mg 0.5 Si was investigated by tensile test,dynamic elasticity modulus test,scanning electron microscopy(SEM),trans...The effect of Li(2.0 wt%)addition on mechanical properties and ageing precipitation behavior of Al-3.0 Mg 0.5 Si was investigated by tensile test,dynamic elasticity modulus test,scanning electron microscopy(SEM),transmission electron microscopy(TEM)and high-resolution transmission electron microscopy(HRTEM)images.The results show that the tensile strength of the Li-containing alloy can be significantly improved;however,the ductility is sharply decreased and the fracture mechanism changes from ductile fracture to intergranular fracture.The elasticity modulus of the Li-containing alloy increases by 11.6%compared with the base alloy.The microstructure observation shows that the Li addition can absolutely change the precipitation behavior of the base alloy,andδ′-Al_(3)Li phase becomes the main precipitates.Besides,β′′-Mg_(2)Si andδ′-Al_(3)Li dual phases precipitation can be visibly observed at 170℃ ageing for 100 h,although the quantity ofδ′-Al_(3)Li phase is more thanβ′′-Mg_(2)Si phase.The width of the precipitate-free zone(PFZ)of the Li-containing alloy is much wider at the over-ageing state than the base alloy,which has a negative impact on the ductile and results in the decrease of elongation.展开更多
The effect of temperature in range of 155-175 ℃ on the creep behavior, microstructural evolution, and precipitation of an Al-Cu-Li alloy was experimentally investigated during creep ageing deformation under 180 MPa f...The effect of temperature in range of 155-175 ℃ on the creep behavior, microstructural evolution, and precipitation of an Al-Cu-Li alloy was experimentally investigated during creep ageing deformation under 180 MPa for 20 h. Increasing temperature resulted in a noteworthy change in creep ageing behaviour, including a variation in creep curves, an improvement in creep rate during early creep ageing, and an increased creep strain. Tensile tests indicate that the specimen aged at higher temperature reached peak strength within a shorter time. Transmission electron microscopy(TEM) was employed to explore the effect of temperature on the microstructural evolution of the AA2198 during creep ageing deformation. Many larger dislocations and even tangled dislocation structures were observed in the sample aged at higher temperature. The number of T1 precipitates increased at higher ageing temperature at the same ageing time. Based on the analysed results, a new mechanism, considering the combined effects of the formation of larger dislocation structures induced by higher temperature and diffusion of solute atoms towards these larger or tangled dislocations, was proposed to explain the effect of temperature on microstructural evolution and creep behaviour.展开更多
基金Project(JQ2022E004)supported by the Natural Science Foundation of Heilongjiang Province,China。
文摘Traditional manufacturing processes for lightweight curved profiles are often associated with lengthy procedures,high costs,low efficiency,and high energy consumption.In order to solve this problem,a new staggered extrusion(SE)process was used to form the curved profile of AZ31 magnesium alloy in this paper.The study investigates the mapping relationship between the curvature,microstructure,and mechanical properties of the formed profiles by using different eccentricities of the die.Scanning electron microscopy(SEM)and electron backscatter diffraction techniques are employed to examine the effects of different eccentricity values(e)on grain morphology,recrystallization mechanisms,texture,and Schmid factors of the products.The results demonstrate that the staggered extrusion method promotes the deep refinement of grain size in the extruded products,with an average grain size of only 15%of the original billet,reaching 12.28μm.The tensile strength and elongation of the curved profiles after extrusion under the eccentricity value of 10 mm,20 mm and 30 mm are significantly higher than those of the billet,with the tensile strength is increased to 250,270,235 MPa,and the engineering strain elongation increased to 10.5%,12.1%,15.9%.This indicates that staggered extrusion enables curvature control of the profiles while improving their strength.
基金Project supported by ClassⅢPeak Discipline of Shanghai-Materials Science and Engineering(High-Energy Beam Intelligent Processing and Green Manufacturing),China。
文摘High-entropy alloy composites(HEACs)have attracted significant attention due to their exceptional mechanical properties and chemical stability.By adjusting the content of reinforcing particles in the high-entropy alloy and by employing advanced additive manufacturing techniques,high-performance HEACs can be fabricated.However,there is still considerable room for improvement in their performance.In this study,CoCrFeMnNi HEA powders were used as the matrix,and NiCoFeAlTi high-entropy intermetallic powders were used as the high-entropy reinforcement(HER).CoCrFeMnNi/NiCoFeAlTi HEACs were fabricated using selective laser melting technology.The study results indicate that after aging,the microstructure of HEACs with HER exhibits Al-and Ti-rich nano-oxide precipitates with an orthorhombic CMCM type structure system.After aging at 873 K for 2 h,HEACs with HER achieved excellent overall mechanical properties,with an ultimate tensile strength of 731 MPa.This is attributed to the combined and synergistic effects of precipitation strengthening,dislocation strengthening,and the high lattice distortion caused by high intragranular defects,which provide a multi-scale strengthening and hardening mechanism for the plastic deformation of HEACs with HER.This study demonstrates that aging plays a crucial role in controlling the precipitate phases in complex multi-element alloys.
基金Project(ZZYJKT2024-08)supported by the State Key Laboratory of Precision Manufacturing for Extreme Service Performance,ChinaProject(2022JB11GX004)supported by Selection of the best Candidates to Undertake Key Research Projects by Dalian City,ChinaProject(201806835007)supported by China Scholarship Council。
文摘Wire-arc additive manufacture(WAAM)has great potential for manufacturing of Al-Cu components.However,inferior mechanical properties of WAAM deposited material restrict its industrial application.Inter-layer cold rolling and thermo-mechanical heat treatment(T8)with pre-stretching deformation between solution and aging treatment were adopted in this study.Their effects on hardness,mechanical properties and microstructure were analyzed and compared to the conventional heat treatment(T6).The results show that cold rolling increases the hardness and strengths,which further increase with T8 treatment.The ultimate tensile strength(UTS)of 513 MPa and yield stress(YS)of 413 MPa can be obtained in the inter-layer cold-rolled sample with T8 treatment,which is much higher than that in the as-deposited samples.The cold-rolled samples show higher elongation than that of as-deposited ones due to significant elimination of porosity in cold rolling;while both the T6 and T8 treatments decrease the elongation.The cold rolling and pre-stretching deformation both contribute to the formation of dense and dispersive precipitatedθ′phases,which inhibits the dislocation movement and enhances the strengths;as a result,T8 treatment shows better strengthening effect than the T6 treatment.The strengthening mechanism was analyzed and it was mainly related to work hardening and precipitation strengthening.
基金Projects(52274397,52275382)supported by the National Natural Science Foundation of ChinaProject(tsqn202211115)supported by the Taishan Scholars Program of Shandong Province,China+2 种基金Project supported by the Yantai High-end Talent Introduction“Double Hundred Plan”(2021),ChinaProject(ZR2024JQ020)supported by the Shandong Provincial Natural Science Foundation of ChinaProjects(CZ20210034,CM20223013)supported by the Changzhou Sci&Tech Program,China。
文摘In this work,a novel type of short-process deformation technology of Mg alloys,bifurcation-equal channel angular pressing(B-ECAP),was proposed to refine grain and improve the basal texture.The cylindrical billets were first compressed into the die cavity,then sequentially flowed downward through a 90°corner and two 120°shear steps.The total strain of B-ECAP process could reach 3.924 in a single pass.The results of microstructure observation showed that DRX occurred at upsetting process in the die cavity and completed at position D.The grains were refined to 6.3μm at being extruded at 300℃ and grew obviously with the extrusion temperature increase.The shear tress induced by 900 corner and two 120°shear steps resulted in the basal poles of most grains tilted to extrusion direction(ED)by±25°.Compared with the original billets,the extruded sheets exhibited higher yield strengths(YS),which was mainly attributed to the grain refinement.The higher Schmid factor caused by ED-tilt texture resulted in a fracture elongation(FE)more than that of the original bar in ED,while was equivalent to that in transverse direction(TD).As the extrusion temperature increased,the variation of UTS and YS in ED and TD decreased gradually without ductility obviously decrease.
基金Project(51601024)supported by the National Natural Science Foundation,ChinaProjects(2016YFB0700403,2016YFB0301100)supported by the National Key Research and Development Program of China+1 种基金Project(cstc2016jcyj A0418)supported by the Chongqing Research Program of Basic Research and Frontier Technology,ChinaProject(106112016CDJXZ138811)supported by the Fundamental Research Funds for the Central Universities,China
文摘Mg–8Li–3Al–0.7Si alloy was prepared by casting and deformed by hot extrusion in this study.And the microstructure of as-cast and extruded specimens was analyzed with OM,XRD,SEM and EDS.Results show that the specimens are composed ofα-Mg,β-Li,AlLi,MgLiAl2 and Mg2Si phases.In as-extruded specimen,the microstructure is refined and theβ-Li phase has the effect of coordination during deformation.After hot extrusion,Chinese script Mg2Si phase is crushed into block-like and distributes uniformly in the matrix.Mechanical properties results show that the strength and elongation are both improved after hot extrusion.
基金Project(2019zdzx-04-03) supported by the Science&Technology Specific Projects of Shaanxi Province,ChinaProject(2021KJXX-75) supported by the Innovation Capability Support Plan of Shaanxi Province,China。
文摘As the next generation biomedical titanium alloy, β-type titanium alloys are excellent candidates for biomedical applications due to the relative low elastic modulus and the contained non-toxic elements. However, the relative low strength and unsatisfactory tribological property are undesired for load-bearing implant applications. In this study, 0-5 at% Si was added to the classic Ti-35Nb-5Ta-7Zr alloy to improve its strength and wear resistance, and the(Ti-35Nb-5Ta-7Zr)1-x-Six(x=0, 1 at% and 5 at%) alloy were fabricated by selective electron beam melting(SEBM)technology. The results indicated that Si addition significantly increases in compressive yield strength, which is mainly due to grain refinement strengthening. At the same time, the wear rate of the as-built TNTZ-5Si alloy in SBF solution was only ~30% of the Ti-6Al-4V alloy. Consequently, the TNTZ-5Si alloy showed an excellent combination of compressive yield strength, elastic modulus and wear resistance for potential load-bearing implant applications.
基金Project(51971129) supported by the National Natural Science Foundation of ChinaProject(19ZR1421200) supported by the Shanghai Natural Science Foundation,China。
文摘In this paper, 3 mm 6061 aluminum alloy sheets were welded by laser MIG hybrid welding. Based on the experiment, the best welding parameters were determined to ensure the penetration welding. The detailed microstructure,tensile and fatigue fracture morphology and surface fatigue damage of the welded joints were analyzed by optical microscope(OM), scanning electron microscope(SEM) and energy dispersive spectrometer(EDS). The results show that there are two main kinds of precipitates, one is the long Si rich precipitates at the grain boundaries, the other is the intragranular Cu rich precipitates. The tensile test results show that the tensile strength of the joint is 224 MPa, which is only 70.2% of the base metal. Through the analysis of tensile fracture, there are great differences in the formation of tensile dimple. In the tensile-tensile fatigue test with a stress rate of 0.1, the conditional fatigue limits of base metal and welded joint are 101.9 MPa and 54.4 MPa, respectively. By comparing the fatigue fracture of the welded joints under different stress amplitudes, it was found that the main factor leading to the fracture of the joint is porosity. Through further analysis of the pore defects, it was found that there are transgranular and intergranular propagation ways of microcracks in the pores, and the mixed propagation way was also found.
基金Projects(51671152,51874225)supported by the National Natural Science Foundation of ChinaProject(2020ZDLGY13-10)supported by Shaanxi Provincial Science and Technology,China。
文摘Ti185 alloy is widely used in key industrial fields such as aerospace due to its excellent mechanical properties.The traditional method of preparing Ti185 alloy will inevitably appear“βfleck”,resulting in the decrease of mechanical properties,and the high price of V element limits the wide application of Ti185.In this paper,a low-cost master alloy V-Fe powder is used,a dense block is prepared by spark plasma sintering(SPS)technology,and a high-performance Ti185 alloy is prepared by controlling the sintering parameters.XRD and SEM were used to investigate the phase and microstructure of the samples prepared under different parameters.The compressive strength and friction properties of the directly prepared samples were studied.The samples with a sintering temperature of 1350 ℃ and a holding time of 30 min exhibited the most excellent comprehensive performance,with the highest compressive strength and lowest friction coefficient of 1931.59 MPa and 0.47,respectively.
基金Projects(51504191,51671152,51874225)supported by the National Natural Science Foundation of ChinaProject(2019GY-188)supported by the Key R&D Projects of Shaanxi,China+2 种基金Project(18JC019)supported by the Industrialization Project of Shaanxi Education Department,ChinaProject(PMMSLKL-901)supported by the State Key Laboratory of Metal Porous Materials,ChinaProject(2020ZDLGY13-10)supported by the Science&Technology Project of Shaanxi,China。
文摘In this study,nano-graphene reinforced titanium matrix composites(GNPs/Ti)with a honeycomb porous structure were fabricated by selective laser melting(SLM).The effects of graphene on the microstructure,mechanical properties and corrosion performance of the SLM GNPs/Ti were systematically investigated.Results of microstructure characterization show that:1)the density of the SLM GNPs/Ti was improved as compared to that of the SLM Ti;2)abundant TiC particles were formed in the SLM GNPs/Ti.The hardness and compressive strength of the composite increased by 90%(from HV 236 to HV 503)and 14%(from 277 MPa to 316 MPa),respectively,attributed to the uniformly distributed TiC and fine GNPs in the Ti matrix.Electrochemical tests reveal that the corrosion current density of the SLM GNPs/Ti is only 0.328μA/cm^(2),that is about 25%less than that of the SLM Ti.The results indicate that the incorporation of nano-graphene is a potential method to strengthen the Ti by SLM.
基金Projects(51705219, 51905227) supported by the National Natural Science Foundation of ChinaProject(BK20200915) supported by the Natural Science Foundation of Jiangsu Province,ChinaProject(19KJB460013) supported by the General University Science Research Project of Jiangsu Province,China。
文摘In this work, laser heat conduction lap welding(LHCLW) of AZ31B magnesium alloy sheet and DP780galvanized steel sheet was carried out by the defocused laser beam. The effects of laser power on the microstructure and mechanical properties of the joint were studied. The pros and cons of the joint were identified and evaluated by measuring the tensile shear strength, microhardness and microstructure observation. The formation mechanism of various phases at the Mg/steel interface was analyzed. The results indicated that the galvanized layer could promote the metallurgical bonding between magnesium alloy and steel by improving the diffusion ability of molten magnesium alloy at the steel interface and reacting with Mg, so as to enhance the strength of the joint. A continuous dense layered eutectic structure(α-Mg+MgZn) was formed at the interface of the joint, while MgZn_(2)and MgZn phase was formed at the weld edge zone and heat affective zone(HAZ), whereas no reaction layer was generated between the uncoated steel and magnesium alloy. A sound joint could be obtained at 2.5 kW, and the corresponding tensile shear strength reached the maximum value of 42.9 N/mm. The strength was slightly reduced at 2.6 kW due to the existence of microcracks in the eutectic reaction layer.
基金Project(TC190H3ZV/2) supported by the National Building Project of Application Demonstration Platform on New Materials Products,China。
文摘Effects of interrupted ageing(T6I6) and asymmetric rolling on microstructures, mechanical properties, and intergranular corrosion(IGC) behaviors of Al-Mg-Si-Zn alloy were investigated. Results showed that the T6 alloy has the lowest strength and the worst IGC resistance, while the T6I6 alloy has higher strength and better IGC resistance.What’ s more, the alloy treated by pre-rolling deformation has higher strength and better IGC resistance;and the alloy treated by the pre-asymmetry rolling achieves the highest strength, the best IGC resistance and lower elongation. The mechanical properties depend on microstructures such as the grain size, texture, dislocation density and precipitation, the grain boundary misorientation and grain boundary microstructure are responsible for the IGC resistance.
基金Project(2021zzts0152) supported by the Fundamental Research Funds for the Central Universities,ChinaProject(U1837207) supported by the National Natural Science Foundation of China。
文摘The influence of different ageing processes on the microstructure, corrosion behaviors and mechanical properties of extruded Al-5.6Zn-1.6Mg-0.05Zr(wt.%) alloy was studied in this work. The changes of morphology, size and distribution of MgZn_(2)precipitate with ageing temperature and time were revealed by optical and electron microscopy. Intergranular corrosion(IGC) and exfoliation corrosion(EXCO) tests were carried out to assess the changes in corrosion susceptibility of the tempered alloy, and some white spots on the surface of the sample aged for longer time were found to be precursors of pits. Electrochemical cyclic polarization test depicted the corrosion behavior under different tempers. Ageing influences on the mechanical behaviors of the alloy were revealed by evaluating its microhardness and tensile strength. The microscopic features of the strengthening phases determined by the ageing procedure directly affect the corrosion resistance and mechanical properties of the alloy.
基金Projects(51705018,U1564202)supported by the National Natural Science Foundation of China
文摘The influences of hot stamping parameters such as heating temperature,soaking time,deformation temperature and cooling medium on the phase transformation,microstructure and mechanical properties of 30MnB5 and 22MnB5 are investigated and analyzed in this work.The quenching experiment,tensile testing,hardness measurement and microstructure observation were conducted to obtain the mechanical and microstructural data.The results indicate that 30MnB5 possesses a higher tensile strength but a lower elongation than 22MnB5,if hot stamped at the same process parameter.The tensile strength and hardness of the hot stamped specimens decrease under inappropriate heating conditions for two reasons,insufficient austenitization or coarse austenite grains.The austenitic forming rate of 30MnB5 is higher than that of 22MnB5,because more cementite leads to higher nucleation rate and diffusion coefficient of carbon atom.More amount of fine martensite forms under the higher deformation temperature or the quicker cooling rate.
基金Project(2016YFB0300802)supported by the National Key Research and Development Program of China。
文摘The effect of Li(2.0 wt%)addition on mechanical properties and ageing precipitation behavior of Al-3.0 Mg 0.5 Si was investigated by tensile test,dynamic elasticity modulus test,scanning electron microscopy(SEM),transmission electron microscopy(TEM)and high-resolution transmission electron microscopy(HRTEM)images.The results show that the tensile strength of the Li-containing alloy can be significantly improved;however,the ductility is sharply decreased and the fracture mechanism changes from ductile fracture to intergranular fracture.The elasticity modulus of the Li-containing alloy increases by 11.6%compared with the base alloy.The microstructure observation shows that the Li addition can absolutely change the precipitation behavior of the base alloy,andδ′-Al_(3)Li phase becomes the main precipitates.Besides,β′′-Mg_(2)Si andδ′-Al_(3)Li dual phases precipitation can be visibly observed at 170℃ ageing for 100 h,although the quantity ofδ′-Al_(3)Li phase is more thanβ′′-Mg_(2)Si phase.The width of the precipitate-free zone(PFZ)of the Li-containing alloy is much wider at the over-ageing state than the base alloy,which has a negative impact on the ductile and results in the decrease of elongation.
基金Project(2017YFB0306300)supported by the National Key R&D Program of ChinaProjects(51601060,51675538)supported by the National Natural Science Foundation of China。
文摘The effect of temperature in range of 155-175 ℃ on the creep behavior, microstructural evolution, and precipitation of an Al-Cu-Li alloy was experimentally investigated during creep ageing deformation under 180 MPa for 20 h. Increasing temperature resulted in a noteworthy change in creep ageing behaviour, including a variation in creep curves, an improvement in creep rate during early creep ageing, and an increased creep strain. Tensile tests indicate that the specimen aged at higher temperature reached peak strength within a shorter time. Transmission electron microscopy(TEM) was employed to explore the effect of temperature on the microstructural evolution of the AA2198 during creep ageing deformation. Many larger dislocations and even tangled dislocation structures were observed in the sample aged at higher temperature. The number of T1 precipitates increased at higher ageing temperature at the same ageing time. Based on the analysed results, a new mechanism, considering the combined effects of the formation of larger dislocation structures induced by higher temperature and diffusion of solute atoms towards these larger or tangled dislocations, was proposed to explain the effect of temperature on microstructural evolution and creep behaviour.