上世纪90年代,我们参加了美国"大陆地壳深部观察和取样计划(Deep Observation and Sampling of the Earth'sContinental Crust,DOSECC for Short)"的加州Cajon Pass科学深钻岩心裂隙构造应力场研究工作[1,2],至今仍对岩...上世纪90年代,我们参加了美国"大陆地壳深部观察和取样计划(Deep Observation and Sampling of the Earth'sContinental Crust,DOSECC for Short)"的加州Cajon Pass科学深钻岩心裂隙构造应力场研究工作[1,2],至今仍对岩芯中晚中生代花岗岩里韧脆性隐裂隙进行扫描电镜(SEM型号HITACH,S-415A、EDAX为PV9100)观察研究,发现其具有球形密集微粒结构,简述如下:展开更多
The influence of sulfur content in raw materials on oxidized pellets was studied. The results show that most sulfur exists in the form of elementary sulfur in pyrite cinder, and over 95% sulfur is removed in producing...The influence of sulfur content in raw materials on oxidized pellets was studied. The results show that most sulfur exists in the form of elementary sulfur in pyrite cinder, and over 95% sulfur is removed in producing pyrite cinder oxidized pellets. The compressive strength of fired pellets drops from 3 186 N to 2 405 N when the ratio of pyrite cinder increases from 40% to 70% under the conditions of preheating at 900℃ for 9 min and firing at 1 230 ℃ for 15 min. The porosity and microstructures of fired pellets prove that the higher ratio of pyrite cinder is given, and the more holes and cracks are achieved, leading to the better reducibility index （RI） and reduction swelling index （RSI）, and the lower compressive strength of fired pellets and the worse reduction degradation index （RDI）.展开更多
In this paper,15Cr-ODS steels containing 0,1 wt%,2 wt%and 3 wt%Al element were fabricated by combining wet-milling and spark plasma sintering(SPS)methods.The microstructure and mechanical properties of ODS steel were ...In this paper,15Cr-ODS steels containing 0,1 wt%,2 wt%and 3 wt%Al element were fabricated by combining wet-milling and spark plasma sintering(SPS)methods.The microstructure and mechanical properties of ODS steel were investigated by XRD,SEM,TEM,EBSD and tensile tests.The results demonstrate that the Al addition significantly refines the particle precipitates in the Fe-Cr matrix,leading to the obvious refinement in grain size of matrix and the improvement of mechanical properties.The dispersion particles in ODS steels with Al addition are identified as Al2O3 and Y_(2)Ti_(2)O_(7)nanoparticles,which has a heterogeneous size distribution in the range of 5 nm to 300 nm.Increasing Al addition causes an obvious increase in tensile strength and a decline in elongation.The tensile strength and elongation of 15Cr-ODS steel containing 3 wt%Al are 775.3 MPa and 15.1%,respectively.The existence of Al element improves the corrosion resistance of materials.The ODS steel containing 2 wt%Al shows corrosion potential of 0.39 V and passivation current density of 2.61×10^(−3)A/cm^(2)(1.37 V).This work shows that Al-doped ODS steels prepared by wet-milling and SPS methods have a potential application in structural parts for nuclear system.展开更多
Effect of electromagnetic stirring on microstructure of AZ91-0.8%Ce magnesium alloy was investigated. The results show that electromagnetic stirring causes a change of morphology of α-Mg phase from coarse dendrites t...Effect of electromagnetic stirring on microstructure of AZ91-0.8%Ce magnesium alloy was investigated. The results show that electromagnetic stirring causes a change of morphology of α-Mg phase from coarse dendrites to fine rosette-like or spherical shape. Grain size is significantly refined within the range of input voltage 75?125 V, moreover, the optimum input voltage corresponded to the minimum value (64 μm) of grain size is 125 V. Compared to the non-stirred condition, the amount of β-Mg17Al12 precipitate under the stirred condition obviously increases. The grain refinement of AZ91-0.8%Ce alloy is mainly attributed to multiplication of existing grains in the melt caused by forced fluid flow under electromagnetic stirring condition. Addition of 0.8% Ce results in the formation of ‘necking’ at secondary dendrite arm roots of α-Mg crystals, and consequently, it is helpful to increase the number of heterogeneous nucleation.展开更多
In the present work, scandium elements with a series of contents(0.06 wt.%, 0.10 wt.%, 0.14 wt.%,0.17 wt.%, 0.20 wt.% and 0.25 wt.%) were added in a high Zn-containing Al-Zn-Mg-Cu-Zr alloy and the corresponding as-cas...In the present work, scandium elements with a series of contents(0.06 wt.%, 0.10 wt.%, 0.14 wt.%,0.17 wt.%, 0.20 wt.% and 0.25 wt.%) were added in a high Zn-containing Al-Zn-Mg-Cu-Zr alloy and the corresponding as-cast microstructure characteristics including grains and phases were thoroughly investigated. The results indicated that fine grain boundaries existed in these alloys and fine MgZn2phases discontinuously distributed on them. Besides,AlZnMgCu eutectic phases and Sc, Zr-containing phases with flocculent morphology were observed. As scandium contents vary from 0.06 wt.% to 0.17 wt.%, the average grain size continuously decreased and its equiaxial characteristics were strengthened. Meanwhile, the content of AlZnMgCu eutectic phase showed a decrease trend. When scandium contents were 0.20 wt.% and 0.25 wt.%, no further enhancement on grain refinement was observed, so as to the reduction of AlZnMgCu eutectic phase content. Besides, Sc, Zr-containing phases with blocky morphology were observed and the alloy with a scandium content of 0.25 wt.% possessed a larger amount of blocky Sc, Zr-containing phase than the alloy with a scandium content of 0.20 wt.%. Grain refinement and reduction of AlZnMgCu eutectic phase content associated with scandium addition were discussed.展开更多
In this study, a lab-scale upflow anaerobic sludge blanket(UASB) reactor was applied to studying the high-rate nitrogen removal of granule-based anammox process. The nitrogen removal rate(NRR) finally improved to 15.7...In this study, a lab-scale upflow anaerobic sludge blanket(UASB) reactor was applied to studying the high-rate nitrogen removal of granule-based anammox process. The nitrogen removal rate(NRR) finally improved to 15.77 kg/m3/d by shortening hydraulic retention time(HRT) to 1.06 h. Well-shaped red anammox granules were extensively enriched inside the reactor. The results of nitrogen removal kinetics indicated that the present bioreactor has great nitrogen removal potential, because the maximum rate of substrate utilization(Umax) predicted by Stover-Kincannon model is suggested as 55.68 kg/(m3·d). Analysis of the microbial community showed that the anammox genus Candidatus Kuenenia dominated the bacterial communities. The relative abundance of Candidatus Kuenenia rose from 12.29% to 36.95% after progressively shorter HRT and higher influent substrate concentrations, illustrating the stability of nitrogen removal performance and biomass enrichment offered by the UASB in carrying out high-rate anammox process.展开更多
Nanometer Ni0.5Zn0.5Fe2O4 powders with spinel phase were prepared by the hydrothermal method using purified FeSO4 solution from sodium jarosite＇s slag as materials. The results show that the spinel phase of Ni0.5Zn0....Nanometer Ni0.5Zn0.5Fe2O4 powders with spinel phase were prepared by the hydrothermal method using purified FeSO4 solution from sodium jarosite＇s slag as materials. The results show that the spinel phase of Ni0.5Zn0.5Fe2O4 powders begins to form at a relatively low temperature （130 ℃） and a shorter holding time （1 h） when pH=8. The crystallization kinetics equation at 200℃ is ln[-ln（1-x）] =-0.78＋0.951n t. The growth activation energy of Ni0.5Zn0.5Fe2O4 grains is 41.6 kJ/moL in hydrothermal synthesis process. With the increase of sintering temperature, the density and diameter shrinkage of ferrite circulus increase, whereas its pores decrease. The results of magnetic measurements show that saturation magnetic flux density Bs increases and the coercivity Hc decreases with the increase of their sintering temperature. Magnetic parameters of all the investigated samples satisfy the character demand of high Bs, low Br and low Hc of soft magnetic ferrite materials.展开更多
Anodized composite films containing Si C nanoparticles were synthesized on Ti6Al4 V alloy by anodic oxidation procedure in C4O6H4Na2 electrolyte. Scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS) ...Anodized composite films containing Si C nanoparticles were synthesized on Ti6Al4 V alloy by anodic oxidation procedure in C4O6H4Na2 electrolyte. Scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS) and X-ray photoelectron spectroscopy(XPS) were employed to characterize the morphology and composition of the films fabricated in the electrolytes with and without addition of Si C nanoparticles. Results show that Si C particles can be successfully incorporated into the oxide film during the anodizing process and preferentially concentrate within internal cavities and micro-cracks. The ball-on-disk sliding tests indicate that Si C-containing oxide films register much lower wear rate than the oxide films without Si C under dry sliding condition. Si C particles are likely to melt and then are oxidized by frictional heat during sliding tests. Potentiodynamic polarization behavior reveals that the anodized alloy with Si C nanoparticles results in a reduction in passive current density to about 1.54×10-8 A/cm2, which is more than two times lower than that of the Ti O2 film(3.73×10-8 A/cm2). The synthesized composite film has good anti-wear and anti-corrosion properties and the growth mechanism of nanocomposite film is also discussed.展开更多
文摘上世纪90年代,我们参加了美国"大陆地壳深部观察和取样计划(Deep Observation and Sampling of the Earth'sContinental Crust,DOSECC for Short)"的加州Cajon Pass科学深钻岩心裂隙构造应力场研究工作[1,2],至今仍对岩芯中晚中生代花岗岩里韧脆性隐裂隙进行扫描电镜(SEM型号HITACH,S-415A、EDAX为PV9100)观察研究,发现其具有球形密集微粒结构,简述如下:
基金Project(2007k02) supported by the Technology Fund of the Land and Resources Department of Hunan Province, China
文摘The influence of sulfur content in raw materials on oxidized pellets was studied. The results show that most sulfur exists in the form of elementary sulfur in pyrite cinder, and over 95% sulfur is removed in producing pyrite cinder oxidized pellets. The compressive strength of fired pellets drops from 3 186 N to 2 405 N when the ratio of pyrite cinder increases from 40% to 70% under the conditions of preheating at 900℃ for 9 min and firing at 1 230 ℃ for 15 min. The porosity and microstructures of fired pellets prove that the higher ratio of pyrite cinder is given, and the more holes and cracks are achieved, leading to the better reducibility index （RI） and reduction swelling index （RSI）, and the lower compressive strength of fired pellets and the worse reduction degradation index （RDI）.
基金Project(2020JJ2001)supported by Outstanding Youth Scientist Foundation of Hunan Province,ChinaProject(6142912200102)supported by Foundation for National Key Laboratory of Science and Technology on Highstrength Structural Materials,China。
文摘In this paper,15Cr-ODS steels containing 0,1 wt%,2 wt%and 3 wt%Al element were fabricated by combining wet-milling and spark plasma sintering(SPS)methods.The microstructure and mechanical properties of ODS steel were investigated by XRD,SEM,TEM,EBSD and tensile tests.The results demonstrate that the Al addition significantly refines the particle precipitates in the Fe-Cr matrix,leading to the obvious refinement in grain size of matrix and the improvement of mechanical properties.The dispersion particles in ODS steels with Al addition are identified as Al2O3 and Y_(2)Ti_(2)O_(7)nanoparticles,which has a heterogeneous size distribution in the range of 5 nm to 300 nm.Increasing Al addition causes an obvious increase in tensile strength and a decline in elongation.The tensile strength and elongation of 15Cr-ODS steel containing 3 wt%Al are 775.3 MPa and 15.1%,respectively.The existence of Al element improves the corrosion resistance of materials.The ODS steel containing 2 wt%Al shows corrosion potential of 0.39 V and passivation current density of 2.61×10^(−3)A/cm^(2)(1.37 V).This work shows that Al-doped ODS steels prepared by wet-milling and SPS methods have a potential application in structural parts for nuclear system.
基金Project(2004ABA110) supported by the Natural Science Foundation of Hubei Province project(471-38300843) supported by the Research Foundation for the Doctoral Program of Wuhan University of Technology
文摘Effect of electromagnetic stirring on microstructure of AZ91-0.8%Ce magnesium alloy was investigated. The results show that electromagnetic stirring causes a change of morphology of α-Mg phase from coarse dendrites to fine rosette-like or spherical shape. Grain size is significantly refined within the range of input voltage 75?125 V, moreover, the optimum input voltage corresponded to the minimum value (64 μm) of grain size is 125 V. Compared to the non-stirred condition, the amount of β-Mg17Al12 precipitate under the stirred condition obviously increases. The grain refinement of AZ91-0.8%Ce alloy is mainly attributed to multiplication of existing grains in the melt caused by forced fluid flow under electromagnetic stirring condition. Addition of 0.8% Ce results in the formation of ‘necking’ at secondary dendrite arm roots of α-Mg crystals, and consequently, it is helpful to increase the number of heterogeneous nucleation.
基金Projects(2020YFB0311400ZL, 2020YFF0218202) supported by the National Key R&D Program of ChinaProject supported by Youth Fund Project of GRINM Group Co.,Ltd.,China。
文摘In the present work, scandium elements with a series of contents(0.06 wt.%, 0.10 wt.%, 0.14 wt.%,0.17 wt.%, 0.20 wt.% and 0.25 wt.%) were added in a high Zn-containing Al-Zn-Mg-Cu-Zr alloy and the corresponding as-cast microstructure characteristics including grains and phases were thoroughly investigated. The results indicated that fine grain boundaries existed in these alloys and fine MgZn2phases discontinuously distributed on them. Besides,AlZnMgCu eutectic phases and Sc, Zr-containing phases with flocculent morphology were observed. As scandium contents vary from 0.06 wt.% to 0.17 wt.%, the average grain size continuously decreased and its equiaxial characteristics were strengthened. Meanwhile, the content of AlZnMgCu eutectic phase showed a decrease trend. When scandium contents were 0.20 wt.% and 0.25 wt.%, no further enhancement on grain refinement was observed, so as to the reduction of AlZnMgCu eutectic phase content. Besides, Sc, Zr-containing phases with blocky morphology were observed and the alloy with a scandium content of 0.25 wt.% possessed a larger amount of blocky Sc, Zr-containing phase than the alloy with a scandium content of 0.20 wt.%. Grain refinement and reduction of AlZnMgCu eutectic phase content associated with scandium addition were discussed.
基金Project(51878662)supported by the National Natural Science Foundation of ChinaProject(2017SK2420)supported by the Science and Technology of Hunan Province,ChinaProject(2019JJ20033)supported by the Distinguished Youth Natural Science Foundation of Hunan Province,China。
文摘In this study, a lab-scale upflow anaerobic sludge blanket(UASB) reactor was applied to studying the high-rate nitrogen removal of granule-based anammox process. The nitrogen removal rate(NRR) finally improved to 15.77 kg/m3/d by shortening hydraulic retention time(HRT) to 1.06 h. Well-shaped red anammox granules were extensively enriched inside the reactor. The results of nitrogen removal kinetics indicated that the present bioreactor has great nitrogen removal potential, because the maximum rate of substrate utilization(Umax) predicted by Stover-Kincannon model is suggested as 55.68 kg/(m3·d). Analysis of the microbial community showed that the anammox genus Candidatus Kuenenia dominated the bacterial communities. The relative abundance of Candidatus Kuenenia rose from 12.29% to 36.95% after progressively shorter HRT and higher influent substrate concentrations, illustrating the stability of nitrogen removal performance and biomass enrichment offered by the UASB in carrying out high-rate anammox process.
基金Project(50204001) supported by the National Natural Science Foundation of China
文摘Nanometer Ni0.5Zn0.5Fe2O4 powders with spinel phase were prepared by the hydrothermal method using purified FeSO4 solution from sodium jarosite＇s slag as materials. The results show that the spinel phase of Ni0.5Zn0.5Fe2O4 powders begins to form at a relatively low temperature （130 ℃） and a shorter holding time （1 h） when pH=8. The crystallization kinetics equation at 200℃ is ln[-ln（1-x）] =-0.78＋0.951n t. The growth activation energy of Ni0.5Zn0.5Fe2O4 grains is 41.6 kJ/moL in hydrothermal synthesis process. With the increase of sintering temperature, the density and diameter shrinkage of ferrite circulus increase, whereas its pores decrease. The results of magnetic measurements show that saturation magnetic flux density Bs increases and the coercivity Hc decreases with the increase of their sintering temperature. Magnetic parameters of all the investigated samples satisfy the character demand of high Bs, low Br and low Hc of soft magnetic ferrite materials.
基金Project(51271012)supported by the National Natural Science Foundation of China
文摘Anodized composite films containing Si C nanoparticles were synthesized on Ti6Al4 V alloy by anodic oxidation procedure in C4O6H4Na2 electrolyte. Scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS) and X-ray photoelectron spectroscopy(XPS) were employed to characterize the morphology and composition of the films fabricated in the electrolytes with and without addition of Si C nanoparticles. Results show that Si C particles can be successfully incorporated into the oxide film during the anodizing process and preferentially concentrate within internal cavities and micro-cracks. The ball-on-disk sliding tests indicate that Si C-containing oxide films register much lower wear rate than the oxide films without Si C under dry sliding condition. Si C particles are likely to melt and then are oxidized by frictional heat during sliding tests. Potentiodynamic polarization behavior reveals that the anodized alloy with Si C nanoparticles results in a reduction in passive current density to about 1.54×10-8 A/cm2, which is more than two times lower than that of the Ti O2 film(3.73×10-8 A/cm2). The synthesized composite film has good anti-wear and anti-corrosion properties and the growth mechanism of nanocomposite film is also discussed.