Aging precipitation and solid solution heat treatment were carried out on three steels which have chromium content of 18%, manganese content of 12%, 15%, 18%, and nitrogen content of 0.43%, 0.53%, 0.67%, respectively....Aging precipitation and solid solution heat treatment were carried out on three steels which have chromium content of 18%, manganese content of 12%, 15%, 18%, and nitrogen content of 0.43%, 0.53%, 0.67%, respectively. The mechanisms of precipitation and solid solution of high nitrogen anstenitic stainless steel were studied using the scanning electron microscopy, transmission electron microscopy, electron probe micro analysis and mechanical testing. The results show that, Cr2N is the primary precipitate in the tested stainless steels instead of Cr23C6. Cr2N nucleates at austenitic grain boundaries and grows towards inner grains with a lameUar morphology. By means of pre-precipitation of Cr2N at 800 ~C, the microstructure of the steels at solid solution state can be refined, thus improving the strength and plasticity. After the proposed treatment, the tensile strength, the proof strength and the elongation of the tested steel reach 881 MPa, 542 MPa and 54%, respectively.展开更多
In order to investigate the existing form and action mechanism of minor scandium （Sc） and zirconium （Zr） in AI-Cu-Mg alloy, microstructures of Al-4Cu-1Mg-Sc-Zr alloy under different conditions, including states of...In order to investigate the existing form and action mechanism of minor scandium （Sc） and zirconium （Zr） in AI-Cu-Mg alloy, microstructures of Al-4Cu-1Mg-Sc-Zr alloy under different conditions, including states of as-cast, homogenized, hot-rolled, as-solution and natural aged, were observed by scanning electron microscopy （SEM）, X-ray diffractometry （XRD） and transmission electron microscopy （TEM）. It is revealed that Sc and Zr are completely dissolved into the supersaturated solid solution in as-cast ingot, but grain refinement is not observed. Coffee-bean-like AI3（Sc, Zr） particles deposit during homogenization of ingot induce an increase in hardness. Al3（Sc, Zr） particles are slightly coarsened in as-solution samples, but they still maintain coherent to matrix, which indicates a high thermal stability of these particles. Good coherency ofAl3（Sc, Zr） particles makes some benefits for inhibiting recrystallization and reserving work-hardening.展开更多
A yttrium-containing high-temperature titanium alloy(Ti-6Al-2.7Sn-4Zr-0.4Mo-0.45Si-0.1Y, mass fraction, %) has been additively manufactured using selective electron beam melting(SEBM). The resulting microstructure and...A yttrium-containing high-temperature titanium alloy(Ti-6Al-2.7Sn-4Zr-0.4Mo-0.45Si-0.1Y, mass fraction, %) has been additively manufactured using selective electron beam melting(SEBM). The resulting microstructure and textures were studied using scanning electron microscopy(SEM), transmission electron microscopy(TEM), X-ray diffraction(XRD) and electron backscattered diffraction(EBSD) and compared with the conventionally manufactured form. A notable distinct difference of microstructures is that additive manufacturing by SEBM enables homogeneous precipitation of fine Y2O3 dispersoids in the size range of 50-250 nm throughout the as-fabricated alloy, despite the presence of just trace levels of oxygen(7×10-4, mass fraction) and yttrium(10-3, mass fraction) in the alloy. In contrast, the conventionally manufactured alloy shows inhomogeneously distributed coarse Y2O3 precipitates, including cracked or debonded Y2O3 particles.展开更多
The durability of silty clay embankments is partially controlled by the moisture migration, which depends on soil hydraulic properties. This paper presents an experimental study of hydraulic properties of compacted bi...The durability of silty clay embankments is partially controlled by the moisture migration, which depends on soil hydraulic properties. This paper presents an experimental study of hydraulic properties of compacted binary silty clay. Specimens with different mixing ratios and dry densities were prepared. Scanning electron microscopy and mercury intrusion porosimetry were used to characterise the microstructure of silty clay. Thereafter, falling-head permeability tests and water retention tests were conducted to study the permeability and water retention property, respectively. The results demonstrate that clay particles are dispersed and show preferred arrangements after compaction when the clay content is 100%. As the clay content decreases, the arrangement of clay particles is gradually disturbed because of the existence of silt particles, causing the formation of large pores around silt particles. When the dry density increases, the pores around silt particles significantly decrease. Moreover, the permeability of silty clay decreases but the water retention capacity increases with increasing clay content and dry density. This is because the silty clay with larger clay content and dry density has fewer large pores, which greatly restrains the flow of water. Both the permeability and water retention property of silty clay can be predicted from pore size distribution parameters.展开更多
A LiFePO4/（C＋Fe2P） composite cathode material was prepared by a sol-gel method using Fe（NO3）3.9H20, LiAc·H2O）, NHaH2PO4 and citric acid as raw materials, and the physical properties and electrochemical perf...A LiFePO4/（C＋Fe2P） composite cathode material was prepared by a sol-gel method using Fe（NO3）3.9H20, LiAc·H2O）, NHaH2PO4 and citric acid as raw materials, and the physical properties and electrochemical performance of the composite cathode material were investigated by X-ray diffractometry （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and electrochemical tests. The Fe2P content, morphology and electrochemical performance of LiFePOa/（C＋Fe2P） composite depend on the calcination temperature. The optimized LiFePO4/（C＋FeeP） composite is prepared at 650 ~C and the optimized composite exhibits sphere-like morphology with porous structure and Fe2P content of about 3.2% （mass fraction）. The discharge capacity of the optimized LiFePO4/（C＋FeRP） at 0.1C is 156 and 161 mA.h/g at 25 and 55 ℃, respectively, and the corresponding capacity retentions are 96% after 30 cycles; while the capacity at 1C is 142 and 149 mA.h/g at 25 and 55 ℃, respectively, and the capacity still remains 135 and 142 mA-h/g after 30 cycles at 25 and 55℃, respectively.展开更多
The elevated-temperature mechanical properties and thermal stability of Al-Cu-Mg-Ag heat-resistant alloy were studied by tensile test, transmission electron microscopy(TEM) and scanning electron microscopy(SEM), respe...The elevated-temperature mechanical properties and thermal stability of Al-Cu-Mg-Ag heat-resistant alloy were studied by tensile test, transmission electron microscopy(TEM) and scanning electron microscopy(SEM), respectively. The results show that with the increase of Ag content, the tensile strength and yield strength increase, which is attributed to the increase of the precipitations number and the decrease of the size. The same conclusions are drawn in the study of increasing Mg content. The alloy possesses excellent thermal stability. At 100-150 °C, the strength of the under-aged alloy increases at the initial stage, and after reaching the peak strength, it remains the same. The secondary precipitation of the under-aged alloy occurs in the process of exposure at 150℃, and it distributes diffusely after thermal exposed for 20 h. Then, the tensile strength decreases gradually with increasing the thermal exposure time at 200-250 °C. The strength of the peak-aged alloy decreases gradually, and the precipitation grows up, but the number decreases gradually with prolonging the exposure time at 100-250 °C. The strength of two kinds of alloys decreases with elevating of exposure temperature.展开更多
Effect of element cerium （Ce） on microstructure and mechanical properties of A1-Zn-Mg-Cu alloys has been investigated by transmission electron microscopy （TEM）, scanning electron microscopy （SEM）, differential s...Effect of element cerium （Ce） on microstructure and mechanical properties of A1-Zn-Mg-Cu alloys has been investigated by transmission electron microscopy （TEM）, scanning electron microscopy （SEM）, differential scanning calorimetry （DSC） and hardness test. The results show that addition of Ce can remarkably refine the as-cast grains and eutectic microstructure. A transformation from Mg（Zn,Cu,A1）2 phase to A12CuMg phase is observed during homogenization. Furthermore, the Ce addition introduces changes in the precipitation process and consequently in the age-hardening behavior of the alloy. Microstructural measurements reveal that the addition of Ce promotes the precipitation of η＇ phase, but it also partly retards the precipitation of GP zones. The density of precipitates decreases in a certain degree and rod-like η＇ precipitates increase when Ce content is from 0.2% to 0.4% （mass fraction）.展开更多
A series of researches were carried out for the soil samples in the Pearl River Delta under the action of consolidation loads,such as the quantitative analyses of the pore scale,shape and size distributions of micro-s...A series of researches were carried out for the soil samples in the Pearl River Delta under the action of consolidation loads,such as the quantitative analyses of the pore scale,shape and size distributions of micro-structure units,with an environmental scanning electron microscope (ESEM),a mercury intrusion analyzer and a mineral diffractometer. The experimental results show that the consolidation pressures remarkably change the pore sizes and distribution characteristics of the silt,thus changing its compressibility and permeability. This can be proved by the fact that,in the earlier stage with a consolidation pressure of p<200 kPa,the pore sizes are greater and the compressibility and permeability coefficients are larger. However,they rapidly decrease with the increase in consolidation pressure. And in the later stage with a consolidation pressure of p>200 kPa,the pore sizes are smaller and the compressibility and permeability coefficients are less. Therefore,the empirical formulas of compression coefficient and permeability coefficient vs consolidation load and average pore diameter are deduced.展开更多
Fe/Si3N4 composite powder was synthesized by the heterogeneous precipitation-thermal reduction process,and then pressed into flakes under a pressure of 10 MPa.Flakes were sintered by pressureless and hot-pressing at 1...Fe/Si3N4 composite powder was synthesized by the heterogeneous precipitation-thermal reduction process,and then pressed into flakes under a pressure of 10 MPa.Flakes were sintered by pressureless and hot-pressing at 1 600℃under 0.1 MPa N2. The chemical composition,phases and microstructure of composite powder and sintered flakes were investigated by energy dispersive spectroscopy(EDS),X-ray diffraction(XRD),scanning electron microscopy(SEM)and transmission electron microscopy (TEM).The results show that the structure of composite powders is Si3N4 coated by nano Fe.The crystal phases of sintered flakes by pressureless are Fe(Si)compound,SiC and Si3N4.The crystal phases of the sintered samples by hot-pressing are Fe,Fe(Si) compound and Si3N4.It is found that crystal phases flakes obtained by pressureless and hot-pressing are very different.展开更多
In order to synthesize ZnO nanoparticles economically, industrial-grade zinc sulfate and urea were utilized to synthesize ZnO precursors in a stirred-tank reactor or a Teflon-lined autoclave at 100-180 ℃ under comple...In order to synthesize ZnO nanoparticles economically, industrial-grade zinc sulfate and urea were utilized to synthesize ZnO precursors in a stirred-tank reactor or a Teflon-lined autoclave at 100-180 ℃ under complete sealing condition. The ZnO precursors were calcined at 450 ℃ for 3 h to, synthesize ZnO nanoparticles. The composition of the precursors and the formation mechanism of ZnO were studied by thermogravimetric analysis and Fourier transform infrared spectroscopy. The results of X-ray diffraction, transmission electron microscopy and scanning electron microscopy of the ZnO powders demonstrate that high-purity zincite ZnO nanoparticles are synthesized. Orthogonal experiments were performed to find out the optimal conditions for the maximum yield and the minimum size. The ettect of temperature on the size ofZnO nanoparticles was investigated. The results show that a higher temperature is propitious to obtain smaller nanoparticles.展开更多
Well-crystallized hexagonal hematite （α-Fe2O3） platelets were synthesized by hydrothermal process, using a highly concentrated ferric hydroxide as precursor. The precursor was prepared by adding ammonia to the ferr...Well-crystallized hexagonal hematite （α-Fe2O3） platelets were synthesized by hydrothermal process, using a highly concentrated ferric hydroxide as precursor. The precursor was prepared by adding ammonia to the ferric sulfate solution which was obtained by leaching pyrite cinders with sulfuric acid. Structure and morphology of the synthesized products were investigated by X-ray diffraction, scanning electron microscope, transmission electron microscope and selected area electron diffraction. The results reveal that the reaction temperature has significant effects on the structure, size and shape of the synthesized hematite particles. Typical hexagonal hematite platelets, about 0.4-0.6 μm in diameter and 0.1 μm in thickness, were prepared at 230 ℃ for 0.5 h. Al^3＋, contained in the sulfuric acid leaching solution as an impurity, plays an extremely important role in the formation of hexagonal hematite. In addition, a possible mechanism about the formation of hexagonal hematite platelets was proposed.展开更多
The effects of low temperature thermo-mechanical treatment （LTTMT） on microstructures and mechanical properties of Ti-6Al-4V （TC4） alloy were studied by optical microscopy （OM）, tensile test, scanning electron m...The effects of low temperature thermo-mechanical treatment （LTTMT） on microstructures and mechanical properties of Ti-6Al-4V （TC4） alloy were studied by optical microscopy （OM）, tensile test, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The experimental results confirm that the strength of TC4 alloy can be improved obviously by LTTMT processing, which combines strain strengthening with aging strengthening. The effect of LTTMT on the alloy depends on the microstructure of the refined and dispersed a＋fl phase on the basis of high dislocation density by pre-deformation below recrystallization temperature. The tensile strength decreases with the increase of pre-deformation reduction. The optimal processing parameters of LTTMT for TC4 alloy are as follows： solution treatment at 900 ℃ for 15 min, pre-deformation in the range of 600-700 ℃ with a reduction of 35%, finally aging at 540 ℃ for 4 h followed by air-cooling.展开更多
The through-thickness corrosion inhomogeneity of 7050-T7451 Al alloy thick plate was studied using immersion tests, potentiodynamic polarization, electrochemical impedance spectroscopy(EIS), slow strain rate testing(S...The through-thickness corrosion inhomogeneity of 7050-T7451 Al alloy thick plate was studied using immersion tests, potentiodynamic polarization, electrochemical impedance spectroscopy(EIS), slow strain rate testing(SSRT) technique combined with optical microscopy(OM), scanning electron microscopy(SEM) and transmission electron microscopy(TEM). The results show that the through-thickness corrosion resistance is ranked in the order of T/2>surface>T/4. And the 75 mm-thick 7050 alloy plate presents better corrosion resistance than the 35 mm-thick plate. The results are discussed in terms of the combined effect of recrystallization and cooling rate in quenching. Alloy with lower volume fraction of recrystallization and smaller grain aspect ratio displays better corrosion resistance. The lower corrosion resistance caused by the slower cooling rate results from the higher coverage rate of grain boundary precipitates and larger width of precipitate free zone.展开更多
A novel carbon fiber pretreatment was proposed.Polyacrylonitrile(PAN)-based carbon fibers were first anodized in H3PO4 electrolyte to achieve an active surface,and then coated with Mo-B catalysts by immersed the carbo...A novel carbon fiber pretreatment was proposed.Polyacrylonitrile(PAN)-based carbon fibers were first anodized in H3PO4 electrolyte to achieve an active surface,and then coated with Mo-B catalysts by immersed the carbon fibers in a uniformly dispersed Mo-B sol.The as-treated carbon fibers were then graphitized at 2 400 ℃ for 2 h.The structural changes were characterized by X-ray diffractometry(XRD),Raman spectroscopy,scanning electron microscopy(SEM) and high-resolution transmission electronic microscopy(HRTEM).The results show that much better graphitization can be achieved in the presence of Mo-B,with an interlayer spacing(d002) of 0.335 8 nm and a crystalline size(Lc) of 28 nm.展开更多
Zn2GeO4 nanorods were prepared by a surfactant-assisted solution phase route.The as-prepared products were characterized by X-ray powder diffraction(XRD),scanning electron microscopy(SEM),high-resolution transmission ...Zn2GeO4 nanorods were prepared by a surfactant-assisted solution phase route.The as-prepared products were characterized by X-ray powder diffraction(XRD),scanning electron microscopy(SEM),high-resolution transmission electron microscopy(HRTEM),inductively coupled plasma atomic emission spectrometer(ICP-AES),UV-vis diffuse reflection spectroscopy and photoluminescence(PL) spectroscopy.The possible formation mechanism of Zn2GeO4 nanorods was discussed.It was supposed that the CTA+ cations preferentially adsorb on the planes of Zn2GeO4 nanorods,leading to preferential growth along the c-axis to form the Zn2GeO4 rods with larger aspect ratio and higher surface area,which showed the improved photocatalytic activity for photoreduction of CO2.The photoluminescence(PL) property of Zn2GeO4 nanorods was investigated through the emission spectra.展开更多
Micaceous iron oxide （MIO） with a hexagonal flaky shape was prepared by hydrothermal method. The ferric hydroxide used as precursor was obtained by an acidic leaching solution of pyrite cinders reacting with ammonia...Micaceous iron oxide （MIO） with a hexagonal flaky shape was prepared by hydrothermal method. The ferric hydroxide used as precursor was obtained by an acidic leaching solution of pyrite cinders reacting with ammonia solution. The optimal experimental conditions for preparing micaceous iron oxide were investigated by orthogonal experiments. Micaceous iron oxide can be successfully prepared when optimal parameters of total iron concentration of 2.0 mol/L, pH value of 8, n（Fe2＋）/n（Fe3＋） of 0.1, mass of seed crystal of 1 g, reaction temperature of 260 ℃ and reaction time of 30 min are applied. X-ray diffractometry （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and selected area electron diffractometry （SAEM） were adopted to characterize the hydrothermal products prepared under optimal conditions. The results indicate that highly crystallized α-Fe2O3 hexagonal flakes, about 1.0-1.5 μm in diameter and 0.1 μm in thickness, are prepared. Furthermore, the quality of micaceous iron oxide prepared can meet the required characteristics of micaceous iron oxide pigments for paints （ISO 10601--2007）.展开更多
The strength, fracture toughness and fatigue crack growth resistance of 7050-T7451 aluminum alloy plate with different thicknesses （35 mm and 160 ram） were investigated by means of optical microscope, scanning elect...The strength, fracture toughness and fatigue crack growth resistance of 7050-T7451 aluminum alloy plate with different thicknesses （35 mm and 160 ram） were investigated by means of optical microscope, scanning electron microscope and transmission electron microscope. The results show that thicker plate has lower strength and fracture toughness but higher fatigue crack growth resistance, by comparison to the thinner plate. The drop of strength is mainly attributed to grain coarsening in the thicker plate, and the increased degree of recrystallization results in the loss of Kio However, the coarsened grains in the thicker plate make cracks deflected and closure effect enhanced due to surface roughness increased. For both of plates, in the fracture surface subjected plain strain, a transition from transgranular dimpled fracture to intergranular dimpled fracture is observed during the fracture process.展开更多
In order to improve the electrochemical hydrogen storage performance of the Mg2Ni-type electrode alloys, Mg in the alloy was partially substituted by La, and the nanocrystalline and amorphous Mg2Ni-type Mg20-xLaxNi10 ...In order to improve the electrochemical hydrogen storage performance of the Mg2Ni-type electrode alloys, Mg in the alloy was partially substituted by La, and the nanocrystalline and amorphous Mg2Ni-type Mg20-xLaxNi10 （x-=0, 2） alloys were synthesized by melt-spinning technique. The microstructures of the as-spun alloys were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The electrochemical hydrogen storage properties of the experimental alloys were tested. The results show that no amorphous phase is detected in the as-spun Mg20Ni10 alloy, but the as-spun Mg18La2Ni10 alloy holds a major amorphous phase. As La content increases from 0 to 2, the maximum discharge capacity of the as-spun （20 m/s） alloys rises from 96.5 to 387.1 mA.h/g, and the capacity retaining rate （S20） at the 20th cycle grows from 31.3% to 71.7%. Melt-spinning engenders an impactful effect on the electrochemical hydrogen storage performances of the alloys. With the increase in the spinning rate from 0 to 30 m/s, the maximum discharge capacity increases from 30.3 to 135.5 mA.h/g for the Mg20Ni10 alloy, and from 197.2 to 406.5 mA-h/g for the Mg18La2Ni10 alloy. The capacity retaining rate （S20） of the Mg2oNi10 alloy at the 20th cycle slightly falls from 36.7% to 27.1%, but it markedly mounts up from 37.3% to 78.3% for the Mg18La2Ni10 alloy.展开更多
基金Project(50974014) supported by the National Natural Science Foundation of China
文摘Aging precipitation and solid solution heat treatment were carried out on three steels which have chromium content of 18%, manganese content of 12%, 15%, 18%, and nitrogen content of 0.43%, 0.53%, 0.67%, respectively. The mechanisms of precipitation and solid solution of high nitrogen anstenitic stainless steel were studied using the scanning electron microscopy, transmission electron microscopy, electron probe micro analysis and mechanical testing. The results show that, Cr2N is the primary precipitate in the tested stainless steels instead of Cr23C6. Cr2N nucleates at austenitic grain boundaries and grows towards inner grains with a lameUar morphology. By means of pre-precipitation of Cr2N at 800 ~C, the microstructure of the steels at solid solution state can be refined, thus improving the strength and plasticity. After the proposed treatment, the tensile strength, the proof strength and the elongation of the tested steel reach 881 MPa, 542 MPa and 54%, respectively.
基金Project(2005DFA50550) supported by International Science and Technology Cooperation Program of ChinaProject(2005CB623705) supported by the National Basic Research Program of China
文摘In order to investigate the existing form and action mechanism of minor scandium （Sc） and zirconium （Zr） in AI-Cu-Mg alloy, microstructures of Al-4Cu-1Mg-Sc-Zr alloy under different conditions, including states of as-cast, homogenized, hot-rolled, as-solution and natural aged, were observed by scanning electron microscopy （SEM）, X-ray diffractometry （XRD） and transmission electron microscopy （TEM）. It is revealed that Sc and Zr are completely dissolved into the supersaturated solid solution in as-cast ingot, but grain refinement is not observed. Coffee-bean-like AI3（Sc, Zr） particles deposit during homogenization of ingot induce an increase in hardness. Al3（Sc, Zr） particles are slightly coarsened in as-solution samples, but they still maintain coherent to matrix, which indicates a high thermal stability of these particles. Good coherency ofAl3（Sc, Zr） particles makes some benefits for inhibiting recrystallization and reserving work-hardening.
基金Projects(2014KTZB01-02-03,2014KTZB01-02-04)supported by Shaanxi Science and Technology Coordination and Innovation Program,ChinaProject(DP120101672)supported by Australian Research Council(ARC)Discovery Grant,ARC Centre of Excellence for Design in Light Metals,Australia
文摘A yttrium-containing high-temperature titanium alloy(Ti-6Al-2.7Sn-4Zr-0.4Mo-0.45Si-0.1Y, mass fraction, %) has been additively manufactured using selective electron beam melting(SEBM). The resulting microstructure and textures were studied using scanning electron microscopy(SEM), transmission electron microscopy(TEM), X-ray diffraction(XRD) and electron backscattered diffraction(EBSD) and compared with the conventionally manufactured form. A notable distinct difference of microstructures is that additive manufacturing by SEBM enables homogeneous precipitation of fine Y2O3 dispersoids in the size range of 50-250 nm throughout the as-fabricated alloy, despite the presence of just trace levels of oxygen(7×10-4, mass fraction) and yttrium(10-3, mass fraction) in the alloy. In contrast, the conventionally manufactured alloy shows inhomogeneously distributed coarse Y2O3 precipitates, including cracked or debonded Y2O3 particles.
基金Projects(51908069, 51908073, 51838001, 51878070) supported by the National Natural Science Foundation of ChinaProject(2019SK2171) supported by the Key Research and Development Program of Hunan Province, China+2 种基金Project(kfj190605) supported by the Open Fund of Engineering Laboratory of Spatial Information Technology of Highway Geological Disaster Early Warning in Hunan Province (Changsha University of Science & Technology),ChinaProject(2019IC04) supported by the Double First-Class Scientific Research International Cooperation Expansion Project of Changsha University of Science & Technology, ChinaProject(kq1905043) supported by the Training Program for Excellent Young Innovators of Changsha, China。
文摘The durability of silty clay embankments is partially controlled by the moisture migration, which depends on soil hydraulic properties. This paper presents an experimental study of hydraulic properties of compacted binary silty clay. Specimens with different mixing ratios and dry densities were prepared. Scanning electron microscopy and mercury intrusion porosimetry were used to characterise the microstructure of silty clay. Thereafter, falling-head permeability tests and water retention tests were conducted to study the permeability and water retention property, respectively. The results demonstrate that clay particles are dispersed and show preferred arrangements after compaction when the clay content is 100%. As the clay content decreases, the arrangement of clay particles is gradually disturbed because of the existence of silt particles, causing the formation of large pores around silt particles. When the dry density increases, the pores around silt particles significantly decrease. Moreover, the permeability of silty clay decreases but the water retention capacity increases with increasing clay content and dry density. This is because the silty clay with larger clay content and dry density has fewer large pores, which greatly restrains the flow of water. Both the permeability and water retention property of silty clay can be predicted from pore size distribution parameters.
基金Project(50571091) supported by the National Natural Science Foundation of ChinaProject(09C947) supported by the Scientific Research Fund of Hunan Provincial Education Department,China
文摘A LiFePO4/（C＋Fe2P） composite cathode material was prepared by a sol-gel method using Fe（NO3）3.9H20, LiAc·H2O）, NHaH2PO4 and citric acid as raw materials, and the physical properties and electrochemical performance of the composite cathode material were investigated by X-ray diffractometry （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and electrochemical tests. The Fe2P content, morphology and electrochemical performance of LiFePOa/（C＋Fe2P） composite depend on the calcination temperature. The optimized LiFePO4/（C＋FeeP） composite is prepared at 650 ~C and the optimized composite exhibits sphere-like morphology with porous structure and Fe2P content of about 3.2% （mass fraction）. The discharge capacity of the optimized LiFePO4/（C＋FeRP） at 0.1C is 156 and 161 mA.h/g at 25 and 55 ℃, respectively, and the corresponding capacity retentions are 96% after 30 cycles; while the capacity at 1C is 142 and 149 mA.h/g at 25 and 55 ℃, respectively, and the capacity still remains 135 and 142 mA-h/g after 30 cycles at 25 and 55℃, respectively.
基金Project(2012zzts067)supported by the Freedom Explore Program of Central South University,China
文摘The elevated-temperature mechanical properties and thermal stability of Al-Cu-Mg-Ag heat-resistant alloy were studied by tensile test, transmission electron microscopy(TEM) and scanning electron microscopy(SEM), respectively. The results show that with the increase of Ag content, the tensile strength and yield strength increase, which is attributed to the increase of the precipitations number and the decrease of the size. The same conclusions are drawn in the study of increasing Mg content. The alloy possesses excellent thermal stability. At 100-150 °C, the strength of the under-aged alloy increases at the initial stage, and after reaching the peak strength, it remains the same. The secondary precipitation of the under-aged alloy occurs in the process of exposure at 150℃, and it distributes diffusely after thermal exposed for 20 h. Then, the tensile strength decreases gradually with increasing the thermal exposure time at 200-250 °C. The strength of the peak-aged alloy decreases gradually, and the precipitation grows up, but the number decreases gradually with prolonging the exposure time at 100-250 °C. The strength of two kinds of alloys decreases with elevating of exposure temperature.
基金Project(2010CB731706) supported by the National Basic Research Program of China
文摘Effect of element cerium （Ce） on microstructure and mechanical properties of A1-Zn-Mg-Cu alloys has been investigated by transmission electron microscopy （TEM）, scanning electron microscopy （SEM）, differential scanning calorimetry （DSC） and hardness test. The results show that addition of Ce can remarkably refine the as-cast grains and eutectic microstructure. A transformation from Mg（Zn,Cu,A1）2 phase to A12CuMg phase is observed during homogenization. Furthermore, the Ce addition introduces changes in the precipitation process and consequently in the age-hardening behavior of the alloy. Microstructural measurements reveal that the addition of Ce promotes the precipitation of η＇ phase, but it also partly retards the precipitation of GP zones. The density of precipitates decreases in a certain degree and rod-like η＇ precipitates increase when Ce content is from 0.2% to 0.4% （mass fraction）.
基金Project(2008ZA11) supported by State Key Laboratory of Subtropical Building Science in South China University of Technology, ChinaProject(20080430815) supported by China Postdoctoral Science Foundation
文摘A series of researches were carried out for the soil samples in the Pearl River Delta under the action of consolidation loads,such as the quantitative analyses of the pore scale,shape and size distributions of micro-structure units,with an environmental scanning electron microscope (ESEM),a mercury intrusion analyzer and a mineral diffractometer. The experimental results show that the consolidation pressures remarkably change the pore sizes and distribution characteristics of the silt,thus changing its compressibility and permeability. This can be proved by the fact that,in the earlier stage with a consolidation pressure of p<200 kPa,the pore sizes are greater and the compressibility and permeability coefficients are larger. However,they rapidly decrease with the increase in consolidation pressure. And in the later stage with a consolidation pressure of p>200 kPa,the pore sizes are smaller and the compressibility and permeability coefficients are less. Therefore,the empirical formulas of compression coefficient and permeability coefficient vs consolidation load and average pore diameter are deduced.
基金Project(50804016)supported by the National Natural Science Foundation of China
文摘Fe/Si3N4 composite powder was synthesized by the heterogeneous precipitation-thermal reduction process,and then pressed into flakes under a pressure of 10 MPa.Flakes were sintered by pressureless and hot-pressing at 1 600℃under 0.1 MPa N2. The chemical composition,phases and microstructure of composite powder and sintered flakes were investigated by energy dispersive spectroscopy(EDS),X-ray diffraction(XRD),scanning electron microscopy(SEM)and transmission electron microscopy (TEM).The results show that the structure of composite powders is Si3N4 coated by nano Fe.The crystal phases of sintered flakes by pressureless are Fe(Si)compound,SiC and Si3N4.The crystal phases of the sintered samples by hot-pressing are Fe,Fe(Si) compound and Si3N4.It is found that crystal phases flakes obtained by pressureless and hot-pressing are very different.
基金Project(20876100) supported by the National Natural Science Foundation of ChinaProject(20090451176) supported by the China Post-doctoral Science Foundation+3 种基金Project(2009CB219904) supported by the National Basic Research Program of ChinaProjects(YJS0917,SG0978) supported by the Commission of Science and Technology of Suzhou MunicipalityProject(11C26223204581) supported by the Ministry of Science and TechnologyProject(BK2011328) supported by the Natural Science Foundation of Jiangsu Province,China
文摘In order to synthesize ZnO nanoparticles economically, industrial-grade zinc sulfate and urea were utilized to synthesize ZnO precursors in a stirred-tank reactor or a Teflon-lined autoclave at 100-180 ℃ under complete sealing condition. The ZnO precursors were calcined at 450 ℃ for 3 h to, synthesize ZnO nanoparticles. The composition of the precursors and the formation mechanism of ZnO were studied by thermogravimetric analysis and Fourier transform infrared spectroscopy. The results of X-ray diffraction, transmission electron microscopy and scanning electron microscopy of the ZnO powders demonstrate that high-purity zincite ZnO nanoparticles are synthesized. Orthogonal experiments were performed to find out the optimal conditions for the maximum yield and the minimum size. The ettect of temperature on the size ofZnO nanoparticles was investigated. The results show that a higher temperature is propitious to obtain smaller nanoparticles.
基金Project(2008A090300016) supported by the Key Science and Technology Item of Guangdong Province,ChinaProject(ZKJ2010022) supported by the Precious Apparatus Opening Center Foundation of Central South University,China
文摘Well-crystallized hexagonal hematite （α-Fe2O3） platelets were synthesized by hydrothermal process, using a highly concentrated ferric hydroxide as precursor. The precursor was prepared by adding ammonia to the ferric sulfate solution which was obtained by leaching pyrite cinders with sulfuric acid. Structure and morphology of the synthesized products were investigated by X-ray diffraction, scanning electron microscope, transmission electron microscope and selected area electron diffraction. The results reveal that the reaction temperature has significant effects on the structure, size and shape of the synthesized hematite particles. Typical hexagonal hematite platelets, about 0.4-0.6 μm in diameter and 0.1 μm in thickness, were prepared at 230 ℃ for 0.5 h. Al^3＋, contained in the sulfuric acid leaching solution as an impurity, plays an extremely important role in the formation of hexagonal hematite. In addition, a possible mechanism about the formation of hexagonal hematite platelets was proposed.
基金Project(2008WK2005) supported by the Science and Technology Plan of Hunan Province, China
文摘The effects of low temperature thermo-mechanical treatment （LTTMT） on microstructures and mechanical properties of Ti-6Al-4V （TC4） alloy were studied by optical microscopy （OM）, tensile test, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The experimental results confirm that the strength of TC4 alloy can be improved obviously by LTTMT processing, which combines strain strengthening with aging strengthening. The effect of LTTMT on the alloy depends on the microstructure of the refined and dispersed a＋fl phase on the basis of high dislocation density by pre-deformation below recrystallization temperature. The tensile strength decreases with the increase of pre-deformation reduction. The optimal processing parameters of LTTMT for TC4 alloy are as follows： solution treatment at 900 ℃ for 15 min, pre-deformation in the range of 600-700 ℃ with a reduction of 35%, finally aging at 540 ℃ for 4 h followed by air-cooling.
基金Project(2012CB619503)supported by the National Basic Research Program of ChinaProject(2013AH100055)supported by the Foshan Civic Technological Innovation Foundation,China
文摘The through-thickness corrosion inhomogeneity of 7050-T7451 Al alloy thick plate was studied using immersion tests, potentiodynamic polarization, electrochemical impedance spectroscopy(EIS), slow strain rate testing(SSRT) technique combined with optical microscopy(OM), scanning electron microscopy(SEM) and transmission electron microscopy(TEM). The results show that the through-thickness corrosion resistance is ranked in the order of T/2>surface>T/4. And the 75 mm-thick 7050 alloy plate presents better corrosion resistance than the 35 mm-thick plate. The results are discussed in terms of the combined effect of recrystallization and cooling rate in quenching. Alloy with lower volume fraction of recrystallization and smaller grain aspect ratio displays better corrosion resistance. The lower corrosion resistance caused by the slower cooling rate results from the higher coverage rate of grain boundary precipitates and larger width of precipitate free zone.
基金Project(2006CB600903) supported by the National Basic Research Program of China
文摘A novel carbon fiber pretreatment was proposed.Polyacrylonitrile(PAN)-based carbon fibers were first anodized in H3PO4 electrolyte to achieve an active surface,and then coated with Mo-B catalysts by immersed the carbon fibers in a uniformly dispersed Mo-B sol.The as-treated carbon fibers were then graphitized at 2 400 ℃ for 2 h.The structural changes were characterized by X-ray diffractometry(XRD),Raman spectroscopy,scanning electron microscopy(SEM) and high-resolution transmission electronic microscopy(HRTEM).The results show that much better graphitization can be achieved in the presence of Mo-B,with an interlayer spacing(d002) of 0.335 8 nm and a crystalline size(Lc) of 28 nm.
基金Project(51208102)supported by the National Natural Science Foundation of China
文摘Zn2GeO4 nanorods were prepared by a surfactant-assisted solution phase route.The as-prepared products were characterized by X-ray powder diffraction(XRD),scanning electron microscopy(SEM),high-resolution transmission electron microscopy(HRTEM),inductively coupled plasma atomic emission spectrometer(ICP-AES),UV-vis diffuse reflection spectroscopy and photoluminescence(PL) spectroscopy.The possible formation mechanism of Zn2GeO4 nanorods was discussed.It was supposed that the CTA+ cations preferentially adsorb on the planes of Zn2GeO4 nanorods,leading to preferential growth along the c-axis to form the Zn2GeO4 rods with larger aspect ratio and higher surface area,which showed the improved photocatalytic activity for photoreduction of CO2.The photoluminescence(PL) property of Zn2GeO4 nanorods was investigated through the emission spectra.
基金Project(2008A090300016) supported by Major Science & Technology Special Program of Guangdong Province,China
文摘Micaceous iron oxide （MIO） with a hexagonal flaky shape was prepared by hydrothermal method. The ferric hydroxide used as precursor was obtained by an acidic leaching solution of pyrite cinders reacting with ammonia solution. The optimal experimental conditions for preparing micaceous iron oxide were investigated by orthogonal experiments. Micaceous iron oxide can be successfully prepared when optimal parameters of total iron concentration of 2.0 mol/L, pH value of 8, n（Fe2＋）/n（Fe3＋） of 0.1, mass of seed crystal of 1 g, reaction temperature of 260 ℃ and reaction time of 30 min are applied. X-ray diffractometry （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and selected area electron diffractometry （SAEM） were adopted to characterize the hydrothermal products prepared under optimal conditions. The results indicate that highly crystallized α-Fe2O3 hexagonal flakes, about 1.0-1.5 μm in diameter and 0.1 μm in thickness, are prepared. Furthermore, the quality of micaceous iron oxide prepared can meet the required characteristics of micaceous iron oxide pigments for paints （ISO 10601--2007）.
基金Project(2012CB619503)supported by State Key Fundamental Research Program of China
文摘The strength, fracture toughness and fatigue crack growth resistance of 7050-T7451 aluminum alloy plate with different thicknesses （35 mm and 160 ram） were investigated by means of optical microscope, scanning electron microscope and transmission electron microscope. The results show that thicker plate has lower strength and fracture toughness but higher fatigue crack growth resistance, by comparison to the thinner plate. The drop of strength is mainly attributed to grain coarsening in the thicker plate, and the increased degree of recrystallization results in the loss of Kio However, the coarsened grains in the thicker plate make cracks deflected and closure effect enhanced due to surface roughness increased. For both of plates, in the fracture surface subjected plain strain, a transition from transgranular dimpled fracture to intergranular dimpled fracture is observed during the fracture process.
基金Projects(50871050, 50961009) supported by the National Natural Science Foundation of ChinaProject(2010ZD05) supported by the Natural Science Foundation of Inner Mongolia, ChinaProject(NJzy08071) supported by the Higher Education Science Research Project of Inner Mongolia, China
文摘In order to improve the electrochemical hydrogen storage performance of the Mg2Ni-type electrode alloys, Mg in the alloy was partially substituted by La, and the nanocrystalline and amorphous Mg2Ni-type Mg20-xLaxNi10 （x-=0, 2） alloys were synthesized by melt-spinning technique. The microstructures of the as-spun alloys were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The electrochemical hydrogen storage properties of the experimental alloys were tested. The results show that no amorphous phase is detected in the as-spun Mg20Ni10 alloy, but the as-spun Mg18La2Ni10 alloy holds a major amorphous phase. As La content increases from 0 to 2, the maximum discharge capacity of the as-spun （20 m/s） alloys rises from 96.5 to 387.1 mA.h/g, and the capacity retaining rate （S20） at the 20th cycle grows from 31.3% to 71.7%. Melt-spinning engenders an impactful effect on the electrochemical hydrogen storage performances of the alloys. With the increase in the spinning rate from 0 to 30 m/s, the maximum discharge capacity increases from 30.3 to 135.5 mA.h/g for the Mg20Ni10 alloy, and from 197.2 to 406.5 mA-h/g for the Mg18La2Ni10 alloy. The capacity retaining rate （S20） of the Mg2oNi10 alloy at the 20th cycle slightly falls from 36.7% to 27.1%, but it markedly mounts up from 37.3% to 78.3% for the Mg18La2Ni10 alloy.