A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O c...A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O crystal crystallizes in the monoclinic system, space group C2/m , with M=128.13, a =0\^994 7(2) nm, b =1.321 7(3) nm; c =0.463 6(1) nm; β=104.80(3)°, V =0.589 3(2) nm 3, Z=2, R=0.027 2 and wR =0.057 5. The network structure consists of vertex sharing which results in the formation of undulating 4 ring chains and 8 ring sheets.展开更多
开放骨架磷酸铝化合物是多孔晶体材料的一个重要家族。然而,这类材料的合成受到反应原料、凝胶组成、溶剂、模板剂、结晶温度和结晶时间等多个因素的影响。本文以吉林大学"无机制备与合成化学国家重点实验室"建立的开放骨架...开放骨架磷酸铝化合物是多孔晶体材料的一个重要家族。然而,这类材料的合成受到反应原料、凝胶组成、溶剂、模板剂、结晶温度和结晶时间等多个因素的影响。本文以吉林大学"无机制备与合成化学国家重点实验室"建立的开放骨架磷酸铝合成反应数据库为研究对象,采用最大权重最小冗余特征选择算法(Maximum weight and minimum redundancy,MWMR),在充分考虑合成参数自身的重要程度和合成参数之间的相关关系的前提下,分析了溶剂、模板剂等合成参数对于合成含有(8,6)元环结构开放骨架磷酸铝的影响。通过大量实验验证了该方法在开放骨架磷酸铝合成参数分析中的有效性,分析了合成参数对产物生成的影响。实验结果表明模板剂的几何参数、模板剂中C原子和N原子的个数比,溶剂的偶极距等参数可能对于该类结构的合成具有较为重要的影响。展开更多
A new sodium indium phosphate Na 6In 4[P 7O 24(OH) 5]·4H 2O was synthesized under a mild hydrothermal condition and its structure was determined by means of single-crystal X-ray diffraction methods. The title com...A new sodium indium phosphate Na 6In 4[P 7O 24(OH) 5]·4H 2O was synthesized under a mild hydrothermal condition and its structure was determined by means of single-crystal X-ray diffraction methods. The title compound crystallizes in a hexagonal system, space group P6 3, with a= 0.950 23(5) nm, b=0.950 23(5) nm, c=1.694 2(2) nm, α=90°, β=90°, γ=120°, V=1.324 8(2) nm 3, Z=8, structure refined to R=0.052 8 and wR=0.116 5 for 2 134 independent observed reflections. The three-dimensional network structure consists of helical chains formed by apex-sharing polyhedra. The connection of the chains results in 4- and 8-polyhedral rings and cages centered by three indium metal connecting oxygen atoms formed by three 4-rings. The three-connected oxygen atom is firstly observed in indium phosphate systems.展开更多
文摘A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O crystal crystallizes in the monoclinic system, space group C2/m , with M=128.13, a =0\^994 7(2) nm, b =1.321 7(3) nm; c =0.463 6(1) nm; β=104.80(3)°, V =0.589 3(2) nm 3, Z=2, R=0.027 2 and wR =0.057 5. The network structure consists of vertex sharing which results in the formation of undulating 4 ring chains and 8 ring sheets.
文摘开放骨架磷酸铝化合物是多孔晶体材料的一个重要家族。然而,这类材料的合成受到反应原料、凝胶组成、溶剂、模板剂、结晶温度和结晶时间等多个因素的影响。本文以吉林大学"无机制备与合成化学国家重点实验室"建立的开放骨架磷酸铝合成反应数据库为研究对象,采用最大权重最小冗余特征选择算法(Maximum weight and minimum redundancy,MWMR),在充分考虑合成参数自身的重要程度和合成参数之间的相关关系的前提下,分析了溶剂、模板剂等合成参数对于合成含有(8,6)元环结构开放骨架磷酸铝的影响。通过大量实验验证了该方法在开放骨架磷酸铝合成参数分析中的有效性,分析了合成参数对产物生成的影响。实验结果表明模板剂的几何参数、模板剂中C原子和N原子的个数比,溶剂的偶极距等参数可能对于该类结构的合成具有较为重要的影响。
文摘A new sodium indium phosphate Na 6In 4[P 7O 24(OH) 5]·4H 2O was synthesized under a mild hydrothermal condition and its structure was determined by means of single-crystal X-ray diffraction methods. The title compound crystallizes in a hexagonal system, space group P6 3, with a= 0.950 23(5) nm, b=0.950 23(5) nm, c=1.694 2(2) nm, α=90°, β=90°, γ=120°, V=1.324 8(2) nm 3, Z=8, structure refined to R=0.052 8 and wR=0.116 5 for 2 134 independent observed reflections. The three-dimensional network structure consists of helical chains formed by apex-sharing polyhedra. The connection of the chains results in 4- and 8-polyhedral rings and cages centered by three indium metal connecting oxygen atoms formed by three 4-rings. The three-connected oxygen atom is firstly observed in indium phosphate systems.