In this work, through the comparison analysis with the results of the thermogravimetry-differential scanning calorimetry-mass spectrometry (TG-DSC-MS) coupling techniques for the three organic additive and aqueous tap...In this work, through the comparison analysis with the results of the thermogravimetry-differential scanning calorimetry-mass spectrometry (TG-DSC-MS) coupling techniques for the three organic additive and aqueous tape casting aluminum nitride in air and nitrogen atmosphere, it can be found that the plasticity glycerol was almost burnout before 350℃ in two atmosphere; the binder PVA124 was almost burnout before 600℃ in air, there was little left in nitrogen; The mass losses of the dispersant DP270 in air and nitrogen atmosphere were about 73.32% and 65.51% before 600℃ ; The mass losses of the aqueous tape casting aluminum nitride in air (14.08%) were higher that in nitrogen (10.75%) before 600℃. It can be concluded that the organic additive burnout of the aqueous tape casting aluminum nitride in air atmosohere was better than in nitrogen atmosphere.展开更多
The effects of alkali oxides （Na2O and K2O addition on both the sintering behavior and dielectric properties of Ca-AI-B-Si-O glass/Al2O3 composites were investigated by Fourier transform infrared spectroscopy （FTIR...The effects of alkali oxides （Na2O and K2O addition on both the sintering behavior and dielectric properties of Ca-AI-B-Si-O glass/Al2O3 composites were investigated by Fourier transform infrared spectroscopy （FTIR）, differential scanning calorimeter （DSC）, X-ray diffractometry （XRD） and scanning electron microscopy （SEM）. The results show that the increasing amount of alkali oxides in the glass causes the decrease of [SiO4], which results in the decrease of the continuity of glass network, and leads to the decrease of the softening temperature Tf of the samples and the increasing trend of crystallization. And that deduces corresponding rise of densification, dielectric constant, dielectric loss of the low temperature co-fired ceramic （LTCC） materials and the decrease of its thermal conductivity. By contrast, the borosilicate glass/A1203 composites with 1.5% （mass fraction） alkali oxides sintered at 875 ℃ for 30 rain exhibit better properties of a bulk density of 2.79 g/cm3, a porosity of 0.48%, a 2 value of 2.28 W/（m.K）, a er value of 7.82 and a tand value of 9.1 × 10-4 （measured at 10 MHz）.展开更多
Mechanical properties and microstructures of Al-Li-Cu-Mg-Ag alloy after solution treatments were investigated by means of optical microscopy （OM）, tensile test, hardness measurement and electrical conductivity test,...Mechanical properties and microstructures of Al-Li-Cu-Mg-Ag alloy after solution treatments were investigated by means of optical microscopy （OM）, tensile test, hardness measurement and electrical conductivity test, differential scanning calorimetric （DSC）, energy dispersive X-ray （EDX）, scanning electron microscopy （SEM） and transition electron microscopy （TEM）, respectively The results show that both tensile strength and hardness increase first and then decrease with temperature at constant holding time of 30 min with maximum strength and hardness appearing at 520 ℃. Tensile strength, hardness and elongation of samples treated at 520 ℃ for 30 min are 566 MPa （σb）, 512 MPa （σ0.2）, HB 148 and 8.23% （δ）, respectively. There are certain amount of fine T1 （AI2CuLi） phase dispersing among AI substrates according to TEM images. This may result in mixed fracture morphology with trans-granular and inter-granular delamination cracks observed in SEM images.展开更多
Using novolac phenolic resin, aniline and formaldehyde as raw materials, benzoxazine-phenolic copolymers with different percentages of benzoxazine rings were prepared. FT-IR was adopted to characterize the molecular s...Using novolac phenolic resin, aniline and formaldehyde as raw materials, benzoxazine-phenolic copolymers with different percentages of benzoxazine rings were prepared. FT-IR was adopted to characterize the molecular structure of the novolac-type phenolic resin and the benzoxazine-phenolic copolymer BP31. In order to understand the curing process of the copolymers, the curing behavior and curing kinetic characteristics were studied by differential scanning calorimetry （DSC）, and the catalytical effect of phenolic hydroxyl on the curing behavior of copolymers was investigated. To investigate the thermal properties of this resin, the thermal degradation behaviors of the cured samples were studied by thermal gravimetric （TG） method, and glass-transition temperatures （Tg） of the cured copolymers were also evaluated by DSC. The dynamic Ozawa method was adopted to determine the kinetic parameters of the curing process as well. The activation energy is 78.8 kJ/mol and the reaction rate constant is in the range from 40.0 to 5.2 （K/min）＂ according to reaction temperatures. The Ozawa exponent decreases from 2.4 to 0.7 with the increase of reaction temperature, and curing mechanism is expounded briefly according to the results. TG result shows that the highest char yield of copolymers is 50.3%. The highest Tg of copolymers is 489 K, which is much higher than that of pure benzoxazine resin.展开更多
Sodium fluoride and high specific area silica were synthesized by using sodium hexafluorosilicate(Na2Si F6) and sodium carbonate decahydrate(Na2CO3·10H2O). The influencing factors of react temperature, contact ti...Sodium fluoride and high specific area silica were synthesized by using sodium hexafluorosilicate(Na2Si F6) and sodium carbonate decahydrate(Na2CO3·10H2O). The influencing factors of react temperature, contact time, sodium dodecyl sulfate(SDS) and molar ratio of Na2 Si F6 to Na2CO3·10H2O were investigated. The optimum process involves the reaction of 0.075 mol Na2 Si F6 and 150 m L, 0.225 mol Na2CO3·10H2O(molar ratio of 1:3) at 85 °C for 90 min, and 2.0×10-3 mol sodium dodecyl sulfate(SDS) as additive. The results show that the purities of Si O2 and Na F at extraction yields of 96.5% and 98.0% are 91.0% and 98.6%, respectively. The obtained Si O2 were characterized by X-ray diffraction(XRD), scanning electron microscope(SEM), Fourier transform infrared ray(FTIR), differential scanning calorimetry and thermogravimetric analysis(DSC-TGA), N2 absorption/desorption(BET) and laser particle size analyzer. The result demonstrates that Si O2 particles have a high BET surface area of 103 m2/g, and a mean grain size of 985 nm.展开更多
A simple hydrothermal process followed by heat treatment was applied to the preparation of spinel Li1.05Mn1.95O4. In this process, electrolytic manganese dioxide(EMD) and LiOH·H2O were used as starting materials....A simple hydrothermal process followed by heat treatment was applied to the preparation of spinel Li1.05Mn1.95O4. In this process, electrolytic manganese dioxide(EMD) and LiOH·H2O were used as starting materials. The physiochemical properties of the synthesized samples were investigated by thermogravimetry-differential scanning calorimetry(TG-DSC), X-ray diffractometry(XRD), and scanning electronic microscopy(SEM). The results show that the hydrothermally synthesized precursor is an essential amorphous. The precursor can be easily transferred to spinel powders with a homogeneous structure and a regularly-shaped morphology by heat treatment. Li1.05Mn1.95O4 powder obtained by heat treating the precursor at 430 °C for 12 h and then calcining at 800 °C for 12 h shows an excellent cycling performance with an initial charge capacity of 118.2 mA·h·g-1 obtained at 0.5C rate and 93.8% of its original value retained after 100 cycles.展开更多
The drawn copper wires have been analyzed by differential scanning calorimeter(DSC) and a new method, which uses DSC measurements to determine the Johnson-Mehl-Avrami-Kolmogorov(JMAK) exponent via introducing Arrheniu...The drawn copper wires have been analyzed by differential scanning calorimeter(DSC) and a new method, which uses DSC measurements to determine the Johnson-Mehl-Avrami-Kolmogorov(JMAK) exponent via introducing Arrhenius behavior and modifying the baseline of DSC curves, has been proposed. The results show that JMAK exponent and recrystallization activation energy of the drawn copper wires with a strain of 2.77 are about 2.39 and 125 k J/mol, respectively. The line linking the tangency points of DSC curve hypotenuse can be used as the baseline when calculating recrystallization fraction. The JMAK exponent obtained by the DSC method is in a good agreement with that obtained by microhardness measurements. Compared to traditional methods to measure the exponent, the proposed method is faster and less labor intensive.展开更多
The mechanical properties and cutting performance of the designed Cu Al Mn Zn Ti B shape memory alloy were studied by tensile test and microstructure observation. Using X-ray diffractometry, differential scanning calo...The mechanical properties and cutting performance of the designed Cu Al Mn Zn Ti B shape memory alloy were studied by tensile test and microstructure observation. Using X-ray diffractometry, differential scanning calorimetry(DSC) and semi-quantitative shape memory effect test, the microstructure and shape memory effect were analyzed. It is found that lots of βphase and few α phase are formed in the quenching of Cu-7.5Al-9.7Mn-3.4Zn-0.3Ti-0.14B(mass fraction, %) alloy, a great deal of martensite and few α phase are formed in the aging alloy, while the annealing alloy is composed of a great deal of α phase and few βphase. The tensile strength and elongation of the annealed alloy are 649 MPa and 17.1%, respectively. Some tiny and dispersion distributed second phase particles are generated in Ti and B precipitates, greatly improving the alloy machinability.展开更多
文摘In this work, through the comparison analysis with the results of the thermogravimetry-differential scanning calorimetry-mass spectrometry (TG-DSC-MS) coupling techniques for the three organic additive and aqueous tape casting aluminum nitride in air and nitrogen atmosphere, it can be found that the plasticity glycerol was almost burnout before 350℃ in two atmosphere; the binder PVA124 was almost burnout before 600℃ in air, there was little left in nitrogen; The mass losses of the dispersant DP270 in air and nitrogen atmosphere were about 73.32% and 65.51% before 600℃ ; The mass losses of the aqueous tape casting aluminum nitride in air (14.08%) were higher that in nitrogen (10.75%) before 600℃. It can be concluded that the organic additive burnout of the aqueous tape casting aluminum nitride in air atmosohere was better than in nitrogen atmosphere.
基金Project(2007AA03Z0455) supported by the National High Technology Research and Development Program ("863" Program) of ChinaProject(BE2010194) supported by Science & Technology Pillar Program of Jiangsu in China+3 种基金Project(BE2009168) supported by Science & Technology Pillar Program of Jiangsu in ChinaProject supported by the Priority Academic Program Development (PAPD) of Jiangsu Higher Education InstitutionsProject(KF201103) supported by State Key Laboratory of New Ceramic and Fine Processing Tsinghua UniversityProject(CXZZ12_0415) supported by Innovation Foundation for Graduate Students of Jiangsu Province,China
文摘The effects of alkali oxides （Na2O and K2O addition on both the sintering behavior and dielectric properties of Ca-AI-B-Si-O glass/Al2O3 composites were investigated by Fourier transform infrared spectroscopy （FTIR）, differential scanning calorimeter （DSC）, X-ray diffractometry （XRD） and scanning electron microscopy （SEM）. The results show that the increasing amount of alkali oxides in the glass causes the decrease of [SiO4], which results in the decrease of the continuity of glass network, and leads to the decrease of the softening temperature Tf of the samples and the increasing trend of crystallization. And that deduces corresponding rise of densification, dielectric constant, dielectric loss of the low temperature co-fired ceramic （LTCC） materials and the decrease of its thermal conductivity. By contrast, the borosilicate glass/A1203 composites with 1.5% （mass fraction） alkali oxides sintered at 875 ℃ for 30 rain exhibit better properties of a bulk density of 2.79 g/cm3, a porosity of 0.48%, a 2 value of 2.28 W/（m.K）, a er value of 7.82 and a tand value of 9.1 × 10-4 （measured at 10 MHz）.
基金Foundation item： Project（6140506） supported by GAD （General Armament Department）, China
文摘Mechanical properties and microstructures of Al-Li-Cu-Mg-Ag alloy after solution treatments were investigated by means of optical microscopy （OM）, tensile test, hardness measurement and electrical conductivity test, differential scanning calorimetric （DSC）, energy dispersive X-ray （EDX）, scanning electron microscopy （SEM） and transition electron microscopy （TEM）, respectively The results show that both tensile strength and hardness increase first and then decrease with temperature at constant holding time of 30 min with maximum strength and hardness appearing at 520 ℃. Tensile strength, hardness and elongation of samples treated at 520 ℃ for 30 min are 566 MPa （σb）, 512 MPa （σ0.2）, HB 148 and 8.23% （δ）, respectively. There are certain amount of fine T1 （AI2CuLi） phase dispersing among AI substrates according to TEM images. This may result in mixed fracture morphology with trans-granular and inter-granular delamination cracks observed in SEM images.
基金Project (20050106) supported by the Key Science and Technology Item of Guangdong Province,China
文摘Using novolac phenolic resin, aniline and formaldehyde as raw materials, benzoxazine-phenolic copolymers with different percentages of benzoxazine rings were prepared. FT-IR was adopted to characterize the molecular structure of the novolac-type phenolic resin and the benzoxazine-phenolic copolymer BP31. In order to understand the curing process of the copolymers, the curing behavior and curing kinetic characteristics were studied by differential scanning calorimetry （DSC）, and the catalytical effect of phenolic hydroxyl on the curing behavior of copolymers was investigated. To investigate the thermal properties of this resin, the thermal degradation behaviors of the cured samples were studied by thermal gravimetric （TG） method, and glass-transition temperatures （Tg） of the cured copolymers were also evaluated by DSC. The dynamic Ozawa method was adopted to determine the kinetic parameters of the curing process as well. The activation energy is 78.8 kJ/mol and the reaction rate constant is in the range from 40.0 to 5.2 （K/min）＂ according to reaction temperatures. The Ozawa exponent decreases from 2.4 to 0.7 with the increase of reaction temperature, and curing mechanism is expounded briefly according to the results. TG result shows that the highest char yield of copolymers is 50.3%. The highest Tg of copolymers is 489 K, which is much higher than that of pure benzoxazine resin.
文摘Sodium fluoride and high specific area silica were synthesized by using sodium hexafluorosilicate(Na2Si F6) and sodium carbonate decahydrate(Na2CO3·10H2O). The influencing factors of react temperature, contact time, sodium dodecyl sulfate(SDS) and molar ratio of Na2 Si F6 to Na2CO3·10H2O were investigated. The optimum process involves the reaction of 0.075 mol Na2 Si F6 and 150 m L, 0.225 mol Na2CO3·10H2O(molar ratio of 1:3) at 85 °C for 90 min, and 2.0×10-3 mol sodium dodecyl sulfate(SDS) as additive. The results show that the purities of Si O2 and Na F at extraction yields of 96.5% and 98.0% are 91.0% and 98.6%, respectively. The obtained Si O2 were characterized by X-ray diffraction(XRD), scanning electron microscope(SEM), Fourier transform infrared ray(FTIR), differential scanning calorimetry and thermogravimetric analysis(DSC-TGA), N2 absorption/desorption(BET) and laser particle size analyzer. The result demonstrates that Si O2 particles have a high BET surface area of 103 m2/g, and a mean grain size of 985 nm.
基金Project(50174058)supported by the National Natural Science Foundation of ChinaProject(2011A025)supported by the Glorious Laurel Scholar Program of Guangxi Zhuang Autonomous Region,China
文摘A simple hydrothermal process followed by heat treatment was applied to the preparation of spinel Li1.05Mn1.95O4. In this process, electrolytic manganese dioxide(EMD) and LiOH·H2O were used as starting materials. The physiochemical properties of the synthesized samples were investigated by thermogravimetry-differential scanning calorimetry(TG-DSC), X-ray diffractometry(XRD), and scanning electronic microscopy(SEM). The results show that the hydrothermally synthesized precursor is an essential amorphous. The precursor can be easily transferred to spinel powders with a homogeneous structure and a regularly-shaped morphology by heat treatment. Li1.05Mn1.95O4 powder obtained by heat treating the precursor at 430 °C for 12 h and then calcining at 800 °C for 12 h shows an excellent cycling performance with an initial charge capacity of 118.2 mA·h·g-1 obtained at 0.5C rate and 93.8% of its original value retained after 100 cycles.
基金Projects(51171135,51371132,51471123) supported by the National Natural Science Foundation of ChinaProjects(2012K07-08,2013KJXX-61) supported by Key Science and Technology Program of Shaanxi Province,ChinaProject(2013JC14) supported by the Education Department Foundation of Shaanxi Province,China
文摘The drawn copper wires have been analyzed by differential scanning calorimeter(DSC) and a new method, which uses DSC measurements to determine the Johnson-Mehl-Avrami-Kolmogorov(JMAK) exponent via introducing Arrhenius behavior and modifying the baseline of DSC curves, has been proposed. The results show that JMAK exponent and recrystallization activation energy of the drawn copper wires with a strain of 2.77 are about 2.39 and 125 k J/mol, respectively. The line linking the tangency points of DSC curve hypotenuse can be used as the baseline when calculating recrystallization fraction. The JMAK exponent obtained by the DSC method is in a good agreement with that obtained by microhardness measurements. Compared to traditional methods to measure the exponent, the proposed method is faster and less labor intensive.
基金Project(51271203)supported by the National Natural Science Foundation of ChinaProject(CX2012B037)supported by Hunan Provincial Innovation Foundation for Postgraduate,China+1 种基金Project(2013zzts017)supported by the Graduate Degree Thesis Innovation Foundation of Central South University,ChinaProject(2012bjjxj015)supported by the Excellent Doctor Degree Thesis Support Foundation of Central South University,China
文摘The mechanical properties and cutting performance of the designed Cu Al Mn Zn Ti B shape memory alloy were studied by tensile test and microstructure observation. Using X-ray diffractometry, differential scanning calorimetry(DSC) and semi-quantitative shape memory effect test, the microstructure and shape memory effect were analyzed. It is found that lots of βphase and few α phase are formed in the quenching of Cu-7.5Al-9.7Mn-3.4Zn-0.3Ti-0.14B(mass fraction, %) alloy, a great deal of martensite and few α phase are formed in the aging alloy, while the annealing alloy is composed of a great deal of α phase and few βphase. The tensile strength and elongation of the annealed alloy are 649 MPa and 17.1%, respectively. Some tiny and dispersion distributed second phase particles are generated in Ti and B precipitates, greatly improving the alloy machinability.