Octa(tetramethylammonium)-polyhedral oligomeric silsesquioxane(TMA-POSS) with cage-like structure was synthesized, the structure was characterized by NMR, FTIR and Elemental analyses. The mesoporous silica was prepare...Octa(tetramethylammonium)-polyhedral oligomeric silsesquioxane(TMA-POSS) with cage-like structure was synthesized, the structure was characterized by NMR, FTIR and Elemental analyses. The mesoporous silica was prepared under alkaline condition using TMA-POSS as the silicon source and hexadecyltrimethylammonium bromide (CTAB) as the template, the structures of these products were characterized by XRD, TEM and nitrogen adsorption and desorption methods. The results indicate that the synthesized silica exhibites a well-ordered hexagonal pore structure with larger specific surface area. With increasing of CTAB molar ratio, the spacing of the crystal plane d100 is increased. The effects of the pH values on the mesoporous structure in the reaction system with different molar ratio of nPOSS / nCTAB were investigated. The synthesis mechanism of mesoporous silica was also discussed.展开更多
文摘Octa(tetramethylammonium)-polyhedral oligomeric silsesquioxane(TMA-POSS) with cage-like structure was synthesized, the structure was characterized by NMR, FTIR and Elemental analyses. The mesoporous silica was prepared under alkaline condition using TMA-POSS as the silicon source and hexadecyltrimethylammonium bromide (CTAB) as the template, the structures of these products were characterized by XRD, TEM and nitrogen adsorption and desorption methods. The results indicate that the synthesized silica exhibites a well-ordered hexagonal pore structure with larger specific surface area. With increasing of CTAB molar ratio, the spacing of the crystal plane d100 is increased. The effects of the pH values on the mesoporous structure in the reaction system with different molar ratio of nPOSS / nCTAB were investigated. The synthesis mechanism of mesoporous silica was also discussed.
基金financial support from the National Natural Science Foundation of China (Grant No.51502285)National Natural Science Foundation for Creative Research Group (Grant No.21701047)+2 种基金National Basic Research Program of China (Grant No.21521092)the Science and Technology Development of Jilin Province of China (Grant No.20180520191JH)the Thirteenth FiveYear Program for Science and Technology of the Education Department of Jilin Province (Grant No.JJKH20191024KJ)~~