[SiO2/FePt]5/Ag thin films were deposited by RF magnetron sputtering on the glass substrates and post annealing at 550 ℃ for 30 min in vacuum. Vibrating sample magnetometer and X-ray diffraction analyser were applied...[SiO2/FePt]5/Ag thin films were deposited by RF magnetron sputtering on the glass substrates and post annealing at 550 ℃ for 30 min in vacuum. Vibrating sample magnetometer and X-ray diffraction analyser were applied to study the magnetic properties and microstructures of the films. The results show that without Ag underlayer [SiO2/FePt]5 films deposited onto the glass are FCC disordered; with the addition of Ag underlayer [SiO]FePt]5/Ag films are changed into L10 and （111） mixed texture. The variation of the SiO2 nonmagnetic layer thickness in [SiO2/FePt]5/Ag films indicates that SiO2-doping plays an important role in improving the order parameter and the perpendicular magnetic anisotropy, and reducing the grain size and intergrain interactions. By controlling SiO2 thickness the highly perpendicular magnetic anisotropy can be obtained in the [SiO2 （0.6 nm）/FePt （3 nm）]5/Ag （50 nm） films and highly （001）-oriented films can be obtained in the [SiO2 （2 nm）/FePt （3 nm）]5/Ag （50 nm） films.展开更多
The Nd Fe B/Co multilayer films were prepared by magnetron sputtering. After that, the samples were annealed at 600 ℃ for 20 min. The surface morphology, phase structures and magnetic properties of Mo（50 nm）/[Nd F...The Nd Fe B/Co multilayer films were prepared by magnetron sputtering. After that, the samples were annealed at 600 ℃ for 20 min. The surface morphology, phase structures and magnetic properties of Mo（50 nm）/[Nd Fe B（100 nm）/Co（y）]×10/Mo（50 nm） thin films were researched by AFM, XRD and VSM, respectively. The results show that the films show stronger perpendicular magnetic anisotropy. When the thickness of Co layers is 10 nm, the coercivity Hc⊥ is the maximum, 295 k A/m. However, for y=10-20, the reduced remanence M/Ms of films has increased. When the thickness of Co layers is 20-30 nm, the Nd Fe B/Co multilayer films obtained more superior magnetic properties with M/Ms =0.95.展开更多
基金Project(10574085) supported by the National Natural Science Foundation of ChinaProject(207020) supported by the Science Technology Key Project of the Ministry of Education, China
文摘[SiO2/FePt]5/Ag thin films were deposited by RF magnetron sputtering on the glass substrates and post annealing at 550 ℃ for 30 min in vacuum. Vibrating sample magnetometer and X-ray diffraction analyser were applied to study the magnetic properties and microstructures of the films. The results show that without Ag underlayer [SiO2/FePt]5 films deposited onto the glass are FCC disordered; with the addition of Ag underlayer [SiO]FePt]5/Ag films are changed into L10 and （111） mixed texture. The variation of the SiO2 nonmagnetic layer thickness in [SiO2/FePt]5/Ag films indicates that SiO2-doping plays an important role in improving the order parameter and the perpendicular magnetic anisotropy, and reducing the grain size and intergrain interactions. By controlling SiO2 thickness the highly perpendicular magnetic anisotropy can be obtained in the [SiO2 （0.6 nm）/FePt （3 nm）]5/Ag （50 nm） films and highly （001）-oriented films can be obtained in the [SiO2 （2 nm）/FePt （3 nm）]5/Ag （50 nm） films.
文摘The Nd Fe B/Co multilayer films were prepared by magnetron sputtering. After that, the samples were annealed at 600 ℃ for 20 min. The surface morphology, phase structures and magnetic properties of Mo（50 nm）/[Nd Fe B（100 nm）/Co（y）]×10/Mo（50 nm） thin films were researched by AFM, XRD and VSM, respectively. The results show that the films show stronger perpendicular magnetic anisotropy. When the thickness of Co layers is 10 nm, the coercivity Hc⊥ is the maximum, 295 k A/m. However, for y=10-20, the reduced remanence M/Ms of films has increased. When the thickness of Co layers is 20-30 nm, the Nd Fe B/Co multilayer films obtained more superior magnetic properties with M/Ms =0.95.