Micro arc oxidation(MAO) and electrophoretic deposition(EPD) process are employed to fabricate a dense coating on magnesium alloy to protect it from corrosion in engineering application. The EPD film changes the dampi...Micro arc oxidation(MAO) and electrophoretic deposition(EPD) process are employed to fabricate a dense coating on magnesium alloy to protect it from corrosion in engineering application. The EPD film changes the damping characteristic of magnesium alloy, and both the MAO and EPD process change the bending stiffness of samples being treated. Damping loss factor(DLF) test and sound transmission experiments were carried out for AZ31 B magnesium alloy with coating fabricated by MAO and EPD processes. The results indicate that DLF is improved in frequency range from 0-850 Hz. Bending stiffness of the samples is improved with MAO and EPD treatment. As a result, the sound transmission loss(LST) is improved in the stiffness control stage of the sound transmission verse frequency curve. To the samples by electrophoresis process, the LST is improved in frequency range from 2500-3200 Hz, because the damping loss factor is improved with EPD process. The results are useful for the surface treatment to enhance the damping loss factor, LST and widespread application of magnesium alloy while improving the corrosion resistance.展开更多
基金Project(2011BAE22B05)supported by National Technology R&D Program in the 12th Five year Plan of ChinaProject(2011DFA50900)supported by the Canada-China-USA Collaborative Research&Development ProjectProject(51071121)supported by the National Natural Science Foundation of China
文摘Micro arc oxidation(MAO) and electrophoretic deposition(EPD) process are employed to fabricate a dense coating on magnesium alloy to protect it from corrosion in engineering application. The EPD film changes the damping characteristic of magnesium alloy, and both the MAO and EPD process change the bending stiffness of samples being treated. Damping loss factor(DLF) test and sound transmission experiments were carried out for AZ31 B magnesium alloy with coating fabricated by MAO and EPD processes. The results indicate that DLF is improved in frequency range from 0-850 Hz. Bending stiffness of the samples is improved with MAO and EPD treatment. As a result, the sound transmission loss(LST) is improved in the stiffness control stage of the sound transmission verse frequency curve. To the samples by electrophoresis process, the LST is improved in frequency range from 2500-3200 Hz, because the damping loss factor is improved with EPD process. The results are useful for the surface treatment to enhance the damping loss factor, LST and widespread application of magnesium alloy while improving the corrosion resistance.