Textile reinforced concrete(TRC)has good bearing capacity,crack resistance and corrosion resistance and it is suitable for repairing and reinforcing concrete structures in harsh marine environments.The four-point bend...Textile reinforced concrete(TRC)has good bearing capacity,crack resistance and corrosion resistance and it is suitable for repairing and reinforcing concrete structures in harsh marine environments.The four-point bending method was used to analyze the influence of the salt concentration,the damage degree and the coupled effect of the environment and load on the bending performance of TRC-strengthened beams with a secondary load.The results showed that as the salt concentration increased,the crack width and mid-span deflection of the beam quickly increased,and its bearing capacity decreased.As the damage degree increased,the early-stage crack development and mid-span deflection of the beam were less affected and the ultimate bearing capacity significantly decreased.In addition,the coupled effect of the environment and load on the beams with a secondary load was significant.As the sustained load increased,the ultimate bearing capacity of the strengthened beam decreased,and cracks developed faster in the later stage.In addition,the mid-span deflection of the beam decreased at the same load level because of the influence of the initial deflection due to the sustained load corrosion.展开更多
Textile-reinforced concrete(TRC)is suitable to repair and reinforce concrete structures in harsh environments.The performance of the interface between TRC and existing concrete is an important factor in determining th...Textile-reinforced concrete(TRC)is suitable to repair and reinforce concrete structures in harsh environments.The performance of the interface between TRC and existing concrete is an important factor in determining the strengthening effect of TRC.In this paper,a double-sided shear test was performed to investigate the effects of the chloride dry-wet cycles on the average shear strength and slip at the interface between the TRC and existing concrete,also considering the existing concrete strength,bond length,textile layer and short-cut fiber arrangements.In addition,X-ray diffraction(XRD)technology was used to analyze the microscopic matter at the interface in the corrosive environment.The experimental results indicate that the interface performance between TRC and existing concrete would decrease with continued chloride dry-wet cycles.Compared with the specimen with a single layer of textile reinforcement,the specimens with two layers of textile with added PVA or AR-glass short-cut fibers could further improve the properties of the interface between the TRC layer and existing concrete.For the TRC with a single layer of textile,the average shear strength tended to decrease with increasing bond length.In addition,the strength grade of the existing concrete had a minor effect on the interface properties.展开更多
Reinforcement inside the concrete is protected from corrosion and its damages until several years after the construction. After corrosion initiation, the cross section of reinforcement begins to reduce and often load ...Reinforcement inside the concrete is protected from corrosion and its damages until several years after the construction. After corrosion initiation, the cross section of reinforcement begins to reduce and often load bearing of the reinforced concrete structure will be reduced significantly. Corrosion of reinforcements in concrete in polluted and contaminated areas can occur in two ways: chloride and carbonation. In this work, meta-heuristic approach of charged system search(CSS) is used to calculate corrosion occurrence probability due to chloride ions penetration. The model efficiency is verified by comparing the available examples in technical literature and results of Monte Carlo analysis. According to the analyses performed, using different probabilistic distributions regardless of probabilistic moments based on real distribution leads to diverse results. In addition, influence of each effective parameter in corrosion occurrence varies by changing other parameters.展开更多
This article presents an experimental study on the flexural performance of reinforced concrete(RC)beams with fiber reinforced cementitious composites(FRCC)and hybrid fiber reinforced cementitious composites(HFRCC)in t...This article presents an experimental study on the flexural performance of reinforced concrete(RC)beams with fiber reinforced cementitious composites(FRCC)and hybrid fiber reinforced cementitious composites(HFRCC)in the hinge portion.Beam specimens with moderate confinement were used in the study and tested under monotonic loading.Seven diverse types of FRCC including hybrid composites using fibers in different profiles and in different volumes are employed in this study.Companion specimens such as cylindrical specimens and prism specimens are also used to study the physical properties of composites employed.The moment?curvature,stiffness behavior,ductility,crack pattern and modified flexural damage ratio are the main factors considered in this study to observe the efficacy of the employed hybrid composites.The experimental outputs demonstrate the improved post yield behavior with less rate of stiffness degradation and better damage tolerance capacity than conventional technique.展开更多
Combining fiber reinforced polymer(FRP)with seawater sea-sand concrete(SSC)can solve the shortage of river sand that will be used for marine engineering construction.The bond performance of BFRP bars and SSC specimens...Combining fiber reinforced polymer(FRP)with seawater sea-sand concrete(SSC)can solve the shortage of river sand that will be used for marine engineering construction.The bond performance of BFRP bars and SSC specimens is researched by pull-out test in this paper.The effects of the parameters,such as bar type,bar diameter,concrete type and stirrup restraint,are considered.It is beneficial to the bonding performance by the reduction of bar diameter.The utilization of seawater sea-sand has a low influence on the bond properties of concrete.The bond strength of BFRP is slightly lower than the steel rebar,but the difference is relatively small.The failure mode of the specimen can be changed and the interfacial bond stress can be improved by stirrups restraint.The bond-slip curves of BFRP ribbed rebar include micro slip stage,slip stage,descent stage and residual stage.The bond stress shows the cycle attenuation pattern of sine in the residual stage.In addition,the bond-slip model of BFRP and SSC is obtained according to the experimental results and related literature,while the predicted curve is also consistent well with the measured curve.展开更多
Rehabilitation of existing structures with fiber reinforced plastic(FRP)has been growing in popularity because they offer superior performance in terms of resistance to corrosion and high specific stiffness.The strain...Rehabilitation of existing structures with fiber reinforced plastic(FRP)has been growing in popularity because they offer superior performance in terms of resistance to corrosion and high specific stiffness.The strain coordination results of 34 reinforced concrete beams(four groups)strengthened with different methods were presented including external-bonded or near-surface mounted glass or carbon FRP or helical rib bar in order to study the strain coordination of the strengthening materials and steel rebar of RC beam.Because there is relative slipping between concrete and strengthening materials(SM),the strain of SM and steel rebar of RC beam satisfies the double linear strain distribution assumption,that is,the strain of longitudinal fiber parallel to the neutral axis of plated beam within the scope of effective height(h0)of the cross section is in direct proportion to the distance from the fiber to the neutral axis.The strain of SM and steel rebar satisfies the equation εGCH=βεsteel,where the value of β is equal to 1.1-1.3 according to the test results.展开更多
基金Project(2017XKZD09)supported by the Fundamental Research Funds for the Central Universities,China
文摘Textile reinforced concrete(TRC)has good bearing capacity,crack resistance and corrosion resistance and it is suitable for repairing and reinforcing concrete structures in harsh marine environments.The four-point bending method was used to analyze the influence of the salt concentration,the damage degree and the coupled effect of the environment and load on the bending performance of TRC-strengthened beams with a secondary load.The results showed that as the salt concentration increased,the crack width and mid-span deflection of the beam quickly increased,and its bearing capacity decreased.As the damage degree increased,the early-stage crack development and mid-span deflection of the beam were less affected and the ultimate bearing capacity significantly decreased.In addition,the coupled effect of the environment and load on the beams with a secondary load was significant.As the sustained load increased,the ultimate bearing capacity of the strengthened beam decreased,and cracks developed faster in the later stage.In addition,the mid-span deflection of the beam decreased at the same load level because of the influence of the initial deflection due to the sustained load corrosion.
基金Project(2017XKZD09)supported by the Fundamental Research Funds for the Central Universities,China。
文摘Textile-reinforced concrete(TRC)is suitable to repair and reinforce concrete structures in harsh environments.The performance of the interface between TRC and existing concrete is an important factor in determining the strengthening effect of TRC.In this paper,a double-sided shear test was performed to investigate the effects of the chloride dry-wet cycles on the average shear strength and slip at the interface between the TRC and existing concrete,also considering the existing concrete strength,bond length,textile layer and short-cut fiber arrangements.In addition,X-ray diffraction(XRD)technology was used to analyze the microscopic matter at the interface in the corrosive environment.The experimental results indicate that the interface performance between TRC and existing concrete would decrease with continued chloride dry-wet cycles.Compared with the specimen with a single layer of textile reinforcement,the specimens with two layers of textile with added PVA or AR-glass short-cut fibers could further improve the properties of the interface between the TRC layer and existing concrete.For the TRC with a single layer of textile,the average shear strength tended to decrease with increasing bond length.In addition,the strength grade of the existing concrete had a minor effect on the interface properties.
文摘Reinforcement inside the concrete is protected from corrosion and its damages until several years after the construction. After corrosion initiation, the cross section of reinforcement begins to reduce and often load bearing of the reinforced concrete structure will be reduced significantly. Corrosion of reinforcements in concrete in polluted and contaminated areas can occur in two ways: chloride and carbonation. In this work, meta-heuristic approach of charged system search(CSS) is used to calculate corrosion occurrence probability due to chloride ions penetration. The model efficiency is verified by comparing the available examples in technical literature and results of Monte Carlo analysis. According to the analyses performed, using different probabilistic distributions regardless of probabilistic moments based on real distribution leads to diverse results. In addition, influence of each effective parameter in corrosion occurrence varies by changing other parameters.
基金support of Reliance Industries and Bakaert Industries, India for providing fiber for the experimental work
文摘This article presents an experimental study on the flexural performance of reinforced concrete(RC)beams with fiber reinforced cementitious composites(FRCC)and hybrid fiber reinforced cementitious composites(HFRCC)in the hinge portion.Beam specimens with moderate confinement were used in the study and tested under monotonic loading.Seven diverse types of FRCC including hybrid composites using fibers in different profiles and in different volumes are employed in this study.Companion specimens such as cylindrical specimens and prism specimens are also used to study the physical properties of composites employed.The moment?curvature,stiffness behavior,ductility,crack pattern and modified flexural damage ratio are the main factors considered in this study to observe the efficacy of the employed hybrid composites.The experimental outputs demonstrate the improved post yield behavior with less rate of stiffness degradation and better damage tolerance capacity than conventional technique.
基金Project(BE2019642)supported by the Jiangsu Provincial Key Research and Development Program,China。
文摘Combining fiber reinforced polymer(FRP)with seawater sea-sand concrete(SSC)can solve the shortage of river sand that will be used for marine engineering construction.The bond performance of BFRP bars and SSC specimens is researched by pull-out test in this paper.The effects of the parameters,such as bar type,bar diameter,concrete type and stirrup restraint,are considered.It is beneficial to the bonding performance by the reduction of bar diameter.The utilization of seawater sea-sand has a low influence on the bond properties of concrete.The bond strength of BFRP is slightly lower than the steel rebar,but the difference is relatively small.The failure mode of the specimen can be changed and the interfacial bond stress can be improved by stirrups restraint.The bond-slip curves of BFRP ribbed rebar include micro slip stage,slip stage,descent stage and residual stage.The bond stress shows the cycle attenuation pattern of sine in the residual stage.In addition,the bond-slip model of BFRP and SSC is obtained according to the experimental results and related literature,while the predicted curve is also consistent well with the measured curve.
基金Project(11B033)supported by the Foundation for Excellent Young Scholars of Hunan Scientific Committee,ChinaProject(116001)supported by the Consultative Program of the Chinese Academy of Engineering+1 种基金Project(11JJ6040)supported by the National Natural Science Foundation of Hunan Province,ChinaProject(2010GK3198)supported by the Science and Research Program of Hunan Province,China
文摘Rehabilitation of existing structures with fiber reinforced plastic(FRP)has been growing in popularity because they offer superior performance in terms of resistance to corrosion and high specific stiffness.The strain coordination results of 34 reinforced concrete beams(four groups)strengthened with different methods were presented including external-bonded or near-surface mounted glass or carbon FRP or helical rib bar in order to study the strain coordination of the strengthening materials and steel rebar of RC beam.Because there is relative slipping between concrete and strengthening materials(SM),the strain of SM and steel rebar of RC beam satisfies the double linear strain distribution assumption,that is,the strain of longitudinal fiber parallel to the neutral axis of plated beam within the scope of effective height(h0)of the cross section is in direct proportion to the distance from the fiber to the neutral axis.The strain of SM and steel rebar satisfies the equation εGCH=βεsteel,where the value of β is equal to 1.1-1.3 according to the test results.