Particle erosion of C/C-SiC composites prepared by reactive melt infiltration with different Al addition was studied by gas-entrained solid particle impingement test.SEM,EDS and XRD were performed to analyze the compo...Particle erosion of C/C-SiC composites prepared by reactive melt infiltration with different Al addition was studied by gas-entrained solid particle impingement test.SEM,EDS and XRD were performed to analyze the composites before and after erosion.The results indicate that a U shape relationship curve presents between the erosion rates and Al content,and the lowest erosion rate occurs at 40 wt%Al.Except for the important influence of compactness,the increasing soft Al mixed with reactive SiC,namely the mixture located between carbon and residual Si also,plays a key role in the erosion of the C/C-SiC composites through crack deflection,plastic deformation and bonding cracked Si.展开更多
基金Project(51902239)supported by the National Natural Science Foundation of ChinaProject(2020JQ-808)supported by the Science and Technology Fund of Shaanxi Province,China+3 种基金Projects(19JK0400,19JK0402)supported by the Education Fund of Shaanxi Province,ChinaProject(SKLSP201752)supported by the State Key Laboratory of Solidification Processing in Northwestern Poly Technical University,ChinaProject(XAGDXJJ17008)supported by the Principal Fund of Xi’an Technological University,ChinaProject supported by the Youth Innovation Team of Shaanxi Universities,China。
文摘Particle erosion of C/C-SiC composites prepared by reactive melt infiltration with different Al addition was studied by gas-entrained solid particle impingement test.SEM,EDS and XRD were performed to analyze the composites before and after erosion.The results indicate that a U shape relationship curve presents between the erosion rates and Al content,and the lowest erosion rate occurs at 40 wt%Al.Except for the important influence of compactness,the increasing soft Al mixed with reactive SiC,namely the mixture located between carbon and residual Si also,plays a key role in the erosion of the C/C-SiC composites through crack deflection,plastic deformation and bonding cracked Si.