为提高镁合金板材拉深性能,提出一种基于固体颗粒介质成形（Solid granules medium forming,SGMF）工艺的镁合金板材差温拉深工艺。以单向拉伸试验获取的AZ31B镁合金板材真应力—应变曲线和颗粒材料性能试验构建的介质线性Drucker-Prage...为提高镁合金板材拉深性能,提出一种基于固体颗粒介质成形（Solid granules medium forming,SGMF）工艺的镁合金板材差温拉深工艺。以单向拉伸试验获取的AZ31B镁合金板材真应力—应变曲线和颗粒材料性能试验构建的介质线性Drucker-Prager本构模型为基础,采用有限元法对板材拉深成形进行热力耦合数值模拟并进行试验验证,研究压边力、压边间隙和温度对板材拉深性能的影响。结果表明：压边间隙和压边力联合控制比单纯控制压边力或是压边间隙更能有效地提高板材拉深性能;AZ31B镁合金板材在拉深过程中对温度有较强敏感性,板材变形温度为250~300℃,颗粒介质与其温差100~150℃时,板材达到最佳拉深性能;颗粒介质能够对工件筒壁部位提供轴向摩擦力,该摩擦力能有效提高材料拉深性能并保证板厚的均匀性,这是SGMF工艺的优势所在。展开更多
The experimental die apparatus of the solid granules medium forming on sheet metal was designed and manufactured.Typical parts,such as conical,parabolic,cylindrical and square-box-shaped components,were successfully t...The experimental die apparatus of the solid granules medium forming on sheet metal was designed and manufactured.Typical parts,such as conical,parabolic,cylindrical and square-box-shaped components,were successfully trial-produced as well.According to the analysis of the changing trends of the cross-section shape and the wall thickness during the process,it can be found that the shape of the free deformation zone of the sheet metal,which is the most critical thinning area,can be described as an approximately spherical cap.According to this forming feature,back pressure deep drawing technology with solid granules medium on sheet metal was proposed to restrain drastic thinning at the bottom of the part through the joint friction effect of solid granules medium,the back pressure tringle and the sheet metal.Therefore,the deep drawing limit of the sheet metal is significantly improved.In order to fabricate thin-walled rotary parts with great drawing ratio and complex cross-sections,a finite element model based on the material property test of the solid granules medium was established to optimize the scheme of the back pressure deep drawing.The effects on the forming performance of sheet metal from back pressure load and the approach of blank holding control were analyzed through this model.展开更多
文摘为提高镁合金板材拉深性能,提出一种基于固体颗粒介质成形（Solid granules medium forming,SGMF）工艺的镁合金板材差温拉深工艺。以单向拉伸试验获取的AZ31B镁合金板材真应力—应变曲线和颗粒材料性能试验构建的介质线性Drucker-Prager本构模型为基础,采用有限元法对板材拉深成形进行热力耦合数值模拟并进行试验验证,研究压边力、压边间隙和温度对板材拉深性能的影响。结果表明：压边间隙和压边力联合控制比单纯控制压边力或是压边间隙更能有效地提高板材拉深性能;AZ31B镁合金板材在拉深过程中对温度有较强敏感性,板材变形温度为250~300℃,颗粒介质与其温差100~150℃时,板材达到最佳拉深性能;颗粒介质能够对工件筒壁部位提供轴向摩擦力,该摩擦力能有效提高材料拉深性能并保证板厚的均匀性,这是SGMF工艺的优势所在。
基金Project(50775197) supported by the National Natural Science Foundation of China
文摘The experimental die apparatus of the solid granules medium forming on sheet metal was designed and manufactured.Typical parts,such as conical,parabolic,cylindrical and square-box-shaped components,were successfully trial-produced as well.According to the analysis of the changing trends of the cross-section shape and the wall thickness during the process,it can be found that the shape of the free deformation zone of the sheet metal,which is the most critical thinning area,can be described as an approximately spherical cap.According to this forming feature,back pressure deep drawing technology with solid granules medium on sheet metal was proposed to restrain drastic thinning at the bottom of the part through the joint friction effect of solid granules medium,the back pressure tringle and the sheet metal.Therefore,the deep drawing limit of the sheet metal is significantly improved.In order to fabricate thin-walled rotary parts with great drawing ratio and complex cross-sections,a finite element model based on the material property test of the solid granules medium was established to optimize the scheme of the back pressure deep drawing.The effects on the forming performance of sheet metal from back pressure load and the approach of blank holding control were analyzed through this model.